NGHIÊN CỨU THÀNH PHẦN CẤP PHỐI CỐT LIỆU THỦY TINH Y TẾ ĐỂ SẢN XUẤT BÊ TÔNG. LUẬN VĂN THẠC SĨ KỸ THUẬT XÂY DỰNG CÔNG TRÌNH DÂN DỤNG VÀ CÔNG NGHIỆP

HUỲNH THỊ MỸ DUNG ĐẠI HỌC ĐÀ NẴNG TRƯỜNG ĐẠI HỌC BÁCH KHOA - HUỲNH THỊ MỸ DUNG KỸ THUẬT XÂY DỰNG CƠNG TRÌNH DÂN DỤNG VÀ CƠNG NGHIỆP NGHIÊN CỨU THÀNH PHẦN CẤP PHỐI CỐT LIỆU THỦY TINH Y TẾ ĐỂ SẢN XUẤT BÊ TÔNG LUẬN VĂN THẠC SĨ KỸ THUẬT XÂY DỰNG CƠNG TRÌNH DÂN DỤNG VÀ CƠNG NGHIỆP KHOÁ K32TV Đà Nẵng – Năm 2018 ĐẠI HỌC ĐÀ NẴNG TRƯỜNG ĐẠI HỌC BÁCH KHOA - HUỲNH THỊ MỸ DUNG NGHIÊN CỨU THÀNH PHẦN CẤP PHỐI CỐT LIỆU THỦY TINH Y TẾ ĐỂ SẢN XUẤT BÊ TÔNG Chuyên ngành: Kỹ thuật Xây dựng Cơng trình Dân dụng Cơng nghiệp Mã số: 60 58 02 08 LUẬN VĂN THẠC SĨ NGƯỜI HƯỚNG DẪN KHOA HỌC: PGS TS TRƯƠNG HOÀI CHÍNH Đà Nẵng – Năm 2018 LỜI CAM ĐOAN Tôi xin cam đoan cơng trình nghiên cứu riêng Các số liệu, kết nêu luận văn trung thực chưa công bố cơng trình khoa học khác Tác giả luận văn Huỳnh Thị Mỹ Dung MỤC LỤC DANH MỤC CÁC BẢNG v DANH MỤC CÁC HÌNH VẼ, ĐỒ THỊ i MỞ ĐẦU 1 Lý chọn đề tài Đối tượng phạm vi nghiên cứu Phương pháp nghiên cứu Kết dự kiến Bố cục đề tài CHƯƠNG TỔNG QUAN VỀ VẬT LIỆU BÊ TÔNG 1.1 Khái niệm chung 1.2 Thành phần, cấu trúc các loại bê tông 1.2.1 Vật liêu, thành phần bê tông 1.2.2 Cấu trúc bê tông 1.2.3 Các loại bê tông 1.3 Cường độ bê tông (R) 1.3.1 Thí nghiệm mẫu xác định cường độ chịu nén 1.3.2 Cường độ chịu kéo Rt 1.3.3 Các yếu tố ảnh hưởng đến cường độ bê tông 1.4 Giá trị trung bình giá trị tiêu chuẩn cường độ 15 1.4.1 Giá trị trung bình 15 1.4.2 Độ lệch quân phương, hệ số biến động 15 1.4.3 Giá trị đặc trưng 15 1.5 Cấp độ bền mác bê tông 16 1.5.1 Mác theo cường độ chịu nén 16 1.5.2 Cấp độ bền chịu nén 16 1.5.3 Cấp độ bền chịu kéo Bt 17 1.5.4 Mác theo khả chống thấm theo khối lượng riêng 17 1.6 Các tính chất chủ yếu hỗn hợp bê tông bê tông 17 1.6.1 Tính co nở thể tích bê tông 17 1.6.2 Tính chịu nhiệt 18 1.6.3 Tính cơng tác bê tông 19 1.7 Kết luận chương 21 CHƯƠNG NGHIÊN CỨU THAY THẾ CỐT LIỆU TRONG THÀNH PHẦN CHẾ TẠO BÊ TÔNG 22 2.1 Các loại cốt liệu chế tạo bê tông 22 2.1.1 Cốt liệu mịn 22 2.1.2 Cốt liệu thô (đá dăm) 23 2.1.3 Cốt liệu thô (thủy tinh y tế) 25 2.2 Các nghiên cứu ứng dụng thủy tinh 29 2.2.1 Sợi thủy tinh 29 2.2.2 Thủy tinh bột 30 2.2.3 Thủy tinh bọt 30 2.2.4 Tái chế thủy tinh 30 2.3 Phương pháp xác định cường độ chịu nén (theo tiêu chuẩn Việt Nam 3118 : 1993) 31 2.3.1 Qui trình lấy mẫu, bảo dưỡng thí nghiệm 31 2.3.2 Thiết bị thử 32 2.3.3 Chuẩn bị mẫu thử 32 2.3.4 Tiến hành thử 33 2.3.5 Tính kết 33 2.3.6 Biên thử: 34 2.4 Xây dựng đề cương thí nghiệm 34 2.5 Kết luận chương 43 CHƯƠNG THÍ NGHIỆM THỰC NGHIỆM ĐÁNH GIÁ SỰ THAY ĐỔI CƯỜNG ĐỘ CHỊU NÉN CỦA BÊ TÔNG THỦY TINH THEO THỜI GIAN 44 3.1 Thực thí nghiệm 44 3.1.1 chuẩn bị vữa bê tông 44 3.1.2 Đúc mẫu bê tông: 46 3.1.3 Hình dáng kích thước viên mẫu 47 3.1.4 Số tổ mẫu cần đúc 48 3.1.5 Khuôn đúc mẫu 48 3.1.6 Đổ đầm hỗn hợp bê tông khuôn 49 3.2 Tiến hành thí nghiệm mẫu thử 50 3.2.1 Thí nghiệm cường độ nén bê tông ngày tuổi: 50 3.2.2 Thí nghiệm cường độ uốn bê tơng ngày tuổi: 50 3.2.3 Thí nghiệm cường độ uốn bê tông 14 ngày tuổi: 51 3.2.4 Thí nghiệm cường độ uốn bê tông 28 ngày tuổi: 51 3.3 Tính kết 51 3.4 Biểu đồ quan hệ cường độ bê tông theo thời gian 54 3.4.1 Biểu đồ quan hệ cường độ bê tông thường bê tông thủy tinh - cấp bền B15 54 3.4.2 Biểu đồ quan hệ cường độ bê tông thường bê tông thủy tinh - cấp bền B20 54 3.5 So sánh kết mẫu thử 55 3.6 Kết luận chương 56 TÓM TẮT LUẬN VĂN NGHIÊN CỨU THÀNH PHẦN CẤP PHỐI CỐT LIỆU THỦY TINH Y TẾ ĐỂ SẢN XUẤT BÊ TÔNG Học viên: Huỳnh Thị Mỹ Dung Chun ngành: Kỹ thuật Xây dựng Cơng trình Dân dụng Công nghiệp Mã số: 60 58 02 08 Khóa: K32TV Trường Đại học Bách khoa - ĐHĐN Tóm tắt - Bê tơng vật liệu sử dụng rộng rãi xây dựng với khối lượng lớn Khi tính toán thiết kế kết cấu bê tông bê tông cốt thép cần phải xác định thành phần cấp phối hợp lí bê tông.Quy chế Quản lý chất thải y tế (2007) bổ sung nội dung tái chế chất thải rắn (CTR) y tế không nguy hại làm để các sở y tế thực Tuy nhiên, nhiều địa phương chưa có sở tái chế, việc quản lý tái chế các CTR y tế khơng nguy hại cịn gặp nhiều khó khăn Việc “Nghiên cứu thành phần cấp phối cốt liệu thủy tinh y tế để sản xuất bê tơng” cần thiết góp phần để xử lý lượng chất thải rắn y tế địa phương tạo sản phẩm xây dựng có khả ứng dụng vào thực tế Trong luận văn tác giảđã nghiên cứu thay đổi cường độ chịu nén bê tông thủy tinh theo thời gian, từ mẫu bê tông ngày tuổi 28 ngày tuổi Nghiên cứu với hai cấp phối thủy tinh, mẫu thí nghiệm lập phương 15x15x15 cm đúc, bảo dưỡng thí nghiệm phòng So sánh cường độ chịu nén các cấp bền bê tông đá dăm thông thường bê tông cốt liệu thủy tinh, từ suy cấp bền bê tơng thuỷ tinh tương ứng Từ khóa – Bê tông thủy tinh; Bê tông tái chế; Bê tông từ chai lọ thủy tinh; Vật liệu mới; Cốt liệu bê tông RESEARCH ON THE COMPOSITION OF MEDICAL GLASS AGGREGATES FOR CONCRETE PRODUCTION Abstract – Concrete is the material that is widely used in construction with great volume When calculating the structural design of concrete and reinforced concrete, it is necessary to determine the proper mix of concrete The Medical Waste Management Regulation (2007) has added nonhazardous medical solid waste recycling as a basis for medical facilities However, many localities not have recycling facilities, so the management of recycling non-hazardous medical solid waste is still difficult The "Research on the composition of medical glass aggregates for the concrete production" is necessary to contribute to the solid waste treatment in local health and to the creation of a viable construction product which is used in practice In this thesis the author has studied the change in compressive strength of glass concrete over time, since the concrete is days old until 28 days old Study with two layers of glass, 15x15x15 cm cube samples were molded, maintained and tested in the lab Comparison of compressive strength between durable grades of conventional macadam concrete and glass-reinforced concrete, thus inferring the durable grade of glass concrete Key words – Glass - reinforced concrete; Recycled concrete; Concrete from glass bottles; New material; New aggregate in concrete DANH MỤC CÁC CHỮ VIẾT TẮT ASTM: Tiêu chuẩn Mỹ B: Cấp độ bền bê tông CTR: Chất thải rắn EN: Tiêu chuẩn châu Âu M: Mác bê tông N/X: Nước/xi măng TCVN: Tiêu chuẩn Việt Nam TB: Trung bình Rb: Cường độ bê tông Rk: Cường độ chịu kéo bê tông Rn: Cường độ chịu nén bê tông Ru: Cường độ chịu uốn bê tông : Khối lượng riêng DANH MỤC CÁC BẢNG Số hiệu bảng Tên bảng Trang 2.1 Phân loại cốt liệu theo khối lượng riêng 23 2.2 Thời gian trộn hỗn hợp bê tông (phút) 32 2.3 Độ sụt hỗn hợp bê tông nên dùng cho các dạng kết cấu 34 2.4 Lượng nước trộn ban đầu cần cho 1m3 bê tơng, lít 35 2.5 Hệ số chất lượng vật liệu A A1 36 2.6 Hệ số quy đổi cường độ nén bê tông các tuổi cường độ bê tông 28 ngày kt 36 2.7 Hàm lượng xi măng tối thiểu 1m3 bê tông, kg 37 2.8 Hệ số dư vữa hợp lý (Kd) dùng cho hỗn hợp bêtông dẻo (ĐS =  12cm); cốt liệu lớn đá dăm (nếu dùng sỏi, Kd tra bảng cộng thêm 0,06) 38 2.9 Vật liệu sử dụng thí nghiệm 40 2.10 Thành phần vật liệu cho 1m3 bêtông B15 (cốt liệu đá  2) 40 2.11 Thành phần vật liệu cho 1m3 bêtông B15 (50% đá + 50% Thủy tinh) 40 2.12 Thành phần vật liệu cho 1m3 bêtông B15 (100% cốt liệu thủy tinh) 41 2.13 Thành phần vật liệu cho 1m3 bêtông B20 (cốt liệu đá  2) 41 2.14 Thành phần vật liệu cho 1m3 bêtông B20 (50% đá + 50% Thủy tinh) 42 2.15 Thành phần vật liệu cho 1m3 bêtông B20 (100% cốt liệu thủy tinh) 42 2.16 Bảng tổng hợp các cấp phối cho 1m3 bê tông các loại 43 3.1 Kết thí nghiệm tổng hợp cấp bền B15 53 3.2 Kết thí nghiệm tổng hợp cấp bền B20 53 3.3 Sự chênh lệch cường độ chịu nén Bê tông thường Bê tông thủy tinh (50% đá+50% Thủy tinh) cấp bền B15 55 3.4 Sự chênh lệch cường độ chịu nén Bê tông thường Bê tông thủy tinh (100% Thủy tinh) cấp bền B15 55 3.5 Sự chênh lệch cường độ chịu nén Bê tông thủy tinh (50% Thủy tinh 100% Thủy tinh) cấp bền B15 55 3.6 Sự chênh lệch cường độ chịu nén Bê tông thường Bê tông thủy tinh (50% đá+50% Thủy tinh) cấp bền B20 55 3.7 Sự chênh lệch cường độ chịu nén Bê tông thường Bê tông thủy tinh (100% Thủy tinh) cấp bền B20 56 3.8 Sự chênh lệch cường độ chịu nén Bê tông thủy tinh (50% Thủy tinh 100% Thủy tinh) cấp bền B20 56 DANH MỤC CÁC HÌNH VẼ, ĐỒ THỊ Số hiệu hình Tên hình Trang 1.1 Mẫu thí nghiệm cường độ chịu nén 1.2 Sự phá hoại mẫu thử khối vuông 1.3 Thí nghiệm xác định cường độ chịu kéo 1.4 Quan hệ R Rt theo thực nghiệm 1.5 Đường cong biểu thị phụ thuộc cường độ bê tông tỷ lệ xi măng nước Rb = f(X/N) dạng phương trình đường thẳng biểu thị cường độ bê tông phụ thuộc vào tỷ lệ X/N X/N  2,5 X/N >2,5 11 1.6 Sự phụ thuộc cường độ bê tông nặng vào X/N mác xi măng khác 12 1.7 Sự ảnh hưởng mức độ lèn chặt hỗn hợp bê tông đến lượng nước thích hợp cuờng độ 13 1.8 Quá trình thay đổi lượng nước cấu trúc gel đá xi măng 17 1.9 Thiết bị xác định độ sụt hỗn hợp bê tơng 20 1.10 Thí nghiệm xác định độ chảy xịe bê tơng 21 2.1 Cấp phối hạt tốt cho cốt liệu nhỏ bê tông 22 2.2 Lựa chọn cỡ hạt lớn cốt liệu thô 24 2.3 Các dạng hạt đạt yêu cầu 25 2.4 Rác thủy tinh phân loại nguồn 26 2.5 Rác y tế phân loại xử lý 26 2.6 Lị đốt chất thải y tế khơng tái chế 27 2.7 Rác thải thủy tinh y tế phân loại 27 2.8 Rác thải nhựa y tế phân loại 27 2.9 Rác thải chuyển giao đến nơi tái chế 27 ... THỊ MỸ DUNG NGHIÊN CỨU THÀNH PHẦN CẤP PHỐI CỐT LIỆU TH? ?Y TINH Y TẾ ĐỂ SẢN XUẤT BÊ TÔNG Chun ngành: Kỹ thuật X? ?y dựng Cơng trình Dân dụng Công nghiệp Mã số: 60 58 02 08 LUẬN VĂN THẠC SĨ NGƯỜI HƯỚNG... luận chương 56 TÓM TẮT LUẬN VĂN NGHIÊN CỨU THÀNH PHẦN CẤP PHỐI CỐT LIỆU TH? ?Y TINH Y TẾ ĐỂ SẢN XUẤT BÊ TÔNG Học viên: Huỳnh Thị Mỹ Dung Chuyên ngành: Kỹ thuật X? ?y dựng Cơng trình Dân. .. ứng dụng vào thực tế Đối tượng phạm vi nghiên cứu - Đối tượng nghiên cứu: Vật liệu bê tông sử dụng cốt liệu th? ?y tinh - Phạm vi nghiên cứu: Nghiên cứu thay đổi cường độ chịu nén bê tông th? ?y tinh