Nghiên cứu ảnh hưởng của sự biến đổi bề mặt một số khoáng chất đến tương tác pha và tính chất cơ lý của vật liệu tổ hợp trên cơ sở nhựa nền polypropylen tt tieng anh

1 PREFACE Urgency of the thesis Reinforcement of thermoplastic by using particle has studied in few decades ago Until now, it plays an important role in as well [1] The flexibility of thermoplastic composite materials expands the scope of application in the life and research field When the materials are reinforced by fillers, their properties are changed Typically, the filler impacts in hardness, thermal conductivity, thermal expansion However, they improve strength and elasticity as well because of the filler properties and the changing of morphology matrix The inorganic filler are used wide in thermoplastic such as CaCO3, talc, SiO2, mice and Mg(OH)2 Most of the researches carried paying attention on the factors such as (i) component; (ii) shape and size; (iii) composition; (iv) compatibility of matrix and filler Some of them showed a polymer layer locating aninteraction phase between filler surface and matrix which have special property However, the role, influenceand a parameters relationship ofthe phase interaction betweenthe filler and the matrix on the mechanical properties (i.e tensile strength, impact resistance) is not determined clearly Thus, supervisor and PhD student carried on a thesis:” Effect of surface fillers modification on phase interaction and mechanical properties of thermoplastic materials” The aim of thesis To study relation of molecular structural changing between polypropylene microcomposite system and the particle fillers with varies phase interactions by using solid-state NMR(ssNMR) spectra.Therein,emphasizing the molecular flexibility on mechanical properties of materials Main contents of thesis a Preparing polypropylene composites materials by using the filler was modified/unmodified surface at varies contents b Research phase interaction morphology, determine the mechanical properties of materials including tensile strength and impact resistance (integral J) c Application of solid-state nuclear magnetic resonance (ss-NMR) method to determine molecular mobility in polymer composite materials, study the relation of mechanical properties of material Outline of the thesis: The thesis has 24 pages including introduction, chapters of content, contributions and a list of publication The main results of the thesis are published in: - 01 article in an international journal in the ISI list (IF = 3.7) - 04 articles in national journal - 05 reports in the International Science Conference (1 international conference to publish ISBN) Chapter 1: INTRODUCTION 1.1 Thermoplastic polypropylene Polypropylene (PP) was invented by research groups in the United States and Europe in the early 1950s The commercial production of PP began in 1957 in the US and in 1958 in Europe On the other hand, PP ranks first in the largest volumes group of thermoplastic products used such as: polyethylene (PE), polyvinylchloride (PVC) and polystyrene (PS) Average consumption of PP increases about 10% per year and the trend will keep increasing in future The flexibility is important property of PP The structure and characteristics (including processing) of PP can be adjusted according to usage requirements Polypropylene has many advantagedproperties such as low density, chemical resistance, easy processing and recyclability In addition, its mechanical properties are well suited to engineering plastics Besides, PP also has some disadvantages such as deteriorationin properties at low temperatures and low impact resistance Thus, PP copolymers and their blendsare studied to develop in commercial fields 1.2 Polymer composite materials base on fillers reinforced PP Fillers reinforced PP composite materials have been used in large quantities in many different fields such as automotive, furniture, electrical equipment, etc Because of the relation between cost and achieved properties, filler reinforced PP composites are used widely and gradually replaced ABS inthe traditional fields Other materials like Many efforts have been made to expand its scope of application in engineering thermoplastic materials There are many types of reinforced fillers using in PP, however, CaCO3, talcand fiber glass play the most important role and will keep it in the near future including In thermoplastic market, CaCO3 consumptionmakes up a majority of the filler field However,talc mineral ranks first inthe PP market, CaCO3 only ranks second and glass fiber follow Hence, glass fiber reinforced PP is studied to improve its capabilities and expand its scope of application In despite of many efforts,they are still potential and expectant researches In reality, application and the growth rate of fiber glass for PP are lower than that of particle fillers Nowadays, not only the technical and aesthetic requirements but also the costs of processing and raw materialsare increasing To meet these requirements, the researchers need understanding the relevant properties of fillers as well as their influence on the structure and properties of composite materials touse all the advantages of fillers or just use them as diluents forreducing costs 1.3 Solid state magnetic resonance spectroscopy and its application for molecular mobility in polypropylene composites Today, the high-resolution 13 C NMR spectrum is a common tool for studying the structure of polymers H-NMR isa standard technique in structural analysis of liquid-state substances, but in solidstate substances Isotactic polypropylene isa polymorphic material due to a modifying arrangement of polymer chains Hence, ss-NMR spectroscopy technique showed complicatedanalysis for polypropylene.It is more complicated particularlyif the composition of these components that plays a decisive role changing the properties of polymer is significantly lower than composition of the matrix This difference prevents the use calibration curve analysis Therefore, special method must be used to describe the small differences between the amorphous and crystals disordering in the phase interaction region However, the less attention has been paid to the multi-molecular analysis of the ss-NMR spectrum for amorphous or disordered solids, which can be considered an extreme limit due to the frequency range being too much for signals for which only one signal is available are defined Therefore, the thesis also demonstrates that 13 C MAS ss-NMR spectrocopy is a fast, reliable tool for describing extremely complex crystal forms in PP material for clarifying the relationship between spectral data at the molecular level and the macroscopic properties of materials such as mechanical properties 1.4 These studies were carriedon in Vietnam The basic researches in Vietnam on thermoplastic composite materials in general and polypropylene in particular were studied by Hoang Thai and et al at the Institute of Tropical Technology and Dieu Tran Vinh and et al at Hanoi University of Technology Hoang Thai et al treated titan dioxide or nano BaSO4 surface by silane coupling agent for studying mechanical properties and morphological structure of titan dioxide or nano BaSO4 filled polypropylene composites This surface modification process improved significantly the mechanical properties of composite materials Tensile strength and elastic modulus of PP composite materials with 2% of surfacemodified nanoparticles are 42 Mpa and 979 Mpa, respectively Based on results of the cumulative module (G ') and phase interaction from X-ray diffraction analysis and FE-SEM, they showed that the properties and phase interaction of the material containing modified nanoparticle are better than these of the material containing unmodified nanoparticle Besides, the research team of Prof Hoang Thai mixed melting polypropylene and vinysilane modified fly ash particles The effect of fly ash content on viscosity, mechanical properties and material morphology was determined The results indicated that the viscosity of the mixture decreased with increasing fly ash content Tensile strength and elongation at break of the material with different loading of untreated fly ash are lower than the original PP After modifying by vinyl silane,PP / fly ash composite material showed higher tensile strength and elongation at break while viscosity of the mixture was lower The research team of Prof Dieu Tran Vinh had many studies on composite materials based organic fibers reinforced polypropylene They was considered that the adhesion between the plastic substrate and polar organic fiber affects incredibly the properties of the composite Thus, maleic anhydride– grafted polypropylene (MA-g-PP) compatibilizer or acetic anhydride and acrylonitrile was used Comparing the mechanical properties of polypropylene composite materials containing jute fibers and glass fibers, although tensile strength and elastic modulus of jute were lower than that of fiberglass, the specific module of jute was higher than glass fiber, and the module cost of jute is much higher than that of fiberglass The effect of jute and MAPP on PP tensile and flexural strength were determined When 50% weight of jute is loaded, the flexural strength of PP increases from 31.33 Mpa to 49.97 Mpa and increases sharply to 87.66 Mpa when adding 3% of MAPP weight Tensile strength does not increase much without MAPP However, when MAPP has tensile strength, composites increase about times (from 28.92 MPa to 59.12 MPa) Similarly, composite is reinforced with NaOH solution treated short bamboo fiber adding 0.6% of MAPP compatibilizer, its tensile strength, flexural strength and impact strength are respectively increased by 24%; 23% and 40% compared with its of raw PP The team also carried on the acetylation of bamboo fibers and determined the effect of this process on the reinforcement of polypropylene based composite material Acetylation reduces the hygroscopic of bamboo fibers, increases the adhesion between bamboo fibers and PP resin 50% of short bamboo fibers reinforced PP composites has the highest tensile strength (36.45 MPa), increase of 2% compared with its raw PP Chapter EXPERIMENTAL 2.1 Materials 2.1.1 Polymer Isotactic polypropylene homopolymer Mosten 52.412 (Chemopetrol, Czech Republic) was used as a matrix in this study 2.1.2 Fillers Glass beads, average size ~ 20 µm supplied by SOVITEC, France Calcium carbonate, average particle size ~ 1.7 µm (1VA) and ~ 12 µm (15VA), supplied by Omycarb, Switzerland Talc mineral originated from Thanh Son district, Phu Tho province, Vietnam The main components of this mineral are SiO2 (60,82 %) and MgO (32,16 %) Average particle size ~ 6,58 µm 2.1.3 Surface modification agents Vinyltriethoxysilane supplied by Momentive (Switzerland) and methacryloxy propyltrimethoxysilane supplied by DowCorning (USA) Oleic and stearic acids (technical grade products supplied by Sigma-Aldrich) were used for calcium carbonate surface modification 2.1.4 Other materials Dicumyl peroxite (technical grade ) supplied by Sigma-Aldrich 2.2 Methods 2.2.1 Surface modification The surface modification of filler particles is carried out in 96% ethanol solution containing 2% of the surface modification agent 2.2.2 Composite preparation Polypropylene and fillers were been compounded in the twin-screw compounder (extruder) Brabender DSE and subsequently injection-molded into form of specimens (dog-bone) by ENGEL Spex victory 50 machine 2.3 Properties assessment 2.3.1 Morphology The morphology was assessed by scanning electron microscope (SEM) taken on impact fracture cross-section of composites 2.3.2 Tensile properties Tensile mechanical tests were carried out on Instron 5800 material tester at room temperature and cross-head speeds alternating of mm/min and 50 mm/min 5 2.3.3 Impact properties An instrumented Charpy impact tester Ceast Resil Impactor with 7,5J work capacity was used for the J-integral evaluation 2.3.4 ss-NMR The ss-NMR experiments were performed using a Bruker Avance 500 WB/US NMR (Karlsruhe, Germany, 2003; B0 ¼ 11.7 T) with mm ZrO2 rotors at a MAS frequency of kHz The 13C crosspolarization (CP) MAS NMR spectra were measured with a B1(13C) field nutation frequency of 62.5 kHz, a contact time of 1.75 ms and a recycle delay of s To record the T1-filtered, domain-selective spectra of the highly mobile components, the single-pulse 13C MAS NMR spectrawere measured with a repetition delay of s The VT experiments were performed in the temperature range from 295 to 355 K The frictional heating of the sample was compensated, and the sample temperature was calibrated using the 207Pb chemical shift in Pb(NO3)2 2.3.5 Factor analysis (FA) FA is a method that uses the Singular Value Decomposition (SVD) algorithm to extract specific information from experimental data This technique allows visualization and distinguishing subtle differences between the prepared PP/CaCO3 microcomposites in 2D or 3D maps Chapter 3: RESULS AND DISCUSION 3.1 Composite based on polypropylene and glass beads 3.1.1 Morphology observation The introduction of inorganic filler into a polymer matrix results in a heterogeneous system Adhesion among different materials is created by physical or chemical bonds between the adhesive and the substrate, and this depends on the selection of coupling agent Figure 3.1 presents structure morphology taken of the impact fracture cross section of PP/glass beadcomposites with 20% of filler content a) b) c) Fig 3.1 Degree of interfacial adhesion between glass bead and PP matrix As revealed by SEM in the cases of non-treated and NO adhesion, there was a poor interfacial with the strong debonding of particles While in case of GOOD adhesion, a strong bonding achieved between glass bead particles and PP matrix, coated spheres adhere to the matrix 3.1.2 Tensile properties The effects of glass bead with different surface properties on the mechanical properties of composites are showed in Fig 3.2 It can be sheen that the tensile moduli in all cases of composites increase with increasing filler loading Generally, the addition of rigid particulate fillers increases stiffness, which is measured through Young's modulus This is due to the fact that fillers often exhibit higher stiffness compared matrix polymer Besides, Young's modulus is measured at the very beginning of a tensile test, where deformation is insufficient to cause particle-matrix debonding However, obtained results indicated slightly change in value among cases of no-treated, NO adhesion and GOOD adhesion This comes from the difference in adhesion between particles and polymer matrix with zero adhesion in case of NO adhesion and a strong adhesion in case of GOOD adhesion The increasing in Young's modulus of glass bead-filled composites indicates an increase in the rigidity of PP related to the restriction of the mobility in PP matrix due to the presence of fillers This mechanical restraint resulted from the enhanced surface interaction between two phases in composites The similar trend also found in other studies that enhancement of the interfacial adhesion between the matrix and glass beads is helpful in improving the stiffness of filled PP composites Fig 3.2 Tensile properties of PP/Glass beads composites For particulate filled thermoplastic composites, it is generally believed that the interfacial adhesion between the filler particles and matrix is an important factor affecting strength and toughness of composites On the other hand, yield stress gives information on filler-matrix interactions and consequently it is one of the preferred methods of composite testing In thecase of a poor interaction (nontreated and NO adhesion) between the matrixand the filler, the interfacial layer cannot transferstresswas reflected by the lower yield stress value in comparison with a strong interaction in case of GOOD adhesion (Fig 3.2) Therefore, one can assume that the strengthof a particulate-filled composite is determined by theeffective available area of load borne by the matrix asa result of the absence of the filler The higher yield stress values in case of GOOD adhesion in comparison with cases of non-treated and NO adhesion at the corresponding concentration reflect the interaction between glass bead particles and polypropylene matrix On the other hand, it can be seen that in all cases, yield stress decreases with increasing filler loading.This is due to the fact that theconcentration of the inclusions is the main factoraffecting the yield strength of a filled polymer besidesthe interfacial adhesion between the fillers and matrix The presence of glass beads has a weakening effect on the composite due to debonding Poor adhesion and debonding reduce the volume fraction which can carry the applied load.Tensile strain at break is a parameter characterizing the extensibility of materialsand it is usually inversely proportional to tensile strength which means that increasing the tensile strength of filled material usually contributes to a decrease in the strain at break The strain at break value for composite of GOOD adhesion had a lowest strain at break value which corresponds with highest tensile strength value 7 3.1.3 Impact properties The J-integral was used to characterize the energy absorption of polymer materials at the initial stage of crack and the resistance for crack initiation Figure 3.3 showed Jld values of polypropylene and glass bead composites Fig 3.3 Impact strength of PP/glass beads composites The fracture behavior of polymers is strongly affected by the addition of rigid particles The incorporation of them into the polypropylene matrix leads to differences in the overall process of crack propagation and fracture The process starts with the plastic deformation of the matrix ahead of the initial crack The adsorption of polymer molecules on the filler surface through chemical bonds leads to the rigidity in structure of polymer chains This leads to earlier crack initiation and propagation with dramatically decreasing of J-integral value in case of GOOD adhesion (Figure 3.3) Plastic deformation of the matrix polymer is the main energy absorbing process in impact and this increases when the interaction between particles and polymer matrix is lowered in case of non-treated and NO adhesion 3.1.4 ss-NMR In general, narrowing of 1H lineshapes indicates the increase in global segmental dynamics as 1H1 H dipolar couplings are motionally averaged out As demonstrated in Figure 3.4 in our particular case, the most mobile polymers segments were found in parent PP Slightly hindered segmental dynamics in the composites Non-treated and NO-adhesion is reflected by the broadening of the corresponding signals The most rigid polymer segments were found in the composite GOOD-adhesion that is reflected by the broadest 1H MAS NMR line GOOD-adhesion Non-treated and NO adhesion PP Fig 3.4 1H MAS NMR spectra of the parent PP and composites recorded at 350 K and MAS kHz Similar trends were found in the 1H MAS NMR spectra measured with Hahn-echo (Figure 3.5) that allowed separation of relatively flexible fractions of polymer chains of amorphous phase GOOD-adhesion Non-treated PP and NO adhesion Hình 3.5 1H MAS Hahn-echo NMR spectra of the parent PP and composites recorded at 350 K and MAS kHz In contrast to solid-state 1H NMR spectra it is generally accepted that narrowing of 13C CP/MAS NMR signals indicates the increase in conformational ordering, and in extreme cases of perfectly evolved crystal phases very narrow signals are expected In polypropylene systems presence of polymorphic form alpha is reflected by the doublet of CH signal at ca 44 ppm The doublet is schematically indicated by dashed lines in Figure 3.6, and evolution of the narrow symmetric doublet requires long term annealing If considerable amount of amorphous phase is presented than the expected symmetrical doublet disappears 9 Rather an asymmetric broad line is expected Such a signal was detected for the parent PP (Figure 3.6) In contrast, the prepared composites exhibit symmetrization of the doublet and increase in spectral resolution This finding can be explained by the conformational ordering occurred particularly in the composite NO-adhesion (additional crystallization, reorganization of the amorphous phase, formation of protocrystalline phases etc….) GOOD-adhesion Non-treated NO-adhesion PP 13 Fig 3.6 C CP/ MAS NMR spectra of the parent PP and composites recorded at 300 K and MAS kHz 3.3 Composite based on polypropylene and calcium carbonate 3.3.1 Morphology observation The introduction of inorganic filler into a polymer matrix results in a heterogeneous system Adhesion between different materials is created by physical or chemical bonds between the adhesive and the substrate, and this depends on the selection of coupling agent The morphology of the compounds up to concentration of 40 wt% treated and untreated CaCO3 are shown in Figure 3.7 and Figure 3.8 The CaCO3 particles are generally supplied as agglomerates, however, it can be seen that aggregates are broken up to the primary particles during the extrusion process In the case of CaCO3 with average particle size ~ 1.7 µm, the interaction between untreated filler particles with the polymer matrix is stronger compared with treated filler particles (Figure 1a) The strong debonding of particles can be observed in cases of treated particles (Figure 3.7-b and 3.7-c) a b c Figure 3.7 SEM images of morphology of PP filled with a) untreated CaCO3, b) oleic acid treated CaCO3 and c) stearic acid treated CaCO3, average particle size ~ 1.7 µm, filler content 40 wt% 10 Similar trend was found in case of CaCO3 with higher size (12 µm, Figure 2) of filler particles, filler-matrix interaction in case of treated filler is lower compared with untreated filler a b c ) Figure 3.8 SEM images of morphology of PP filled with a) untreated CaCO3, b) oleic acid treated CaCO3 and c) stearic acid treated CaCO3, average particle size ~12 µm, filler content 40% wt 3.3.2 Tensile properties Tensile mechanical properties of composites of PP matrix with calcium carbonate particles were investigated (Figure 3.9) Generally, the addition of rigid particulate fillers increases stiffness, which is measured through Young modulus As can be seen in the figure, all the samples investigated in the present study show monotonic increasing of Young modulus values This is due to the fact that fillers often exhibit higher stiffness compared with polymer matrix Furthermore, Young modulus is measured at the very beginning of a tensile test, where deformation is insufficient to cause particle-matrix debonding Experimental results also indicated that, Young modulus of composites have none effect by particle size and surface modification Strength and toughness are very important for polymer composites used as structural materials For particulate filled thermoplastic composites, it is generally believed that the interfacial adhesion between the filler particles and matrix is an important factor affecting strength and toughness of composites As revealed by SEM, the lower adhesion in case of treated filler led to a decrease in yield stress of composites compared with untreated filler for both particle size, especially at filler content of 40 wt% In addition to the decreasing yield stress value as the filler content increases, the smaller of the particle size leading to the higher of value of tensile yield stress On the other hand, surface treatment reduced particleparticle interaction, therefore, reduced the aggregation of filler particles, resulting a better dispersion of particle filler in polymer matrix, increasing interface leading to increasing yield stress The extent of plastic deformation characterized by strain at break is then very sensitive to composition and morphology of the composites As shown in Figure 3.9, various types of calcium carbonate fillers have distinctly different effects in strain at break values 11 Figure 3.9 Effects of particle size, surface modification and filler loading on the tensile mechanical behaviour of injection-moulded specimens 3.3.3 Độ bền va đập J-integral was originally defined by Rice as a contour integral independent on the path, which express the energy per unit area necessary to create new fracture surfaces in a loaded body containing a crack Figure show J-integral values of PP/CaCO3 composites with different types of particle size, filler loading and surface properties 12 Figure 3.10 Fracture behaviour of PP/CaCO3 composites The addition of calcium carbonate led to a change in the fracture mode from brittle fracture for virgin PP to ductile fracture for the filled composites, which was attributed to the changes of stress fields in the PP matrix around the filler particles For the unfilled PP, when the notched composite specimen receives an impact load, the crazes will be rapidly developed cracks, and then will propagate toward the whole cross section The incorporation of rigid particles into the polypropylene matrix leads to differences in the overall process of crack propagation and fracture The process starts with the plastic deformation of the matrix ahead of the initial crack Assuming a poor bonding between filler and matrix in cases of treated calcium carbonate, the filler particles detach easily from the matrix by creating voids as observed by SEM These voids be formed will absorb impact deformation energy Otherwise, the particle will block the propagation of the crack developed from the crazes to increase the fracture resistance Jilken et al [8] also observed that the high impact strength, at high filler content, could be obtained for low aspect ratio filler, such as dolomite and calcium carbonate And this only obtains for sufficiently fine fraction and if the filler particles are good dispersion That is why J-integral values for composites of small particle size higher than those of large particle size The results in Figure 3.10 also showed that fracture resistance was increased up to 20 wt% of calcium carbonate 3.2.4 ss-NMR Two types of VT ss-NMR experiments were performed in a temperature range from 295 to 355 K The C CP/MAS NMR spectra preferentially detect rigid molecular segments When the 13C CP/MAS NMR spectra were acquired at 295 K, three signals corresponding to the CH2 (44 ppm), CH (26 ppm) and CH3 (21.3 ppm) groups were easily distinguished 13 13 Figure 3.11 13C CP/MAS NMR spectra at 295 Figure 3.12 13C MAS NMR spectra at 295 K K and 355 K of the pure PP and modified PP and 355 K of pure PP and modified PP At elevated temperatures (far above Tg), the segmental motion in the amorphous phase increased, as indicated by the separate signals corresponding to the free r.c.amorphous phase that appeared in the high-frequency region (Fig 3.11) The recorded spectra clearly identified the disordered α2 polymorphic form of isotactic polypropylene However, the corresponding 13C MAS NMR spectra measured with a short repetition delay (1-2 s) reflected a preference for the highly mobile fractions Consequently, the signals of the CH and CH2 groups were suppressed, and at high temperatures, the signals for the polymer segments in the amorphous r.c conformation were relatively enhanced (Figure 3.12) Unfortunately, although the prepared PP/CaCO3 systems considerably differed in their mechanical properties, a visual inspection of the recorded 13C CP/MAS NMR and 13C MAS NMR spectra did not reveal any systematic spectral changes or features that reflected the plastic deformation In a subsequent step, we determined the amount of the highly mobile r.c amorphous fraction in the prepared composite materials using the 13C MAS NMR spectra measured at 355 K As shown in Fig 3.13, the amount of the highly mobile amorphous r.c fraction systematically decreased as the critical value of the J-integral increased, which represents a measure of the composite The neat, unfilled PP surprisingly had a dependence in the middle of the other dependences, and regardless of the amount of filler particles the composite systems that were modified by larger particles (12 mm) nearly exclusively exhibited a lower J-integral critical value in comparison with the systems that were modified by smaller particles (1.7 mm) 14 : Jid [N/m] is calibrated to [%] : Highly-mobile fraction of CH % Figure 3.13 Graph of the toughness expressed as the J-integral (JId) critical value and the contents of the highly mobile amorphous fractions in the PP systems calculated from the integral intensities of the CH signal in the 13C MAS NMR spectra The maximum integral intensity value was calibrated to the maximum content (100%) of the highly mobile fraction The maximum J-integral value was normalized to 100% To find other consistent trends and characteristic spectral features related to the changes in the mechanical properties of the samples, we used FA to extract the key information from the relatively large experimental data sets that were obtained The recorded 13C CP/MAS NMR and/or 13C MAS NMR spectra were separately analyzed in sets representing each temperature Subsequently, the FA generated subspectra, Sj, and the corresponding singular values, wj, for each set of NMR spectra Because only the singular values w1 - w4 were significantly high (Fig 3.14, left panel), the spectral variation in the analyzed dataset was completely described by the corresponding subspectra, S1eS4 Sau đó, FA tạo phổ thế, Sj giá trị bất thường tương ứng, wj cho phổ NMR Do giá trị đơn w1 – w4 mức cao đáng kể (hình 3.26), biến thể phổ tập liệu phân tích mơ tả hồn tồn phổ tương ứng, S1 – S4 Fig 3.14 Singular value calculated from the set of 13C MAS NMR spectra at 355 K (on the left) and the relevant subspectra S1, S2 and S4 used for the FA (on the right) The subspectra reflecting the changes in the amorphous (am.) phase and crystalline (cryst.) phase in the CH3 region The first-rank subspectrum, S1, corresponds to the average 13C MAS NMR spectrum for the superposition of the experimental data recorded for all the prepared samples at a given temperature, and the second-order subspectrum, S2, shows the most significant spectral differences found in the analyzed 15 data set In the subspectrum S2, all the components are equally highlighted, including the highly mobile amorphous and crystalline fractions Specifically, for the CH3 signal, the amorphous phase was characterized by a positive signal at approximately 22 ppm, and the crystalline phasewas characterized by a negative signal at approximately 21 ppm In addition, we determined from the analysis of the calculated subspectra that the most significant differences between the samples were in the CH3 regions of the subspectra S1, S2, and S4 (Fig 3.26) The observed differences were subsequently quantified using the corresponding normalized coefficients, Vi1, Vi2 and Vi4 These parameters and their correlation plots were used to find the relationship between the spectroscopically specific features and the changes in the physicochemical and mechanical properties of the analyzed composites Consequently, by applying this strategy, especially for the 13C MAS NMR spectra obtained at 355 K with increased segmental motion, we saw clear clustering of the Vij parameters into two groups that were separated by a vertical line, which is visualized in the 3D correlation plot of the relevant parameters, Vi1, Vi2 and Vi4 (Fig 15 and Fig 3.16) These groups correspond to composite systems that differ in their: (i) highly mobile amorphous fraction content; (ii) filler particle size; (iii) toughening effects; and (iv) PP/filler aspect ratio The correlation plot in Fig shows the two groups of prepared microcomposites that differ in the J-integral critical value The group on the left represents systems with an average JId value of 3.5 N mm-1 (3.2-3.8 N mm-1), and the cluster on the right represents systems with an average JId value of 4.8 N mm-1 The correlation plots for the other characteristics are shown in Fig 3.17 Fig 3.15 3D correlation plots for the Vi1, Vi2 Fig 3.16 3D correlation plots for the Vi1, Vi2 and Vi4 coefficients evaluated from the 13C and Vi4 coefficients evaluated from the 13C MAS NMR data using FA for the full spectra MAS NMR data using FA for the single CH3 signals at 355 K 16 Fig 3.17 3D correlation plots of the Vi1, Vi2 and Vi4 coefficients evaluated from the 13C MAS NMR data at 355 K using FA The FA results also give information on the addition of fatty acids into the PP/CaCO3 microcomposites In this case, at high temperatures (330-355 K), clustering of the systems based on the surface treatment of the CaCO3 particles was not observed However, at lower temperatures (325 K), clustering based on the surface treatment, i.e., with OA or SA and without an acid treatment, was observed (Fig 3.18) This clustering was likely revealed by the lower temperatures because the amorphous phase segmental motion in the systems is not completely free, and the full differences in the chain mobility and the trans-crystalline layer are not yet well resolved Therefore, the samples are clustered based on the subtle differences in the system homogeneity, which is influenced by the nontreated or treated regimes of the two fatty acids 17 Fig 3.18 3D correlation plot of the Vi1, Vi2 and Vi4 coefficients evaluated from the 13C MAS NMR data at 325 K using FA The plot shows the PP samples based on the fatty acid treatment and the corresponding 13C MAS NMR spectra of the grouped systems and the pure PP sample When searching for the molecular origin of the toughness differences in the prepared PP/CaCO3 microcomposites, we determined that the systems with a higher toughness (higher JId) mostly contained filler particles with a smaller diameter (1.7 mm), smaller amounts of these particles (80/20), and smaller amounts of the highly mobile r.c amorphous fraction based on the 13C MAS NMR spectra at 355 K The key role of the amorphous phase in understanding the toughness of the PP/CaCO3 composites was further evidenced by the FA, which highlighted the prominent spectral differences between the prepared composite systems In particular, the subspectrum S4 unambiguously identified the signal at 22 ppm as corresponding to the methyl groups of the amorphous, free polymer chains in the r.c conformation The crystallinity of the prepared systems was determined by wide angle X-ray scattering experiments to be approximately 50%, and the crystallinity did not show a systematic trend with respect to the observed changes in the composite toughness Therefore, the observed decrease in the free r.c amorphous fraction amount must be compensated by an increase in the amount of amorphous PP chains with a helical conformation in the confined domains The PP chains that adopt a helical conformation can be attributed to the transcrystalline phase described in the literature In general, the formation of this trans-crystalline phase is induced: i) by the adsorption of polymer chains onto the active sites of the filler particles; ii) by a suitable orientation of the backbone bonds in the polymer toward the solid surface; and iii) by the hindered chain mobility, which affects the crystallization kinetics and induces the formation of imperfect crystallites These imperfect crystallites are thought to undergo a larger plastic deformation in the system than the perfect crystallites, and this deformation increases the composite toughness Our experimental findings indicate that the key mechanism that is responsible for the enhanced toughness in the PP/CaCO3 composites is related to the PP chain mobility The mobility is induced by the presence of filler particles, and these particles not allow perfect crystallites to form and promote the formation of partially ordered amorphous and trans-crystalline domains near the filler surfaces to dissipate the deformation energy Smaller filler particles with larger specific surface areas offer more active sites for polymer adhesion onto the solid surface, which consequently results in a larger decrease in the polymer chain motion, the creation of imperfect crystallites and increased toughness However, systematic trends in the 13C NMR parameters were observed only at high temperatures Although we measured the spectra for the whole temperature range from 295 to 355 K at K increments, the trends in the signal intensities and the sample clustering in the principle components plots first appeared at 325 K At this temperature, the thermal energy introduced into the systemswas sufficient to overcome the energy barriers and free the highamplitude segmental motions of the polymer chains in the amorphous domains with an r.c conformation As the temperature increased, the higher energy barriers were overcome, and the highamplitude cooperative motions of the PP chains occurred above the critical temperature (approximately 350 K) as expected Near and above the critical fusion temperature, the differences among the prepared composites were observable using ss-NMR spectroscopy Below this temperature, these differences were hidden by the overlapping and unresolved signals 3.3 Composite based on polypropylene and talc 3.3.1 Morphology observation 18 Fracture surface morphology of polypropylene composites containing 40% talc mineral powder non-modified surface is shown in Figure 3.19 Fig 3.19 SEM images of morphology of PP filled with 40% untreated talc SEM images of the fracture surface of the material samples show that talc minerals are not denatured, the surface is unevenly dispersed in the polypropylene substrate with the appearance of agglomerated particles in the substrate In addition, the interaction between the phases is poor when gaps appear between the filler particles and the polymer substrate Fig 3.20 SEM images of morphology of PP filled with 40% silane treated talc In the case of modified talc mineral powders (Figure 3.20), the dispersion and phase interoperability were improved Thus, it is clear that the surface modification process has been shown to be effective when increasing the adhesion between the surface of the talc and the polypropylene substrate 3.3.2 Tensile properties a Young’s modulus Effects of talc content and surface modification on mechanical behaviour of polypropylene based composites were investigated Figure 3.21 showed Young’s modulus of composites The results showed that Young’s modulus values of composites increased as a function of filler content Generally, the addition of rigid particulate fillers increases stiffness, which is measured through Young modulus This is due to the fact that fillers often exhibit higher stiffness compared matrix polymer On the other hand, Young’s modulus is measured at the very beginning of a tensile test, where deformation is insufficient to cause particle-matrix debonding 19 Fig 3.21 The effects of content and filler surface on the Young’s modulus of PP based composites Surprisingly, there was a difference in Young modulus at high filler content (40 wt%) in comparing between treated and untreated filler This can be explained that the better dispersion of filler particles in the case of PP/talc/T2Mt leads to the increased stress concentration b Yield stress As well known that only when filler particles become very small does the yield stress value increase as the concentration increases However, yield stress behavior not only depends on particle size but also on the interaction with the matrix, yield stress gives additional information on filler-matrix interactions and consequently it is one of the preferred methods of composite testing It can be seen that yield stress values of composites strongly increased with the incorporation of talc filler into polypropylene matrix at small concentration (Figure 3.22) At higher concentration, the increasing is not strongly This occurred for both cases treated and untreated talc Fig 3.22 Effects of talc content and filler surface on the yield stress values of PP based composites The result also indicated that a stronger interaction between the filler and the matrix in case of PP/talc/T2Mt has a higher yield stress value compared with PP/talc at the corresponding concentration c Strain at break The strain at break is usually inversely proportional to tensile strength which means that increasing the tensile strength usually contributes to a decrease in the strain at break It can be seen that the addition of talc filler leaded to a marked decrease in the value of strain at break (Fig 3.23) And this trend continued at higher concentration for both PP/talc and PP/talc/T2Mt composites 20 Fig 3.23 Effects of talc content and filler surface on the strain at break values of PP based composites 3.3.3 Fracture behaviour Introduction of fillers into a polypropylene matrix results in a heterogeneous system Under the effect of an external load these heterogeneities induce stress concentrations, the magnitude of which depends on the geometry of the particles (mean diameter and average size distribution), on the relative properties of the components and on interfacial adhesion Heterogeneous stress distribution and local stress maximums developing in the composite influence its deformation and fracture behaviour as well as its overall performance Also, any influence on the crystalline structure produced by the filler addition will have an influence on the fracture behaviour and deformation mechanisms of the composite Some authors reported a maximum of the notched impact strength at a talc content in range of 10 – 20 % Results in figure 3.24 had a similar trend Maximum of the notched Charpy impact strength at talc content of 10% After this concentration, notched impact toughness decreased with increasing talc content On the other hand, the adsorption of polymer molecules on the filler surface through stronger bonds leading to the rigidity in structure of polymer chains This leads to earlier crack initiation and propagation with decreasing of impact strength values in case of PP/talc/T2Mt composites compared with PP/talc composites at corresponding concentration (figure 4) Plastic deformation of the polymer matrix is the main energy absorbing process in impact and this increases when the interaction between particles and polymer is lowered in case of PP/talc composites Fig 3.24 Effects of talc content and filler surface on the values of notched Charpy impact strength of PP based composites 21 Chapter 4: CONCLUSIONS AND RECOMMENDATIONS A Conclusion The thesis investigated the effect of phase interaction, molecular mobility on the mechanical properties of polypropylene basedcomposite materials reinforcing with three typical fillers such as glass beads, calcium carbonate and talc mineral powder Glass beads are surface treated with silicone oil and vinyl silane, calcium carbonate are surface treated withstearic acid and oleic acid and talc are surface treated withmetacryloxypropyltrimetoxy silane Strong phase interaction increases the modulus of elasticity and tensile strengbut reduces the elongation at break , the value of impact energy absorptionis higher with weak phase interaction Of Among of fillers, talc is the best reinforced filler for polypropylene, the tensile and impact strength composite increase with loadingof 10% talc By using the solid-state magnetic resonance spectroscopy for PP / glass beads composite, the least flexible polymer segments with strong phase interactionare identified Meanwhile, if glass beads surface is modified/unmodified by silicon oil,the more flexible segments are found The raw PP molecule has the highest flexibility segment Application of factor analysis (FA) fromss-NMR spectroscopy, PP / CaCO3 composites system has been able to distinguish the difference in: (i) content of highly flexible amorphous segments; (ii) size of particles fillers; (iii) influence of chemical sustainability; and (iv) the ratioof PP and CaCO3 in composite material These spectral differences explain a systematic changeof the impact strength of material samples Thus, the changes of the molecular mobilityin different phases interaction is determinedby solid state magnetic resonance spectroscopyin both PP / glass beads and PP / CaCO3 materials They cause the change in mechanical properties, especially the destructive mechanical properties of the material B Recommendations The thesis pays attention on analyzing the solid-state magnetic resonance spectrum of composite material samples, so loading of glass beads and CaCO3 are up to 20 % and 40 % respectively to fabricate material In future, the others content of filler will carry on In the case of PP / talc materials, talc minerals play more complex role, PhD student will keep studying on applying solid-state magnetic resonance spectroscopy on this material system NEW CONTRIBUTIONS OF THE THESIS - By the method of solid-state resonance spectroscopy, molecular mobility has been determined in PP/glass beads and PP/CaCO3 composite materials The molecular mobility in different phase interaction changes systematically with the change in mechanical properties of the material These information contribute significantly for building up microstructure polypropylene materials New materials posses designed properties and they will be applied in polymer materials and chemical engineering - Study on the effects of talc mineral, is the separated products of the Institute of Materials Science, Vietnam Academy of Science and Technology, on the mechanical properties of polypropylene composite materials The research results show that polypropylene materials was reinforced with 10% of talc mineral powder achieves the highest tensile strength and impact Talc, is considered as mineral good quality, can be used as reinforcing fillers for composite polymer materials 22 LIST OF PAPERS PUBLISHED A List of papers Olivia Kukackova, Nguyen Viet Dung, Sabina Abbrent, Martina Urbanova, Jiri Kotek, Jiri Brus “A novel insight into the origin of toughness in polypropyleneecalcium carbonate microcomposites: Multivariate analysis of ss-NMR spectra” Polymer 132 (IF = 3,7), 106-113, 2017 Nguyen Viet Dung, Ngo Ke The and Jiri Kotek “Effect of particle size and fatty surface treatment of calcium carbonate on the deformation and fracture behaviour of polypropylene-based composites”, Vietnam Journal of Chemistry, Vol 53 (2e1), 26-30, 2015 Nguyen Viet Dung and Ngo Ke The “Effects of talc content and interfacial adhesion on mechanical behaviour of polypropylene-based composites”, Vietnam Journal of Chemistry, Vol 53 (4A), 2015 Nguyen Viet Dung, Ngo Ke The and Jiri Kotek “A solid-state NMR study of molecular mobility and resulting deformation and fracture behaviour of glass beads filled polypropylene composites”, Vietnam Journal of Chemistry, Vol 53(6e4), 240-244, 12/2015 Nguyen Viet Dung, Ngo Ke The and Jiri Kotek “Effect of interfacial adhesion on deformation and fracture behaviour of composites based on polypropylene and galss beads”, Journal of Science and Technology, Vol 54(1A), 300-307, 2016 B List of papers in Conference Nguyen Viet Dung, Libor Kobera and Jiri Kotek “Effects of filler surface on molecular mobility and resulting deformation and fracture behaviour of thermoplastic polymer composites” Carreer in Polymer VI, Prague, Czech Republic, ISBN 978-80-85009-79-8, 18-19 July 2014 Nguyen Viet Dung, Ngo Ke The and Jiri Kotek "Effects of filler surface on crack initiation and propagation of particulate filled polymer composites" 7th International Workshop on Advanced Materials Science and Nanotechnology, Ha Long city, Vietnam, 2-6 November 2014 Nguyen Viet Dung, Ngo Ke The and Jiri Kotek "Effect of particle size and fatty acid coatings of calcium carbonate on the deformation and fracture behaviour of polypropylene-based composites" Vietnam Malaysia International Congress 2014, Ha Noi, Viet Nam, 7-9 November 2014 Nguyen Viet Dung, Ngo Ke The “Deformation and fracture behaviour of isotactic polypropylene reinforced particle fillers”, The 5th Asian Materials Data Symposium, Hanoi, Vietnam, Oct 30th – Nov 02nd 2016 Nguyen Viet Dung, Ngo Ke The “A solid-state NMR Study of molecular Mobility and Resulting Deformation and Fracture Behaviour of Polypropylene Filled Glass Beads Composites” The 8th Regional Conference on Chemical Engineering, 29 November – 01 December 2015  ... phổ thế, Sj giá trị bất thường tương ứng, wj cho phổ NMR Do giá trị đơn w1 – w4 mức cao đáng kể (hình 3.26), biến thể phổ tập liệu phân tích mơ tả hồn tồn phổ tương ứng, S1 – S4 Fig 3.14 Singular... polypropylene They was considered that the adhesion between the plastic substrate and polar organic fiber affects incredibly the properties of the composite Thus, maleic anhydride– grafted polypropylene... and in extreme cases of perfectly evolved crystal phases very narrow signals are expected In polypropylene systems presence of polymorphic form alpha is reflected by the doublet of CH signal at