(Đồ án hcmute) nghiên cứu tổng hợp vật liệu sio2 bọc ag, tiềm năng sử dụng trong cảm biến sinh học miễn dịch

BỘ GIÁO DỤC VÀ ĐÀO TẠO TRƯỜNG ĐẠI HỌC SƯ PHẠM KỸ THUẬT THÀNH PHỐ HỒ CHÍ MINH ĐỒ ÁN TỐT NGHIỆP NGÀNH CÔNG NGHỆ VẬT LIỆU NGHIÊN CỨU TỔNG HỢP VẬT LIỆU SiO2 BỌC Ag, TIỀM NĂNG SỬ DỤNG TRONG CẢM BIẾN SINH HỌC MIỄN DỊCH GVHD: ĐINH VĂN PHÚC SVTH: CÙ PHẠM THÀNH HIẾU MSSV: 16130018 SKL 0 3 Tp Hồ Chí Minh, tháng 08/2020 an ƢỜ Ọ Ƣ Ậ Ọ Ứ Ụ Ệ Ậ Ậ Ệ Ệ NGHIÊN CỨU TỔNG HỢP VẬT LIỆU SiO2 BỌC Ag, TIỀ Ă Ử DỤNG TRONG CẢM BIẾN SINH HỌC MIỄN DỊCH T Hồ Ă Ú GVHD: TS SVTH: CÙ PH M THÀNH HIẾU MSSV: 16130018 KHÓA: 2016 ,t an ăm 2020 ƢỜ Ọ Ƣ Ậ Ọ Ứ Ụ Ệ Ậ Ậ Ệ Ệ NGHIÊN CỨU TỔNG HỢP VẬT LIỆU SiO2 BỌC Ag, TIỀ Ă Ử DỤNG TRONG CẢM BIẾN SINH HỌC MIỄN DỊCH T Hồ Ă Ú GVHD: TS SVTH: CÙ PH M THÀNH HIẾU MSSV: 16130018 KHÓA: 2016 ,t an ăm 2020 ƢỜ I HỌ Ƣ M K THUẬT TP HCM Ĩ C NG HOÀ XÃ H I CHỦ ỆT NAM Độc lập - Tự – Hạnh phúc KHOA KHOA HỌC ỨNG DỤNG BM CÔNG NGHỆ VẬT LIỆU T Hồ , y t ăm NHIỆM VỤ KHÓA LUẬN T T NGHIỆP Giảng viên hƣớng dẫn: TS inh ăn húc quan công tác giảng viên hƣớng dẫn: Đại học Duy Tân Sinh viên thực hiện: Cù Phạm Thành Hiếu MSSV: 16130018 Tên đề tài: Nghiên cứu tổng hợp vật liệu SiO2 bọc Ag, tiềm ă học miễn học sử dụng cảm biến sinh Nội dung khóa luận: - Tổng hợp vật liệu SiO2 bọc Ag bằ ƣơ óa ọc Nghiên cứu thay đổi yếu tố ả ƣở đến q trính hình thành vật liệu SiO2 bọc Ag ƣ: Nồ độ muối bạc, nhiệt độ phản ứng, thời gian phản ứng, thời gian tiếp xúc hợp chất trƣớc phản ứng, từ c ọ đƣợc đ ều kiện tố ƣu ất cho ứng dụng vật liệu cảm biến sinh học miễn dịch - Khảo sát hình thái, cấu trúc vật liệu bằ ƣ UV-Vis, SEM, DLS, Zeta, Raman c c ƣơ Các sản phẩm dự kiến: Vật liệu dạng rắn (bột) dung dịch Ngày giao đồ án: Ngày nộp đồ án: Ngơn ngữ trình bày: Bản báo cáo: Tiếng Anh  Trình bày bảo vệ: Tiếng Anh  ƢỞNG B MƠN (Ký, ghi rõ họ tên) GIẢ â tc Tiếng Việt Tiếng Việt ệ đại   Ê ƢỚNG DẪN (Ký, ghi rõ họ tên) i an Ọ Ứ Ụ Ệ Ậ Ệ c ậ – ự – Ủ Ĩ ạnh húc Ệ ******* Ậ Ủ Ê ƢỚ Ẫ ọ v tên inh viên hạm Thành Hiếu MSSV:16130018 g nh: Công nghệ Vật liệu ên ề t i Nghiên cứu tổng hợp vật liệu SiO2 bọc Ag, tiềm ă sử dụng cảm biến sinh học miễn học ọ v tên iá viên hƣớng ẫn TS inh ăn Phúc quan công tác hƣớng dẫn: Đại học Duy Tân Địa chỉ: Ậ Về ộ u đề t v ố ƣợ t ực ệ : * Đề t t ực hiệ đầy đủ nộ u đề ra: - Khảo sát yếu tố ả ƣở đến trình tổng hợp vật liệu SiO2 bọc Ag bằ ƣơ pháp hóa học, ƣ t ời gian phản ứng, - Sử dụ ƣơ â t c óa ý UV-V s c ứ m đƣợc tạo thành a o A tro c c đ ều kiện khảo sát, sử dụng kết hợ ƣơ đo t ế Zeat, DLS, SE c ứ m đƣợc hạt SiO2 đƣợc bọc thành công hạt nano Ag - Sử dụ ƣơ t xạ Raman m đƣợc hạt nano Ag có khả ă m tă cƣờng tín hiệu Raman SiO2, cho thấy đƣợc khả ă ứng dụng vật liệu tổng hợ đƣợc tro ĩ vực cảm biến sinh học miễn dịch * Khố ƣợng đề t đảm bảo yêu cầu LUẬ Ă T NGHỆ I HỌC Tinh thần học tập, nghiên cứu sinh viên: Sinh viên Cù Phạm Thành Hiếu có tinh thần học tậ c ăm c ỉ, nghiêm túc trình làm nghiên cứu Đây GIAI N MỞ ẦU, LÀM QUEN trình nghiên cứu, sinh viên Cù Phạm Thành Hiếu t ể hiệ đƣợc tự c, c ăm c ỉ tìm hiểu v đọc tài liệu c c say mê, có t độ tiếp thu học hỏi kinh nghiệm trình làm việc Ƣu đ ểm: - Mặc dù kiến thức ê qua đế ĩ vực Hóa, đặc biệt tổng hợp vật liệu Vơ bằ ƣơ Hóa ọc c ƣa ều, ƣ s vê ù P ạm Thành Hiếu c ăm chịu khó học hỏi, biết lắng nghe cầu thị, tinh thần làm việc nhóm tốt - Làm việc cẩn thận, tỉ mỉ uyết đ ểm: Khơng có Đề ị c o ảo vệ ay ô Đề nghị cho sinh viên Cù Phạm Thành Hiếu đƣợc bảo vệ Đ ểm: 9.5 ằ c ữ: Chín phẩy ăm) T G o v ê ƣớ ii an Ọ Ứ Ụ Ệ Ậ Ệ Ủ Ĩ Ệ – ạnh húc c ậ – ự ******* Ậ Ủ Ê Ả Ệ ọ v tên inh viên: Cù Phạm Thành Hiếu MSSV:16130018 g nh: Công nghệ Vật liệu ên ề t i Nghiên cứu tổng hợp vật liệu SiO2 bọc Ag, tiềm ă sử dụng cảm biến sinh học miễn học ọ v tên iá viên hản iện: quan công tác GV phản biện: ịa chỉ: Ậ Về ộ u đề t v ố ƣợ t ực ệ : Ƣu đ ểm: uyết đ ểm: Kiến nghị câu hỏi: Đề ị c o ảo vệ ay ô Đ ểm: ằ c ữ: ) T 20 G ovê ả ệ ọ iii an LỜI CẢ Ơ Để hồn thành khóa luận tốt nghiệ , trƣớc tiên, xin gửi lời cảm trâ trọng đến ba mẹ a đì c u cấ , động viên tạo động lực để học tập cố gắng suốt ăm ọc Tôi xin chân thành cảm c c T ầy Cô môn Công nghệ Vật liệu dạy v ƣớng d n tơi suốt q trình học tậ tro ăm ọc Tôi xin chân thành cảm T ầy Đ Vă P úc trực tiếp ƣớng d n, giúp đỡ tận tình trình thực khóa luận Khóa luận tốt nghiệp hồn thành, xin cảm Thầy TS Đ o Vĩ Á , PGS.TS Nguyễ Đă Nam cù c c a , c ị phịng thí nghiệm Thiết bị Vật liệu tƣơ a F &D La ), viện nghiên cứu Khoa học ản ứng dụ , trƣờ Đại học Duy Tân, Viện Khoa học Vật liệu Ứng dụng – Viện Hàn lâm Khoa học Công nghệ Việt Nam, phịng Thí nghiệm Bộ mơn Cơng nghệ Vật liệu trƣờ Đại học Sƣ ạm Kỹ thuật TP.Hồ Chí Minh iv an LỜ Tôi x cam đoa to ộ nộ u đƣợc trình bày khóa luận tốt nghiệp bả t â tô m ƣới ƣớng d n hỗ trợ tồn kinh phí hóa chất, thiết bị, dụng cụ Thầy TS Đ Vă P úc, trƣờ Đại học Duy Tân Tô x cam đoa nội dung đƣợc tham khảo khóa luận tốt nghiệ đƣợc trích d n x c v đầy đủ t eo qu định Tháng 08 ăm 020 Ký tên v an MỤC LỤC NHIỆM VỤ KHÓA LUẬN TỐT NGHIỆP i NHẬN X T ỦA GIÁ VI N HƢ NG D N ii NHẬN X T ỦA GIÁ VI N PH N IỆN iii LỜI C ƠN iv LỜI A Đ AN v MỤC LỤC vi DANH MỤC CÁC CHỮ VIẾT TẮT viii DANH MỤC CÁC B NG BIỂU ix DANH MỤC CÁC BIỂU ĐỒ VÀ HÌNH NH x LỜI MỞ ĐẦU ƣơ TỔNG QUAN 1.1 Công nghệ nano vật liệu hạt nano bạc ƣởng plasmon bề mặt cục 1.2 Cộ T xa Rama tă Tă cƣờ cƣờng bề mặt đ ện từ 11 1.3.2 Vai trò Hot s ots đế tă cƣờng SERS 14 1.3.3 Sự phụ thuộc khoảng cách tă cƣờ đ ện từ đế tă cƣờng SERS 17 1.4 Vật liệu SiO2 bọc Ag 17 1.5 Cảm biến sinh học miễn dịch dựa hiệ tƣợng cộ ƣởng plasmon bề mặt 18 1.5.1 Cảm biến sinh học phân loại 18 1.5.2 Cảm biến sinh học miễn dịch dựa hiệ tƣợng cộ ƣởng plasmon bề mặt đƣợc hỗ trợ nano bạc 21 c ƣơ o c o trƣớc cảm biến sinh học miễn dịch 25 VẬT LIỆU VÀ PHƢƠNG PHÁP 27 vi an 2.1 Vật liệu 27 c ƣơ ê cứu 27 P ƣơ ổ tử ngoại – Khả kiến (UV-Vis) 27 P ƣơ ể v đ ện tử quét (SEM) 28 P ƣơ đo Rama 29 2.2.4 P ƣơ P ƣơ t xạ động (DLS) 29 x c định Zeta 30 c ế trình tổng hợp vật liệu SiO2 bọc Ag 31 chế ổ định keo hạt dung dịch 33 2.4 Tiến hành thực nghiệm 35 c đ ều kiện thực thí nghiệm 36 ƣơ ẾT QU VÀ BIỆN LUẬN 39 3.1 Các yếu tố ả ƣở đến trình tổng hợp vật liệu SiO2 bọc Ag 39 3.1.1 ƣởng nhiệt độ phản ứ đến trình tổng hợp vật liệu SiO2 bọc Ag 39 3.1.2 ƣởng thời gian phản ứ đến trình tổng hợp vật liệu SiO2 bọc Ag 41 3.1.3 ƣởng thời gian tiếp xúc SiO2 v PVP đến trình tổng hợp vật liệu SiO2 bọc Ag 42 3.1.4 ƣởng tỷ lệ AgNO3 : trate đến trình tổng hợp vật liệu SiO2 bọc Ag 44 3.1.5 Phổ UV-Vis vật liệu đ ều kiện tố ƣu 44 3.2 Kết ảnh SEM vật liệu SiO2 bọc A tố ƣu 46 3.3 Kết Zeta vật liệu SiO2 bọc A tố ƣu 47 3.4 DLS vật liệu SiO2 bọc A tố ƣu 48 3.5 Phổ Raman vật liệu SiO2 bọc A tố ƣu 49 HƢƠNG ẾT LUẬN 51 TÀI LIỆU THAM KH O 53 vii an Hình 11 Kết Zeta SiO2, Ag vật liệu SiO2 bọc Ag 3.4 DLS vật liệu SiO2 bọc Ag ã tối ƣu M u SiO2 bọc Ag sau tổng hợ , đƣợc khảo s t trê ƣơ DLS Hình 3.12 thể kết đo â ố c t ƣớc hạt với kết đƣợc trung bình đo đƣợc 3277 nm Qua quan sát Hình 3.12, cho thấy đƣợc phân bố c t ƣớc tốt Tro đó, số ƣợng hạt SiO2 bọc Ag nằm vị trí 3m nhiều Kết này, phù hợp với kết SE đƣợc thực Đối vớ ƣơ đo DLS, ƣơ pháp chấp nhận giá trị bao gồm bán kính thủy động học nên kết sai lệch so vớ ƣơ SE 48 an Hình 12 Kết đo DLS m u SiO2 bọc Ag 3.5 Phổ Raman vật liệu SiO2 bọc Ag ã tối ƣu Hình 13 Kết phổ Raman tán xạ bề mặt với m u S m u SiO2/PVP; m u SA1, SA2, SA3, SA4 lầ ƣợt với tỷ lệ AgNO3:Citrate 4:1; 4:1.5; 4:2; 4:3.5 o vớ cù đ ều khiệ ƣ C, 22 phản ứng, 45 phút tiếp xúc 49 an Qua Hình 3.13 kết đo ƣơ t xạ Raman hai m u m u SiO2/PVP (PVP-làm chất ổ định-S) SiO2 bọc Ag (SA1) Ta thấy, xuất đỉnh phổ vị trí 245 cm-1 phổ m u SiO2 bọc Ag Đỉnh phổ 245 cm-1 xuất có mặt liên kết Ag-O/Ag-N vùng không gian bề mặt hạt cầu SiO2 [98] Tro đó, t eo o cáo Phatangera cộng (2016), xác suất để hình thành liên kết Ag-N thấ , o đó, ê ết Ag-N đƣợc bỏ qua ƣờ độ đỉnh 245 cm-1 giải thích tă ê số ƣợng Ag- m c ú đƣợc tạo từ số ƣợng lớn hạt a o A c t ƣớc nhỏ v ƣợng oxy có sẵn phá vỡ liên kết hóa học có liên quan Các hạt a o A cũ có t ể đƣợc gắn vào hạt nano SiO2 thông liên kết oxy tự đƣợc tạo vùng bề mặt [98, 99] Trong Hình 3.13, có xuất đỉnh phổ vị trí 797 cm-1 Đỉnh phổ ó c từ số ƣợng lớn Ag-O-Ag đƣợc tao thông qua liên kết Ag O vùng bề mặt hạt nano SiO2 [98, 100] Bên cạ đó, với m u SiO2 PVP có đỉnh phổ vị trí 800 cm-1 N uyê â ao độ đối xứng Si-O-Si N o cị có đỉnh phổ khác 1080 -1 cm Si-O-Si asymmetric stretching [101, 102] Ha đỉnh phổ xuất m u (S SA1), thấy, sau m u SiO2/PVP (PVP làm chất ổ định) có gắn thêm hạt A ê o , cƣờ độ tín hiệu tă ê rõ rệt Đ ều giải thích việc gắn thêm hạt a o A t uy đƣợc hiệu ứ tă cƣờng tán xạ Raman bề mặt với ả ƣở ƣ tă cƣơ đ ện từ, vị trí -1 ot s ot N o ra, cị có đỉnh phổ vị trí 557 cm xuất ó N-C=O band [103] ƣờ độ vị trí phổ so với m u khơng gắn hạt bạc (S) nhỏ ều so với m u ắn hạt bạc, ƣ qua s t trê Hình 3.13 Việc tă ê tục cƣờ độ tạ đỉnh phổ đặc trƣ cm-1 đƣợc cho o ƣợng nano bạc tạo t tă cao m u SA1, SA2, SA3, SA N ƣ vị trí đỉnh phổ đặc trƣ c ƣ cm-1, 1080 cm-1 m u SA4 lại giảm Đ ều cho thấy, ƣợng bạc tă ê nhiều, d đến hiệ tƣợng tán xạ Raman bề mặt giảm Đ ều y đƣợc giải thích suy giảm việc kết hợp tín hiệu hai vật liệu làm cho tín hiệu tổng vật liệu bị giảm Từ kết hình ảnh phổ Raman đƣợc tă cƣờng bề mặt cho thấy, có t ay đổi tín hiệu rõ ràng vật liệu sau ắn vật liệu nano Ag Kết này, chứng minh đƣợc hạt nano bạc đƣợc bao bọc hạt SiO2 làm xảy hiệ tƣợ tă cƣờng tín hiệu ƣ tro ết đo SE t đƣợc hồn tồn hợp lí 50 an ƢƠ KẾT LUẬN Kết nghiên cứu cho thấy tổng hợ đƣợc vật liệu SiO2 bọc Ag xung quanh Quá trình tổng hợp bị ả ƣởng yếu tố ƣ t ời gian phản ứng, nhiệt độ phản ứng, thời gian tiếp xúc tỷ lệ nồ độ Cụ thể ƣ sau:  ƣởng nhiệt độ phản ứng: Tại nhiệt độ phịng, hạt nano bạc đƣợc tạo thành Khi nhiệt độ tă từ nhiệt độ phòng đến 70 oC, tƣợ tă ảm cƣờ độ hấp thụ quang xuất Đ ều tốc độ hình thành hạt nano bạc Độ hấp thụ tă từ nhiệt độ phòng đến 60 oC ƣợng nano bạc sinh nhiều Và, giảm nhiệt độ tiếp tục tă lên 70 o C keo tụ hạt nano bạc xảy  ƣởng thời gian phản ứng: Khi thời gian phản ứ tă từ 18 đến 24 d đế cƣờ độ hấp thụ tă Do trải qua trình khử liên tục ion bạc Sau đó, c c ạt nano bạc bị phân hủy, đồng thời chúng bị keo tụ thời gian phản ứng tiếp tục kéo dài D đến cƣờ độ hấp thụ giảm  ƣởng thời gian tiếp xúc: Quá trình ổ định ln q trình cần ƣu ý tổng hợp vật liệu nano Sự ổ định lớp polime SiO2 giúp ion Ag+ bám tốt bề mặt Kết quả, cƣờ độ hấp thụ tă thời gian tiế xúc út đến 45 phút, ion Ag+ bị khử thành hạt nano bạc Tuy nhiên, thời gian tiế xúc đƣợc khảo s t tă từ út đến 120 phút, d đến ổ định dung dịch cạnh tranh lực Van der Waals yếu lực đẩy tĩ đ ện Đ ều khiế c o độ hấp thụ quang vật liệu giảm  Sự ả ƣởng tỷ lệ AgNO3 : Citrate: T c động trực tiếp đế c t ƣớc hạt nano bạc đƣợc tạo t Tro đó, độ hấp thụ qua tă ê c t ƣớc hạt nano nhỏ tỷ lệ : đến 4:3 giảm c t ƣớc hạt to lên tỷ lệ : đến 4:5 Cuối cùng, kết tổng hợp vật liệu SiO2 bọc Ag vớ c c đ ều kiện tố ƣu vùng khảo sát, đƣợc tă cƣờng tín hiệu Raman bề mặt với nồ độ khác AgNO3 Citrate khác (4:1, 4:1.5, 4:2, 4:3.5) Với tính hiệu tốt vùng khảo sát tỷ lệ 4:2 Tuy nhiên số ƣợng nano bạc tă cao tỷ lệ 4: 3.5, làm cho hiệu ứng tán xạ Raman bị giảm Đ ều y đƣợc giải thích, số đặc đ ểm ƣ vị trí hot spot, khoảng cách hạt, trƣờ đ ện từ cục xảy bề mặt vật liệu bị giảm Với tiềm ă ứng dụng vật liệu SiO2 bọc Ag cảm biến sinh học miễn dịch đƣợc sử dụng tốt nghiên cứu tƣơ t c phân tử sinh học với việc xử lí m u tối thiểu Tuy nhiên, v đạt đƣợc độ nhạy cực cao Cảm biến sinh học 51 an miễn dịch vớ c c ƣu đ ểm ƣ cấu ì ản, thiết bị cầm tay tiện lợi, tận dụng t ay đổi màu sắc quan sát mắt t ƣờ để nhận biết có mặt phân tử phân tích hứa hẹn thiết bị có tiềm ă tốt chuẩn đo âm s Kiến nghị Khóa luậ y ƣớc đầu nghiên cứu tổng hợp vật liệu SiO2 bọc Ag, ƣớng tới ứng dụng cảm biến sinh học Vì vậy, để vật liệu SiO2 bọc A đạt hiệu tốt cảm biến sinh học cần nhiều cơng trình nghiên cứu chun sâu mở rộ Chúng tơi có số kiến nghị để hoàn thiệ c o đề tài ƣ: khảo sát toàn khoả đ ều kiện vớ ƣớc nhảy nhỏ , t ay đổi nồng độ pH việc tổng hợp vật liệu, đồng thời thực khảo sát vật liệu SiO2 bọc Ag trực tiếp thiết bị cảm biến sinh học để kết đƣợc kiếm soát trực tiếp 52 an TÀI LIỆU THAM KHẢO [1] Hammond, J L., Bhalla, N., Rafiee, S D., & Estrela, P (2014) "Localized surface plasmon resonance as a biosensing platform for developing countries" Biosensors 4, pp.172-188 [2] Petryayeva, E., & Krull, U J (2011) "Localized surface plasmon resonance: Nanostructures, bioassays and biosensing—A review" Anal Chim Acta 706, pp.824 [3] Anker, J N., Hall, W P., Lyandres, O., Shah, N C., Zhao, J., & Van Duyne, R P (2008) "Biosensing with plasmonic nanosensors" Nature Materials 7, pp.442453 [4] Boisselier, E., & Astruc, D (2009) "Gold nanoparticles in nanomedicine: preparations, imaging, diagnostics, therapies and toxicity" Chemical Society Reviews 38, pp.1759-1782 [5] Loiseau, A., Asila, V., Boitel-Aullen, G., Lam, M., Salmain, M., & Boujday, S (2019) "Silver-based plasmonic nanoparticles for and their use in biosensing" Biosens Bioelectron 9, pp.78 [6] Ghorbanpour, M., Manika, K., & Varma, A (2017) "Nanoscience and Plant-Soil Systems" Springer [7] Lyddy, Ruth (2009), "Chapter 36 - Nanotechnology".Academic Press, San Diego: Academic Press; 2009, pp 321-328 [8] Kolahalam, L A., Viswanath, I K., Diwakar, B S., Govindh, B., Reddy, V., & Murthy, Y L N (2019) "Review on nanomaterials: Synthesis and applications" Mater Today 18, pp.2182-2190 [9] Mobasser, S., & Firoozi, A A (2016) "Review of Nanotechnology Applications in Science and Engineering" J Civil Eng Urban 6, pp.84-93 [10] Ramos, A P., Cruz, M A., Tovani, C B., & Ciancaglini, P (2017) "Biomedical applications of nanotechnology" Biophys Rev 9, pp.79-89 [11] Prasad, R., Bhattacharyya, A., & Nguyen, Q D (2017) "Nanotechnology in Sustainable Agriculture: Recent Developments, Challenges, and Perspectives" Front Microbiol [12] Rashidi, L., & Khosravi-Darani, K (2011) "The Applications of Nanotechnology in Food Industry" Crit Rev Food Sci Nutr 51, pp.723-730 53 an [13] Singh, N A (2017) "Nanotechnology innovations, industrial applications and patents" Environ Chem Lett 15, pp.185-191 [14] Bundschuh, M., Filser, J., Lüderwald, S., McKee, M S., Metreveli, G., Schaumann, G E., & Wagner, S (2018) "Nanoparticles in the environment: where we come from, where we go to?" Environ Sci Eur 30, pp.6-6 [15] Lee, Sang Hun, Jun, Bong-Hyun (2019) "Silver Nanoparticles: Synthesis and Application for Nanomedicine" Int J Mol Sci 20, pp.865 [16] Bhakya, S., Muthukrishnan, S., Sukumaran, M., & Muthukumar, M (2016) "Biogenic synthesis of silver nanoparticles and their antioxidant and antibacterial activity" Appl Nanosci 6, pp.755-766 [17] Dong, X Y., Gao, Z W., Yang, K F., Zhang, W Q., & Xu, L W (2015) "Nanosilver as a new generation of silver catalysts in organic transformations for efficient synthesis of fine chemicals" Catal Sci Technol 5, pp.2554-2574 [18] Dankovich, T A., & Gray, D G (2011) "Bactericidal paper impregnated with silver nanoparticles for point-of-use water treatment" Environ Sci Technol 45, pp.1992-1998 [19] Abbasi, E., Milani, M., Fekri Aval, S., Kouhi, M., Akbarzadeh, A., Tayefi Nasrabadi, H., Samiei, M (2016) "Silver nanoparticles: Synthesis methods, bio-applications and properties" Crit Rev Microbiol 42, pp.173-180 [20] Prabhu, S., & Poulose, E K (2012) "Silver nanoparticles: mechanism of antimicrobial action, synthesis, medical applications, and toxicity effects" Int Nano Lett 2, pp.32 [21] Alexander, J W (2009) "History of the medical use of silver" SURG INFECT 10, pp.289-292 [22] Tatsuma, T., & Matsubara, K (2008) "Photocatalytic Deposition and PlasmonInduced Dissolution of Metal Nanoparticles on TiO2" Metal Nanoclusters in Catalysis and Materials Science: The Issue of Size Control pp.263 [23] Chen, Y., & Ming, H (2012) "Review of surface plasmon resonance and localized surface plasmon resonance sensor" Photonic Sensors 2, pp.37-49 [24] Rycenga, M., Cobley, C M., Zeng, J., Li, W., Moran, C H., Zhang, Q., & Xia, Y (2011) "Controlling the synthesis and assembly of silver nanostructures for plasmonic applications" Chem Rev 111, pp.3669-3712 [25] Evanoff Jr, D D., & Chumanov, G (2005) "Synthesis and Optical Properties of Silver Nanoparticles and Arrays" ChemPhysChem 6, pp.1221-1231 54 an [26] Le Ru, Eric, Etchegoin, Pablo (2008) "Principles of Surface-Enhanced Raman Spectroscopy: and related plasmonic effects" Elsevier [27] Liz-Marzán, L M (2006) "Tailoring surface plasmons through the morphology and assembly of metal nanoparticles" Langmuir 22, pp.32-41 [28] Bai, Y., Gao, C., & Yin, Y (2017) "Fully alloyed Ag/Au nanorods with tunable surface plasmon resonance and high chemical stability" Nanoscale 9, pp.14875-14880 [29] Sharma, B., Frontiera, R R., Henry, A I., Ringe, E., & Van Duyne, R P (2012) "SERS: Materials, applications, and the future" Mater Today 15, pp.1625 [30] Liu, X., Li, D., Sun, X., Li, Z., Song, H., Jiang, H., & Chen, Y (2015) "Tunable dipole surface plasmon resonances of silver nanoparticles by cladding dielectric layers" Sci Rep 5, pp.12555 [31] Mulvaney, P (1996) "Surface plasmon spectroscopy of nanosized metal particles" Langmuir 12, pp.788-800 [32] Pilot, R., Signorini, R., & Fabris, L (2018), "Surface-enhanced Raman spectroscopy: Principles, substrates, and applications".Springer: Springer; 2018, pp 89-164 [33] McGregor, H C., Wang, W., Short, M A., & Zeng, H (2016) "Clinical utility of Raman spectroscopy: current applications and ongoing developments" 2016, pp [34] Pilot, R., Signorini, R., Durante, C., Orian, L., Bhamidipati, M., & Fabris, L (2019) "A review on surface-enhanced Raman scattering" Biosensors 9, pp.57 [35] Ding, S Y., You, E M., Tian, Z Q., & Moskovits, M (2017) "Electromagnetic theories of surface-enhanced Raman spectroscopy" Chem Soc Rev 46, pp.4042-4076 [36] Lu, J., Song, Y., Lei, F., Du, X., Huo, Y., Xu, S., & Zhang, C (2020) "electric field-Modulated Surface enhanced Raman Spectroscopy by pVDf/Ag Hybrid" Sci Rep 10, pp.1-8 [37] Rodriguez, I., Shi, L., Lu, X., Korgel, B A., Alvarez-Puebla, R A., & Meseguer, F (2014) "Silicon nanoparticles as Raman scattering enhancers" Nanoscale 6, pp.5666-5670 [38] Zhao, Q., Zhou, J., Zhang, F., & Lippens, D (2009) "Mie resonance-based dielectric metamaterials" Mater Today 12, pp.60-69 55 an [39] Tang, H., Zhu, C., Meng, G., & Wu, N (2018) "Surface-enhanced Raman scattering sensors for food safety and environmental monitoring" J Electrochem Soc 165, pp.B3098 [40] Novotny, L., & Hecht, B (2012) "Principles of nano-optics" Cambridge university press [41] Moskovits, M (2005) "Surface‐enhanced Raman spectroscopy: a brief retrospective" J Raman Spectrosc 36, pp.485-496 Devec , İ , & Mercimek, B (2019) "Performance of SiO2/Ag Core/Shell particles in sonocatalalytic degradation of Rhodamine B" ULTRASON SONOCHEM 51, pp.197-205 [43] Li, Yuanyuan, Zhu, Nan, Ma, Yulong, Li, Qiang, Li, Peng (2018) "Preparation of polysaccharide-based chiral stationary phases on SiO2@Ag core–shell particles by means of coating and intermolecular polycondensation and comparative liquid chromatography enantioseparations" Anal Bioanal Chem 410, pp.441-449 [44] Qin, R., Li, G., Pan, L., Han, Q., Sun, Y., & He, Q (2017) "Preparation of SiO2@ Ag composite nanoparticles and their antimicrobial activity" J Nanosci Nanotechnol 17, pp.2305-2311 [45] Jiang, Z J., Liu, C Y., & Sun, L W (2005) "Catalytic properties of silver nanoparticles supported on silica spheres" J Phys Chem B 109, pp.1730-1735 [46] You, M., Yang, S., Tang, W., Zhang, F., & He, P (2018) "Molecularly imprinted polymers-based electrochemical DNA biosensor for the determination of BRCA-1 amplified by SiO2@Ag" Biosens Bioelectron 112, pp.72-78 [47] Ashurov, M S., Eremina, E A., Abdusatorov, B A., & Klimonsky, S O (2019) "Synthesis of SiO2@ Ag core-shell photonic crystals for SERS application" J Phys Conf Ser 1410, pp.012165 [48] Chi, Y., Yuan, Q., Li, Y., Tu, J., Zhao, L., Li, N., & Li, X (2012) "Synthesis of Fe3O4@SiO2–Ag magnetic nanocomposite based on small-sized and highly dispersed silver nanoparticles for catalytic reduction of 4-nitrophenol" J Colloid Interface Sci 383, pp.96-102 [49] Ma, P., Liang, F., Diao, Q., Wang, D., Yang, Q., Gao, D., & Wang, X (2015) "Selective and sensitive SERS sensor for detection of Hg2+ in environmental water base on rhodamine-bonded and amino group functionalized SiO2-coated Au– Ag core–shell nanorods" RSC Advances 5, pp.32168-32174 56 an [50] Jackson, J B., & Halas, N J (2001) "Silver nanoshells: variations in morphologies and optical properties" The Journal of Physical Chemistry B 105, pp.2743-2746 [51] Averitt, R D., Sarkar, D., & Halas, N J (1997) "Plasmon resonance shifts of Au-coated Au S nanoshells: insight into multicomponent nanoparticle growth" Physical Review Letters 78, pp.4217 [52] Nikhil, B., Pawan, J., Nello, F., & Pedro, E (2016) "Introduction to biosensors" Essays Biochem 60, pp.1-8 Asa , , Öze , Ö , Şa er, , & Po atoğ u, İ 8) "Rece t eve o me ts in enzyme, DNA and immuno-based biosensors" Sensors 18, pp.1924 [54] Vo-Dinh, T., & Cullum, B (2000) "Biosensors and biochips: advances in biological and medical diagnostics" Fresenius J Anal Chem 366, pp.540-551 [55] Marazuela, M., & Moreno-Bondi, M (2002) "Fiber-optic biosensors–an overview" Anal Bioanal Chem 372, pp.664-682 [56] Gaudin, Valérie (2017) "Advances in biosensor development for the screening of antibiotic residues in food products of animal origin – A comprehensive review" Biosensors and Bioelectronics 90, pp.363-377 [57] Turner, A P (2013) "Biosensors: sense and sensibility" Chemical Society Reviews 42, pp.3184-3196 [58] Flanagan, S (Ed.) (2014) "Handbook of food allergen detection and control" Elsevier [59] Kim, G B., Guo, J., Hu, J., Shan, D., & Yang, J (2016), "Novel applications of urethane/urea chemistry in the field of biomaterials".Elsevier: Elsevier; 2016, pp 115-147 [60] Andersson, K., Areskoug, D., & Hardenborg, E (1999) "Exploring buffer space for molecular interactions" Journal of Molecular recognition 12, pp.310315 [61] Aizowd, M (1994) "Immunosensors for clinical analysis" Advances in clinical chemistry pp.247 [62] Choi, J H., Lee, J H., Son, J., & Choi, J W (2020) "Noble Metal-Assisted Surface Plasmon Resonance Immunosensors" Sensors 20, pp.1003 57 an [63] Arcas, A D S., Dutra, F D S., Allil, R C., & Werneck, M M (2018) "Surface plasmon resonance and bending loss-based U-shaped plastic optical fiber biosensors" Sensors 18, pp.648 [64] Zheng, Lingyan, Cai, Gaozhe, Wang, Siyuan, Liao, Ming, Li, Yanbin, Lin, Jianhan (2019) "A microfluidic colorimetric biosensor for rapid detection of Escherichia coli O157:H7 using gold nanoparticle aggregation and smart phone imaging" Biosensors and Bioelectronics 124-125, pp.143-149 [65] Zhou, Y., Xu, H., Wang, H., & Ye, B C (2020) "Detection of breast cancerderived exosomes using the horseradish peroxidase-mimicking DNAzyme as an aptasensor" Analyst 145, pp.107-114 [66] Raghu, D., Christodoulides, J A., Christophersen, M., Liu, J L., Anderson, G P., Robitaille, M., & Raphael, M P (2018) "Nanoplasmonic pillars engineered for single exosome detection" PloS one 13, pp.e0202773 [67] Ma, Xiaoming, Lin, Yue, Guo, Longhua, Qiu, Bin, Chen, Guonan, Yang, Huang-hao, Lin, Zhenyu (2017) "A universal multicolor immunosensor for semiquantitative visual detection of biomarkers with the naked eyes" Biosensors and Bioelectronics 87, pp.122-128 [68] Zhang, Q Y., Chen, H., Lin, Z., & Lin, J M (2012) "Comparison of chemiluminescence enzyme immunoassay based on magnetic microparticles with tra t o a co or metr c ELISA or t e etect o o serum α-fetoprotein" Journal of pharmaceutical analysis 2, pp.130-135 [69] Lee, Jong Uk, Nguyen, Anh H., Sim, Sang Jun (2015) "A nanoplasmonic biosensor for label-free multiplex detection of cancer biomarkers" Biosensors and Bioelectronics 74, pp.341-346 [70] Liang, J., Yao, C., Li, X., Wu, Z., Huang, C., Fu, Q., & Tang, Y (2015) "Silver nanoprism etching-based plasmonic ELISA for the high sensitive detection of prostate-specific antigen" Biosensors and Bioelectronics 69, pp.128-134 [71] Zhang, K., Song, C., Li, Q., Li, Y., Yang, K., & Jin, B (2010) "The establishment of a highly sensitive ELISA for detecting bovine serum albumin (BSA) based on a specific pair of monoclonal antibodies (mAb) and its application in vaccine quality control" Human vaccines 6, pp.652-658 [72] Jia, Kun, Khaywah, Mohammad Y., Li, Yugang, Bijeon, Jean L., Adam, Pierre M., Déturche, Régis, Ionescu, Rodica E (2014) "Strong Improvements of Localized Surface Plasmon Resonance Sensitivity by Using Au/Ag Bimetallic Nanostructures Modified with Polydopamine Films" ACS Applied Materials & Interfaces 6, pp.219-227 58 an [73] Perkampus, H H (2013) "UV-VIS Spectroscopy and its Applications" Springer Science & Business Media [74] Dada, A O., Adekola, F A., Adeyemi, O S., Bello, O M., Oluwaseun, A C., Awakan, O J., & Grace, F A A (2018), "Exploring the effect of operational factors and characterization imperative to the synthesis of silver nanoparticles".IntechOpen: IntechOpen; 2018, pp [75] Seyforth, J A (2015) "Scanning Electron Microscopy (SEM): An Introduction to the use of SEM for character- ising the Surface Topology and Composition of Matter with Further Applications" Experimental Techniques In Condensed Matter Physics [76] Bumbrah, G S., & Sharma, R M (2016) "Raman spectroscopy–Basic principle, instrumentation and selected applications for the characterization of drugs of abuse" Egypt J Forensic Sci 6, pp.209-215 77 Da , au e 8), " c ƣơ â t c cấu trúc nano".Đại học Quốc gia TP.H Chí Minh: Đại học Quốc gia TP.Hồ Chí Minh; 2018, pp 42-45 [78] Meulendijks, N., Van Ee, R., Stevens, R., Mourad, M., Verheijen, M., Kambly, N., & Buskens, P (2018) "Flow cell coupled dynamic light scattering for realtime monitoring of nanoparticle size during liquid phase bottom-up synthesis" Appl Sci 8, pp.108 [79] Ashurov, M S., Eremina, E A., Abdusatorov, B A., & Klimonsky, S O (2019) "Synthesis of SiO2@Ag core-shell photonic crystals for SERS application" J Phys Conf Ser 1410, pp.012165 [80] Williams, Paul Melvyn (2016), "Zeta Potential".Springer Berlin Heidelberg, Berlin, Heidelberg: Springer Berlin Heidelberg; 2016, pp 2063-2064 [81] Hue, Do Thi (2018) "Nghiên cứu chế tạo khảo sát tính chất quang cấu trúc nano vàng dạng cầu, dạng dạng lõi/vỏ s ca v đị ƣớng ứng dụng y sinh" Hà Nội [82] Minh, N T., Hung, D D., Thang, C S., & Duc, T M (2015) "Zeta study of water samples on Ba and Dong Nai river basins" VJES 37 [83] Saegusa, T., & Chujo, Y (1990) "An organic/inorganic hybrid polymer" J Macromol Sci 27, pp.1603-1612 [84] Kozuka, H., Yamano, A., Fujita, M., & Uchiyama, H (2012) "Aqueous dipcoating route to dense and porous silica thin films using silica nanocolloids with an aid of polyvinylpyrrolidone" J Sol-Gel Sci Technol 61, pp.381-389 59 an [85] Wu, Z G., Jia, Y R., Wang, J., Guo, Y., & Gao, J F (2016) "Core-shell SiO2/Ag composite spheres: synthesis, characterization and photocatalytic properties" Mater SCI-Poland 34, pp.806-810 [86] Feng, X., Li, H., Zhang, Q., Zhang, P., Song, X., Liu, J., & Gao, L (2016) "SiO2–Ag–SiO2 core/shell structure with a high density of Ag nanoparticles for CO oxidation catalysis" Nanotechnology 27, pp.455605 [87] Adamson, A W., & Gast, A P (1997) "Physical Chemistry of surfaces" Wiley, New York; 1997, pp [88] Xiong, Y., & Lu, X (2015) "Metallic Nanostructures" Springer [89] Gurunathan, S., Kalishwaralal, K., Vaidyanathan, R., Venkataraman, D., Pandian, S R K., Muniyandi, J., & Eom, S H (2009) "Biosynthesis, purification and characterization of silver nanoparticles using Escherichia coli" Colloids Surf B 74, pp.328-335 [90] Kredy, H M (2018) "The effect of pH, temperature on the green synthesis and biochemical activities of silver nanoparticles from Lawsonia inermis extract" Int J Pharm Sci Res 10, pp.2022-2026 [91] Liu, H., Zhang, H., Wang, J., & Wei, J (2020) "Effect of temperature on the size of biosynthesized silver nanoparticle: deep insight into microscopic kinetics analysis" Arab J Chem 13, pp.1011-1019 [92] Abdel-Mohsen, A M., Abdel-Rahman, R M., Fouda, M M., Vojtova, L., Uhrova, L., Hassan, A F., & Jancar, J (2014) "Preparation, characterization and cytotoxicity of schizophyllan/silver nanoparticle composite" Carbohydr Polym 102, pp.238-245 [93] Darroudi, M., Ahmad, M B., Zamiri, R., Zak, A K., Abdullah, A H., & Ibrahim, N A (2011) "Time-dependent effect in green synthesis of silver nanoparticles" Int J Nanomedicine 6, pp.677 [94] Li, L., Sun, J., Li, X., Zhang, Y., Wang, Z., Wang, C., & Wang, Q (2012) "Controllable synthesis of monodispersed silver nanoparticles as standards for quantitative assessment of their cytotoxicity" Biomaterials 33, pp.1714-1721 [95] Prathna, T C., Chandrasekaran, N., Raichur, A M., & Mukherjee, A (2011) "Biomimetic synthesis of silver nanoparticles by Citrus limon (lemon) aqueous extract and theoretical prediction of particle size" Colloids Surf B Biointerfaces 82, pp.152-159 60 an [96] Yang, Z., Qian, H., Chen, H., & Anker, J N (2010) "One-pot hydrothermal synthesis of silver nanowires via citrate reduction" J Colloid Interface Sci 352, pp.285-291 [97] McClary, F A., Gaye-Campbell, S., Ting, A Y H., & Mitchell, J W (2013) "Enhanced localized surface plasmon resonance dependence of silver nanoparticles on the stoichiometric ratio of citrate stabilizers" J Nanoparticle Res 15, pp.1442 [98] Phatangare, A B., Dhole, S D., Dahiwale, S S., Mathe, V L., Bhoraskar, S V., Late, D J., & Bhoraskar, V N (2016) "Surface chemical bonds, surfaceenhanced Raman scattering, and dielectric constant of SiO2 nanospheres in-situ decorated with Ag-nanoparticles by electron-irradiation" Journal of Applied Physics 120, pp.234901 [99] Ren, M., Jin, Y., Chen, W., & Huang, W (2015) "Rich capping ligand–Ag colloid interactions" The Journal of Physical Chemistry C 119, pp.27588-27593 [100] Wang, C B., Deo, G., & Wachs, I E (1999) "Interaction of polycrystalline silver with oxygen, water, carbon dioxide, ethylene, and methanol: in situ Raman and catalytic studies" The Journal of Physical Chemistry B 103, pp.5645-5656 [101] Peszke, J., Dulski, M., Nowa , A , a , , Zu o, , Sułow cz, S , & Mrozek-Wilczkiewicz, A (2017) "Unique properties of silver and copper silicabased nanocomposites as antimicrobial agents" RSC Advances 7, pp.28092-28104 [102] Gailliez‐Degremont, E., Bacquet, M., Laureyns, J., & Morcellet, M (1997) "Polyamines adsorbed onto silica gel: a Raman microprobe analysis" Journal of applied polymer science 65, pp.871-882 [103] Amyab, S P., Saievar-Iranizad, E., & Bayat, A (2016) "Platinum nanoparticles with superacid-doped polyvinylpyrrolidone coated carbon nanotubes: electrocatalyst for oxygen reduction reaction in high-temperature proton exchange membrane fuel cell" RSC Advances 6, pp.41937-41946 61 an S an K L 0 ... 16130018 Tên đề tài: Nghiên cứu tổng hợp vật liệu SiO2 bọc Ag, tiềm ă học miễn học sử dụng cảm biến sinh Nội dung khóa luận: - Tổng hợp vật liệu SiO2 bọc Ag bằ ƣơ óa ọc Nghiên cứu thay đổi yếu tố... liệu SiO2 bọc Ag, tiềm ă sử dụng cảm biến sinh học miễn dịch? ?? ằm nghiên cứu tổng hợp vật liệu SiO2 bọc Ag ƣơ hóa học ƣơ ản, tốn chi phí, thiết bị giản Các yếu tố ả ƣở đến trình tổng hợp vật liệu. .. cảm biến không nhãn sử dụng kỹ thuật PCR với vật liệu SiO2 bọc Ag phù hợp tiết kiệm chi phi nhiều sản xuất 1.6 ác cá trƣớc ây cảm biến sinh học miễn dịch Việc sử dụng cảm biến sinh học miễn dịch