ASM Metals Handbook - Desk Edition (ASM 1998) WW part 15 ppt

... sheet metal part; the product of the first drawing operation. (2) Any cylindrical part or shell closed at one end. o cup-and-cone-fracture o A mixed-mode fracture, often seen in tensile-test specimens ... where the central portion undergoes plane-strain fracture and the surrounding region undergoes plane-stress fracture. It is called a cup fracture (or cup-and-cone fracture) because o...

Ngày tải lên: 10/08/2014, 20:20

... methyl di-isocyanate (MDI). Part A is usually used between 1 and 2% by weight of sand, and part B is used between 2 and 10% of the weight of part A. Part C is added between 18 and 20% of part A ... between 150 and 200 °C (300 to 400 °F). The phenolic urethane no-bake system is a three -part system consisting of the following: part I, a phenol formaldehyde resin dissolved in...

Ngày tải lên: 10/08/2014, 20:20

... the solvent. Modifications of this cleaning process include vapor-spray-vapor, warm liquid-vapor, boiling liquid-warm liquid-vapor, and ultrasonic degreasing. o vapor deposition o See chemical ... solidifying metals. o zincrometal o A steel coil-coated product consisting of a mixed-oxide underlayer containing zinc particles and a zinc-rich organic (epoxy) topcoat. It is weldable, for...

Ngày tải lên: 10/08/2014, 20:20

... Desk Edition, 1984, is also included. Nondestructive Testing Ti-5Al-2.5Sn 4.46 0.161 Ti-2Fe-2Cr-2Mo 4.65 0.168 Ti-8Mn 4.71 0.171 Ti-7Al-4Mo 4.48 0.162 Ti-4Al-4Mn 4.52 0.163 Ti-4Al-3Mo-1V ... 2 0-1 00 11.0 1.08% C 2 0-1 00 10.8 1.45% C 2 0-1 00 10.1 Invar (36% Ni) 20 2.0 13Mn-1.2C 20 18.0 13Cr-0.35C 2 0-1 00 10.0 12.3Cr-0.4Ni-0.09C 2 0-1 00 9.8 17.7Cr-9.6Ni-0.06C 2...

Ngày tải lên: 10/08/2014, 20:20

... stabilization (Ti-Al), (b) β stabilization with complete miscibility (Ti-V), and (c) β stabilization with a eutectoid reaction (Ti-Cr). Source: Ref 7 The Iron-Carbon System. The iron-carbon diagram ... Range C23000 Red brass, 85% 15 14. 0-1 6.0 C24000 Low brass, 80% 20 18. 5-2 1.5 C26000 Cartridge brass, 70% 30 28. 5-3 1.5 C27000 Yellow brass, 65% 35 32. 5-3 7.0...

Ngày tải lên: 10/08/2014, 20:20

... (XM-14) 0.12 14. 0- 16.0 1.00 17. 0- 19.0 5. 0-6 .0 0.060 0.030 0.3 5-0 .50 N S 2150 0 Esshete 1250 0 .15 5. 5-7 .0 1.20 14. 0- 16.0 9. 0-1 1.0 0.040 0.030 0.00 3-0 .009 B; 0.7 5-1 .25 Nb; 0.1 5-0 .40 ... 7. 0-9 .0 3. 5- 4.5 16. 0- 18.0 8. 0-9 .0 0.040 0.030 0.0 8-0 .18 N S21900 Nitronic 40 (XM-10) 0.08 8. 0-1 0.0 1.00 19. 0-...

Ngày tải lên: 10/08/2014, 20:20

... A-U5GT S, P 0.20 0.35 4. 2-5 .0 0.10 0.1 5-0 .35 . . . 0.05 0.10 0.1 5-0 .30 0.05 0.05 0 .15 bal 204.2 A-U5GT Ingot 0 .15 0.1 0- 0.20 4. 2-4 .9 0.05 0.2 0-0 .35 . . . 0.03 0.05 0.1 5-0 .25 0.05 0.05 0 .15 ... 0.10 0 .15 4. 2-5 .0 0.2 0- 0.50 0.1 5-0 .35 . . . 0.05 0.10 0.1 5-0 .30 0.05 0.05 0 .15 bal 206.2 . . . Ingot 0.10 0.10 4. 2-5 .0 0.2 0- 0.50 0...

Ngày tải lên: 10/08/2014, 20:20

... 5 0.1 5-0 .48 0.00 6-0 .019 186 27.0 228 33.0 152 22.0 . . . . . . 2 0.5 1-1 .27 0.02 0-0 .050 186 27.0 228 33.0 152 22.0 . . . . . . 3 5050-H36 (d) 1.2 9-4 .11 0.05 1-0 .162 ... 12.7 0- 25.40 0.50 0- 1.000 . . . . . . 152 22.0 . . . . . . . . . . . . 18 6061-O sheet and plate 25.4 3- 76.20 1.00 1- 3.000 . . . . . . 152 22.0 . . ....

Ngày tải lên: 10/08/2014, 20:20

... 4 3-8 8 10 3-5 17 1 5-7 5 4 6-2 30 C42500 F 31 0- 634 4 5-9 2 12 4-5 24 1 8-7 6 4 9-2 30 C43000 F 31 7- 648 4 6-9 4 12 4-5 03 1 8-7 3 5 5-3 30 C43400 F 31 0- 607 4 5-8 8 10 3-5 17 1 5-7 5 4 9-3 30 C43500 F, T 31 7- 552 ... 6 9-4 55 1 0-6 6 3 6-2 20 C15500 F 27 6- 552 4 0-8 0 12 4-4 96 1 8-7 2 4 0-3 20 C15710 R, W 32...

Ngày tải lên: 10/08/2014, 20:20

... radiographic absorption equivalence for various metals X-rays, kV X-rays, MeV Gamma rays Material 50 100 150 220 400 1 2 4-2 5 Ir-192 Cs-137 Co-60 Ra Magnesium 0.6 0.6 0.05 0.08 ... 6061-T6 41 42 7075-T6 53 32 2024-T4 52 30 Magnesium 46 37 7 0-3 0 brass 62 28 Phosphor bronzes 160 11 Monel 482 3.6 Zirconium 500 3.4 Zircaloy-2 720 2.4 Titanium...

Ngày tải lên: 10/08/2014, 20:20