Test instruction TIGER DRYLAC Quality Control Powder coating of test sheet metals PA 08 Approved by: Ing. Mathe Issue date October 2001 Update status 08 Folder - Nr HQ 03 - 18 page 1/2 1. Purpose / Target: The conditions are to be determined for coating test sheet metals with powder coatings. 2. Description of the procedure: Testing sets: cup pistol warming cupboard cabinet coating Cab system parameters The system adjustments for the coating are: - Voltage : 50 - 60 kV - Incoming air : 4 - 6 bar - Dosing air : 4 - 6 bar Execution The powder sample is filled into the cup of the pistol, and the required sheet metals are coated with the film strength stated below. With system attempts and pallet samples only a non- chromated box sheet metal is coated. The powdered sheet metals are burned with the burning conditions given in the table (temperature, time) in a circulating air drying furnace. After the cooling the sheet metals will be provided with the filled out labels (system attempt and pallet samples: with the label of the machinist). Test instruction TIGER DRYLAC Quality Control Powder coating of test sheet metals PA 08 Approved by: Ing. Mathe Issue date October 2001 Update status 08 Folder - Nr HQ 03 - 18 page 2/2 3. Parameters : Film thickness of the test sheet metals Surface Short form Film strength / µm smooth, independent from gloss degree GL 60 - 80 basic structure, indep. from gloss degree GS 90 - 120 fine structure FS 70 - 90 Hammer blow HS 100 - 120 Wrinklefinish WF 90 -120 Glitter effects 100 - 120 Series 28 40 - 60 These specification generally apply, excluded other parameters are indicated on the prescription or the product route card. Types of the test sheet metals: Nomenclature Mass / mm Box sheet metal 69 x 119 QUV - sheet metal 75 x 147 DIN A4 - sheet metal 300 x 200 DIN A5 - sheet metal 200 x 150 Original sheet metals variable Special test sheet metals : - Glazes : With glazes additionally a nickel plated test sheet metal with the film strength of 50 must - 80 µm has to be coated. - Colorless, Glitter and similar effects: With colorless products additionally a black and white test sheet metal must be coated. Film strength 50 - 80 µm. - 2-film luminous paints: These luminous paints must be coated on white background (49/11100). Layer strength 50 - 80 µm. A sheet metal is to be coated for mechanical check normally. - 2-film metallic-lacquers: Additionally a box sheet metal must be coated and controlled with the appropriate colorless powder coating. - Base powder coatings for the department Coating Tec must be coated with the series 29, 17, 68, 58 only a chromated and a non-chromated box sheet metal. Burning conditions and checking sheet metals: The up-to-date valid data are summarized by the quality technique in form of a table and distributed to the departments concerned informally. Additionally the current status can be queried at any time over the network: X:\QU- Managementdata.qs\PA08-BEI.DOC Test instruction TIGER DRYLAC Quality Control Powder coating of test sheet metals PA 08 Approved by: Ing. Mathe Issue date October 2001 Update status 08 Folder - Nr HQ 03 - 18 page 3/2 . and controlled with the appropriate colorless powder coating. - Base powder coatings for the department Coating Tec must be coated with the series 29,. determined for coating test sheet metals with powder coatings. 2. Description of the procedure: Testing sets: cup pistol warming cupboard cabinet coating Cab

Ngày đăng: 12/12/2013, 00:15

TỪ KHÓA LIÊN QUAN

w