ĐỀ TÀI NGHIÊN CỨU KHOA HỌC VÀ PHÁT TRIỂN CÔNG NGHỆ CẤP VIỆN KỸ THUẬT NHIỆT ĐỚI

KHẢO SÁT HÀM LƯỢNG HẠT NANO Al2O3 TRONG DUNG DỊCH XỬ LÝ LỚP PHỦ COMPOSITE Al2O340%TiO2 I. Thông tin chung về đề tài 1. Tên đề tài Tên Tiếng Việt: “Khảo sát hàm lượng hạt nano Al2O3 trong dung dịch xử lý lớp phủ composite Al2O340%TiO2”. Tên Tiếng Anh: “The study of Al2O3 nanoparticles content in solutiontreated Al2O340%TiO2 composite coating”. Keywords: plasma spraying, aluminum phosphate, Al2O3TiO2, Al2O3 nanoparticles

VIỆN HÀN LÂM KHOA HỌC VÀ CÔNG NGHỆ VIỆT NAM VIỆN KỸ THUẬT NHIỆT ĐỚI THUYẾT MINH ĐỀ TÀI NGHIÊN CỨU KHOA HỌC VÀ PHÁT TRIỂN CÔNG NGHỆ CẤP VIỆN KỸ THUẬT NHIỆT ĐỚI (DÀNH CHO CÁN BỘ KHOA HỌC TRẺ) TÊN ĐỀ TÀI: KHẢO SÁT HÀM LƯỢNG HẠT NANO Al2O3 TRONG DUNG DỊCH XỬ LÝ LỚP PHỦ COMPOSITE Al2O3-40%TiO2 Chủ nhiệm đề tài: Các cán tham gia: ThS Phạm Thị Hà ThS Phạm Thị Lý KS Nguyễn Văn Tuấn Hà Nội, 02/2017 THUYẾT MINH ĐỀ TÀI NGHIÊN CỨU KHOA HỌC VÀ PHÁT TRIỂN CÔNG NGHỆ CẤP VIỆN KỸ THUẬT NHIỆT ĐỚI (DÀNH CHO CÁN BỘ KHOA HỌC TRẺ) I Thông tin chung đề tài Tên đề tài Tên Tiếng Việt: “Khảo sát hàm lượng hạt nano Al2O3 dung dịch xử lý lớp phủ composite Al2O3-40%TiO2” Tên Tiếng Anh: “The study of Al2O3 nanoparticles content in solution-treated Al2O340%TiO2 composite coating” Keywords: plasma spraying, aluminum phosphate, Al2O3-TiO2, Al2O3 nanoparticles Thời gian thực hiện: 02/2017- 12/2017 Kinh phí: 40.000.000 đồng Chủ nhiệm đề tài: Ths Phạm Thị Hà Chuyên ngành đào tạo: Hóa lý thuyết hóa lý Chuyên ngành làm việc: Hóa lý thuyết hóa lý II Nội dung KHCN đề tài Mục tiêu đề tài: Lựa chọn hàm lượng hạt nano Al2O3 thêm vào dung dịch phốt phát nhôm nhằm tạo hệ lớp phủ composite Al2O3-40%TiO2 có độ bền mài mòn khơ độ bền ăn mòn mơi trường NaCl 3,5% cao sở mẫu lựa chọn để khảo sát Tình hình nghiên cứu nước: Thép cacbon loại vật liệu sử dụng nhiều công nghiệp Tuy nhiên, thép cacbon dễ bị ăn mòn mài mòn làm việc môi trường khắc nghiệt [1] Một phương pháp ứng dụng rộng rãi để bảo vệ thép khỏi tác nhân gây ăn mòn mài mòn sử dụng lớp phun phủ nhiệt Loại lớp phủ sử dụng thường xuyên môi trường làm việc khắc nghiệt lớp phủ gốm oxit [2] Trong tất vật liệu gốm, nhôm oxit (Al 2O3) ứng dụng nhiều chế tạo lớp phủ chúng có độ cứng cao, tính bền hóa học, chống ăn mòn mài mòn tốt [1] Các lớp phủ Al2O3 chế tạo công nghệ phun phủ plasma có khả hoạt động điều kiện khắc nghiệt tải trọng cao, tốc độ cao, nhiệt độ cao, mơi trường mài mòn mơi trường biển Đặc tính lớp phủ Al2O3 nâng cao gia cường thêm TiO2 vào lớp phủ [3-4] Những năm gần đây, khả bảo vệ chống ăn mòn mài mòn lớp phủ Al2O3-TiO2 nhiều nhà khoa học giới quan tâm nghiên cứu Celik cộng [5] kết luận khả bảo vệ chống ăn mòn lớp phủ Al 2O3 Al2O3-TiO2 cao so với lớp phủ Cr 3C2-NiCr, NiAl NiCrAl Kết nghiên cứu [6-9] cho thấy có mặt TiO lớp phủ plasma Al 2O3 nâng cao khả chống ăn mòn cho lớp phủ Trong nghiên cứu [10], lớp phủ plasma Al2O3-TiO2 chế tạo hợp kim Al 6061 với lớp phủ lót Ni(Al) hàm lượng TiO2 thay đổi 0; 13% Kết nghiên cứu với tăng hàm lượng TiO2 bột nguyên liệu, khả chống ăn mòn lớp phủ dung dịch NaCl 3,5% nâng cao Điều giải thích điểm nóng chảy TiO2 thấp so với Al2O3, trình phun, TiO2 dễ dàng phân tán vào Al 2O3 giúp làm kín lỗ xốp, giảm ứng suất vết nứt Các tác giả nghiên cứu [11] nghiên cứu ảnh hưởng tốc độ cấp bột tốc độ dòng khí H2 đến khả chống xâm thực lớp phủ Al 2O3–TiO2 Thử nghiệm xâm thực tiến hành theo tiêu chuẩn ASTM G32 Bề mặt cấu trúc mặt cắt ngang lớp phủ trước sau thử nghiệm xâm thực quan sát phương pháp kính hiển vi điện tử quét Kết cho thấy khả chống xâm thực phụ thuộc vào cấu trúc tế vi lớp phủ Lớp phủ chế tạo điều kiện tốc độ khí H 16 lít/phút tốc độ cấp bột 20 g/phút có khả chống xâm thực cao Tác giả F Vargas cộng tiến hành nghiên cứu trình thẩm thấu dung dịch muối NaCl 3,5% vào lớp phun phủ plasma Al2O3-TiO2 phương pháp phổ tổng trở điện hóa (EIS) [12] Hai loại bột Al2O3-13%TiO2 với kích thước hạt 5-25 µm 15-40 µm sử dụng phun Al 2000 Các tác giả rằng, đầu ngâm mẫu, dung dịch muối ngấm vào lớp phủ Tuy nhiên, sau 340 ngâm, trình thẩm thấu dung dịch muối dừng lại Điện trở phân cực (Rp) mẫu lớp phủ cao với điện trở phân cực mẫu nền, điều cho thấy, lớp phủ có khả sử dụng để phục hồi bảo vệ bề mặt nhôm tiếp xúc với môi trường biển dung dịch nước muối khác Khả bảo vệ lớp phủ chế tạo từ bột Al2O3-13%TiO2 với kích thước hạt 5-25 µm cao so với lớp phủ chế tạo từ bột có kích thước hạt 15-40 µm, độ xốp tỷ lệ vết nứt thấp Nhóm tác giả N.H.N Yusoff [13] nghiên cứu ảnh hưởng kích thước bột nguyên liệu phun lớp phủ lót đến hành vi ăn mòn lớp phủ plasma Al 2O3-13%TiO2 nước biển Kết nghiên cứu cho thấy lớp phủ chế tạo từ bột có kích thước nano có độ xốp nhỏ khả chống ăn mòn tốt so với lớp phủ chế tạo từ bột kích thước micromet Lớp lót kim loại Ni-Al góp phần làm giảm độ xốp vết nứt lớp phủ Kỹ thuật phun phủ plasma sử dụng rộng rãi có nhiều ưu điểm, nhiên lớp phun phủ plasma tồn lỗ xốp làm cho bề mặt dễ bị cơng tác nhân gây ăn mòn Do vậy, để nâng cao khả chống ăn mòn, lớp phủ sau chế tạo cần xử lý để làm giảm độ xốp Xử lý lớp phun phủ nhiệt thực nhiều phương pháp ép nóng đẳng nhiệt lớp phủ, phương pháp bốc hóa học nhiệt độ cao (CVD), thấm hóa học (CVI), phương pháp khác có khả điền đầy lỗ xốp Trong số đó, cách xử lý đơn giản hiệu sử dụng phương pháp thẩm thấu với chất vô hữu Sử dụng chất thẩm thấu hữu điền đầy gần hoàn toàn lỗ xốp, cải thiện khả chống ăn mòn lớp phun phủ nhiệt Tuy nhiên, kim loại làm việc mơi trường vừa chịu ăn mòn mài mòn chất thẩm thấu vơ lựa chọn hàng đầu Một số chất thẩm thấu vô sử dụng natri orthosilicat, natri molipdat, phốt phát nhôm Phốt phát nhôm thường ứng dụng phổ biến làm chất kết dính lĩnh vực chất chịu nhiệt thơng qua việc tạo hợp chất dạng tinh thể hay vơ định hình phụ thuộc vào thành phần dung dịch, thời gian phản ứng chế độ xử lý nhiệt Đối với lớp phủ phốt phát nhơm liên kết phản ứng hóa học với lớp phủ thẩm thấu hấp phụ lỗ xốp, mao quản lớp phủ Trên giới, phốt phát nhôm ứng dụng nhiều cho lớp phủ gốm chịu nhiệt, lớp phủ HVOF lớp phủ plasma từ oxit Al 2O3, Cr2O3 [14-16] Các kết cho thấy phốt phát nhơm có khả làm giảm độ xốp nâng cao khả bảo vệ chống ăn mòn, mài mòn cho lớp phủ nhiệt Theo nghiên cứu [16], ảnh hưởng chất thẩm thấu (phốt phát nhôm, methacrylat, phenol, epoxy, furan, vinyl este…) lớp phủ Al 2O3 chế tạo công nghệ phun phủ plasma nghiên cứu Các kết cho thấy, điện ăn mòn lớp phủ Al2O3 thẩm thấu với phốt phát nhôm so với lớp phủ Al2O3 không không thẩm thấu với phốt phát nhôm thay đổi đáng kể (từ -500 mV tăng lên -200 mV) Ngoài ra, khả chịu mài mòn lớp phủ có thẩm thấu với phốt phát nhôm cao nhiều so với lớp phủ có thẩm thấu chất khác Cụ thể, khả chịu mài mòn lớp phủ Al2O3 thẩm thấu với phốt phát nhôm cao lần so với lớp phủ Al2O3 thẩm thấu với epoxy cao gần 10 lần so với lớp phủ Al 2O3 thẩm thấu với methacrylat Nhằm nâng cao đặc tính chống ăn mòn, mẫu lớp phủ plasma Cr2O3-Al2O3 thẩm thấu với phốt phát nhôm với lượng nhỏ hạt Al 2O3 kích thước nano, sau mẫu xử lý nhiệt độ cao [17] Việc thêm hạt nano Al2O3 vào dung dịch phốt phát nhơm góp phần làm giảm độ xốp lớp phủ đến gần 90% Các phương pháp đo đường cong phân cực, đo tổng trở điện hóa thử nghiệm phun mù muối sử dụng để đánh giá đặc tính chống ăn mòn lớp phủ Các kết nghiên cứu cho thấy, phốt phát nhôm cải thiện đặc tính chống ăn mòn lớp phủ trước sau xử lý nhiệt Lớp phủ composite Cr2O3-Al2O3 sau thẩm thấu với phốt phát nhôm có chứa hạt Al2O3 kích thước nano có khả sử dụng mơi trường ăn mòn khắc nghiệt Tại Việt Nam, tác giả Nguyễn Văn Tuấn cộng có nhiều nghiên cứu hệ lớp phun phủ nhiệt NiCr20 thẩm thấu với phốt phát nhôm [18-24] Các kết nghiên cứu rằng, phốt phát nhơm góp phần làm giảm độ xốp nâng cao khả bảo vệ chống ăn mòn mài mòn lớp phủ Kết nghiên cứu đề tài sở cấp Viện Kỹ thuật nhiệt đới dành cho cán khoa học trẻ năm 2016 nhóm nghiên cứu chúng tơi cho thấy lớp phủ plasma Al2O340%TiO2 thẩm thấu với phốt phát nhơm chứa 5% hạt nano Al2O3 có độ bền mài mòn cao tỷ lệ lỗ xốp thấp so với lớp phủ thẩm thấu phốt phát nhôm khơng chứa hạt nano Al2O3 Sự có mặt hạt nano Al2O3 nâng cao khả thẩm thấu dung dịch phốt phát nhôm vào bên lớp phủ Với mong muốn tiếp tục hoàn thiện hướng nghiên cứu hệ lớp phủ Al2O3-40%TiO2, nghiên cứu này, nghiên cứu ảnh hưởng hàm lượng hạt nano Al2O3 đến khả bảo vệ chống ăn mòn dung dịch NaCl 3,5% chống mài mòn hệ lớp phủ Al2O3-40%TiO2 thẩm thấu với phốt phát nhôm có chứa hạt nano Al2O3 Tài liệu tham khảo: S Sathish, M Geetha, Comparative study on corrosion behavior of plasma sprayed Al2O3, ZrO2, Al2O3/ZrO2 and ZrO2/Al2O3 coatings, Trans Nonferrous Met Soc China, Vol 26, pp 1336−1344 (2016) N Hegazy, M Shoeib, Sh Abdel-Samea, H.Abdel-Kader, Effect of Plasma Sprayed Alumina Coating on Corrosion Resistance, 13th International Conference on AEROSPACE SCIENCES & AVIATION TECHNOLOGY (2009) S Islak, S Buytoz, E Ersoz, N Orhan, J Stokes, M Saleem Hashmi, I Somunkiran, N Tosun, Effect on microstructure of TiO rate in Al2O3-TiO2 composite coating produced using plasma spray method, Optoelectronics and Advanced Materials – Rapid communications, Vol 6, pp 844 – 849 (2012) M.J Ghazali, S.M Forghani, N Hassanuddin, A Muchtar, A.R Daud, Comparative wear study of plasma sprayed TiO2 and Al2O3–TiO2 on mild steels, Tribology International 93, 681–686 (2016) Titan W, Wang Y, Zhang T, Yang Y, Sliding wear and electrochemical corrosion behavior of plasma sprayed nanocomposite Al2O3-13%TiO2 coatings, Materials Chemistry and Physics, Vol 118(1), pp 37−45 (2009) Toma F L, Stahr C C, Berger L M, Saaro S, Herrmann M, Deska D, Michael G, Corrosion resistance of APS- and HVOF-sprayed coatings in the Al 2O3-TiO2 system, Journal of Thermal Spray Technology, Vol 19(1−2), pp 137−147 (2010) J Zhang, J He, Y Dong, X Li, D Yan, Microstructure and properties of Al2O3-13% TiO2 coatings sprayed using nanostructured powders, Rare Metals, Vol 26, pp 391– 397 (2007) R Yilmaz, A.O Kurt, A Demir, Z Tatll, Effects of TiO2 on the mechanical properties of the Al2O3-TiO2 plasma sprayed coating, Journal of the European Ceramic Society Vol 27, pp 1319–1323 (2007) M Wang, L.S Leon, Effects of the powder manufacturing method on microstructure and wear performance of plasma sprayed alumina-titania coatings, Surface and Coatings Technology, Vol 202, pp 34–44 (2007) 10 S JIA, Y.Zou, J Xu, J Wang, L Yu, Effect of TiO2 content on properties of Al2O3 thermal barrier coatings by plasma spraying, Transactions of Nonferrous Metals Society of China, Vol 25, pp 175–183 (2015) 11 K Jafarzadeh, Z Valefi, B Ghavidel, The effect of plasma spray parameters on the cavitation erosion of Al2O3 –TiO2 coatings, Surface and Coatings Technology, Vol 205, pp 1850–1855 (2010) 12 F Vargas, H Ageorges, P Fauchais, M.E López, J.A Calderon, Permeation of saline solution in Al2O3-13wt.% TiO2 coatings elaborated by atmospheric plasma spraying, Surface and Coatings Technology, Vol 220, pp 85–89 (2013) 13 N.H.N Yusoff, M.J Ghazali, M.C Isa, A.R Daud, A Muchtar, Effects of powder size and metallic bonding layer on corrosion behaviour of plasma-sprayed Al 2O3-13% TiO2 coated mild steel in fresh tropical seawater, Ceramics International, Vol 39, pp 2527– 2533 (2013) 14 Y Wang, S.L Jiang, Y.G Zheng, W Ke W.H Sun, J.Q Wang, Effect of porosity sealing treatments on the corrosion resistance of high-velocity oxy-fuel (HVOF)sprayed Fe-based amorphous metallic coatings, Surf Coat Technol, Vol 206, pp 1307-1318 (2011) 15 E.M Leivo, M.S Vippola, P.P.A Sorsa, P.M Vuoristo and T.A Mantyla, Wear andcorrosion properties of plasma sprayed Al2O3 and Cr2O3 coatings sealed by aluminum phosphates, Journal of Thermal Spray Technology, Vol 6(2), pp 205-210 (1997) 16 J Knuuttila, P Sorsa and T Mäntylä, Sealing of thermal spray coatings by impregnation, ASM International - JTTEE5 8, pp 249-257 (1999) 17 Fang Shao, Kai Yang, Huayu Zhao, Chenguang Liu, Liang Wang, Shunyan Tao, Effects of inorganic sealant and brief heat treatments on corrosion behavior of plasma sprayed Cr2O3 –Al2O3 composite ceramic coatings, Surface and Coatings Technology, Vol 276, pp 8–15 (2015) 18 Nguyễn Văn Tuấn, Lê Thu Quý, Nguyễn Thu Hoài, Nghiên cứu chế tạo chất bịt phốt phát nhơm, Tạp chí hóa học, T49 (2ABC), tr 796-800 (2011) 19 Nguyen Van Tuan, Le Thu Quy, Study on the application of aluminum phosphate sealantfor thermal spray nickel chromium coating, Proceedings of the 5th Asian thermal spray conference ATSC2012, Ibaraki, Japan (2012) 20 Nguyen Van Tuan, Le Thu Quy, Influence of molar ratio of P/Al to the application of aluminium phosphate sealant for NiCr20 alloy coating, Vietnam journal of chemistry, Vol 50 (6B), pp 204-209 (2012) 21 Nguyễn Văn Tuấn, Lê Thu Quý, Đỗ Thị Thục, Đào Bích Thủy, Lý Quốc Cường, Phạm Thị Lý, Nghiên cứu khả bảo vệ chống ăn mòn lớp phủ hợp kim NiCr kết hợp với chất bịt phốt phát nhơm mơi trường axit, Tạp chí Hóa học, T 51( 2AB), tr 265-270 (2013) 22 Nguyễn Văn Tuấn, Lê Thu Quý, Nghiên cứu đặc trưng cấu trúc, thành phần pha khả bảo vệ chống ăn mòn hệ lớp phủ hợp kim NiCr20 kết hợp với phốt phát nhơm, Tạp chí Hóa học, T 51, 3AB, tr 383-387 (2013) 23 Nguyễn Văn Tuấn, Lê Thu Quý, Phạm Thị Hà, Phạm Thị Lý, Đỗ Thị Thục, Đào Bích Thủy, Lý Quốc Cường, Ảnh hưởng chất bịt phốt phát nhôm đến khả bảo vệ chống ăn mòn lớp phun phủ hợp kim NiCr20 mơi trường axit sulfuric, Tạp chí Hóa học, T.52 (6B), tr 132-135 (2014) 24 Nguyễn Văn Tuấn, Lê Thu Quý, Phạm Thị Hà, Phạm Thị Lý, Đinh Thị Mai Thanh, Ảnh hưởng nhiệt độ ủ sau xử lí bịt phốt phát nhôm tới khả bảo vệ chống ăn mòn mơi trường axit sulfuric lớp phun phủ hợp kim NiCr20, Tạp chí Khoa học Công nghệ, T.53 (1A), tr 36-43 (2015) Cách tiếp cận (nêu rõ xuất xứ đề tài): - Từ tài liệu công bố - Từ mục tiêu chế tạo lớp phủ có khả làm việc điều kiện khắc nghiệt - Từ nhu cầu thực tế phòng Dữ liệu, thử nghiệm nhiệt đới môi trường muốn mở rộng nghiên cứu ứng dụng lớp phủ nhiệt Việt Nam đặc biệt ngành cơng nghiệp hóa chất, khai khống, nhiệt điện điện hạt nhân - Từ kết nghiên cứu đề tài sở cấp Viện Kỹ thuật nhiệt đới dành cho cán khoa học trẻ năm 2016: lớp phủ plasma Al2O3-40%TiO2 thẩm thấu dung dịch phốt phát nhôm chứa 5% hạt nano Al2O3 có độ bền mài mòn cao tỷ lệ lỗ xốp thấp so với lớp phủ thẩm thấu phốt phát nhôm không chứa hạt nano Al2O3 Tuy nhiên, ảnh hưởng hàm lượng hạt nano Al2O3 đến tính chất ăn mòn mài mòn hệ lớp phủ chưa nghiên cứu Phương pháp nghiên cứu, kỹ thuật sử dụng: Phương pháp Thiết bị, dụng cụ kĩ thuật Chế tạo hệ lớp phủ Thiết bị phun plasma 3710- Lớp composite 40%TiO2 Al2O3- PRAXAIR-TAFA (Mỹ) Mô tả phủ composite Al2O3- - 40%TiO2 với chiều dày khoảng Phòng thí nghiệm trọng điểm 300 μm thép CT3 Công nghệ Hàn Xử lý bề chế tạo phương pháp phun mặt - Viện Nghiên cứu Cơ phủ plasma khí Điều chế phốt phát Bếp gia nhiệt kết hợp với Dung dịch phốt phát nhơm có tỉ lệ nhơm có chứa hạt khuấy từ, cốc thủy tinh chịu mol P/Al= 3,0 với 20% nước nano Al2O3 nhiệt, cân phân tích Libror bổ sung thêm hạt nanon AEG-220G - Viện Kỹ thuật Al2O3 với hàm lượng thay đổi nhiệt đới 0; 3; 5; 10% theo khối lượng Xử lý nhiệt Lò nung NABERTHERM Các lớp phủ sau chuẩn bị lớp phủ (Đức) - Viện Kỹ thuật nhiệt xong xử lý nhiệt nhiệt độ 400oC đới Quét đường cong Thiết bị đo điện hóa Thế ăn mòn Ecor dòng ăn mòn phân cực catôt AUTOLAB PGSTAT30 (Hà Icor lớp phủ dung anôt xác định Lan) - Viện Khoa học Vật dịch NaCl 3,5% xác định ăn mòn Ecor liệu phương pháp ngoại suy dòng ăn mòn Icor Xác định điện trở Tafel Điện trở phân cực Rp lớp phân cực Rp theo phủ dung dịch NaCl 3,5% tiêu chuẩn ASTM xác định sau thời điểm G59 Phổ tổng trở điện ngâm mẫu khác Phổ tổng trở điện hóa lớp hóa EIS phủ dung dịch NaCl 3,5% xác định sau thời điểm ngâm mẫu khác Chụp ảnh SEM cấu Kính hiển vi điện tử quét Chụp ảnh SEM xác định hình thái trúc mặt cắt ngang SM-6510LV (Nhật Bản) cấu trúc mặt cắt ngang Viện Kỹ thuật nhiệt đới lớp phủ lớp phủ sau thử nghiệm quét đường cong phân cực Phân tích XRD Thiết bị phân tích nhiễu xạ Phân tích XRD xác định thành bề mặt lớp phủ Rơnghen SIEMENS D5005 - phần pha bề mặt lớp phủ sau Trường Đại học Khoa học Tự thử nghiệm quét đường cong nhiên, Đại học Quốc gia Hà phân cực Nội Nghiên cứu khả Thiết bị thử mài mòn UMT- Khả chịu mài mòn chịu mài mòn 3MT (CETR-Mỹ) - Học viện lớp phủ đánh giá theo tiêu lớp phủ Kỹ thuật quân chuẩn ASTM G99 Nội dung nghiên cứu: - Khảo sát biến thiên theo thời gian thông số Ecor, Icor, Rp phổ tổng trở điện hóa lớp phủ Al2O3-40%TiO2 dung dịch NaCl 3,5% Các lớp phủ Al2O340%TiO2 nghiên cứu bao gồm: lớp phủ Al2O3-40%TiO2; lớp phủ Al2O3-40%TiO2 thẩm thấu với phốt phát nhôm không chứa hạt nano Al 2O3; lớp phủ Al2O3-40%TiO2 thẩm thấu với phốt phát nhôm chứa hạt nano Al 2O3 với hàm lượng thay đổi 3; 5; 10% theo khối lượng - Nghiên cứu thành phần pha bề mặt lớp phủ sau ngâm dung dịch NaCl 3,5% - Nghiên cứu hình thái cấu trúc mặt cắt ngang lớp phủ sau ngâm dung dịch NaCl 3,5% - Nghiên cứu độ bền mài mòn lớp phủ Hợp tác quốc tế (nếu có): Khơng Tiến độ thực đề tài: Thời gian thực 02/2017 - 03/2017 Nội dung công việc Tìm hiểu tài liệu liên quan chuẩn bị hóa chất 04/2017-09/2017 Khảo sát biến thiên theo thời gian thông số Ecor, Icor, Rp, phổ tổng trở điện hóa lớp phủ Al2O3- 10/2017 40%TiO2 dung dịch NaCl 3,5% Nghiên cứu hình thái cấu trúc mặt cắt ngang thành phần pha bề mặt lớp phủ sau ngâm dung dịch 11/2017 NaCl 3,5% Nghiên cứu độ bền mài mòn lớp phủ 12/2017 Xử lý số liệu viết báo cáo tổng kết đề tài III Kết đề tài Dạng kết dự kiến - Kết nghiên cứu ảnh hưởng hàm lượng hạt nano Al2O3 đến khả bảo vệ chống ăn mòn mơi trường NaCl 3,5% chống mài mòn hệ lớp phủ composite Al2O3-40%TiO2 thẩm thấu với phốt phát nhơm có chứa hạt nano Al2O3 - Gửi đăng 01 báo tạp chí khoa học chuyên ngành nước Yêu cầu kĩ thuật, tiêu chất lượng - Khả bảo vệ chống ăn mòn môi trường NaCl 3,5% lớp phủ Al2O340%TiO2 thẩm thấu với phốt phát nhơm có chứa hạt nano Al2O3 tốt so với lớp phủ Al2O3-40%TiO2 lớp phủ Al2O3-40%TiO2 thẩm thấu với phốt phát nhôm không chứa hạt nano Al2O3 - Lựa chọn hàm lượng hạt nano Al2O3 thích hợp thêm vào dung dịch phốt phát nhơm nhằm chế tạo hệ lớp phủ Al2O3-40%TiO2 thẩm thấu với phốt phát nhơm có độ bền ăn mòn mài mòn cao so với lớp phủ Al2O3-40%TiO2 IV Các cá nhân tham gia thực đề tài STT Họ tên, học hàm, học vị ThS Phạm Thị Hà Trách nhiệm đề tài Cơ quan công tác Ngày công làm việc (snc) Chủ nhiệm đề tài Viện Kỹ thuật nhiệt đới 15 ThS Phạm Thị Lý Thành viên tham gia nt 13 KS Nguyễn Văn Tuấn Thành viên tham gia nt Ký tên V Dự tốn kinh phí thực đề tài STT Mục chi A Nội dung chi Nội dung chi giao khốn Tiền cơng lao động trực tiếp 7012 Tiền cơng thành viên thực nhiệm vụ theo chức danh Số tiền (đồng) 23.986.000 20.086.000 20.086.000 14.338.500 Chủ nhiệm đề tài Thành viên tham gia 5.747.500 Chi giao khoán khác 3.900.000 6500 Thanh tốn dịch vụ cơng cộng 1.900.000 7750 Chi phí quản lý gián tiếp B 7001 Nội dung chi khơng giao khốn 2.000.000 16.014.000 Chi phí nghiệp vụ chuyên môn 16.014.000 Tổng cộng (A+B) 10 40.000.000 Giải trình mục chi 7001: Mua vật tư, hóa chất, hàng hóa STT Tên vật tư, hóa chất ĐVT Đơn giá Thành tiền (đồng) Số lượng Al2O3 (nano) kg 3.000.000 3.000.000 Al2O3-40% TiO2 Giấy thấm KCl (Merk) NaCl(Merk) Bơm AP1550 SiO2 kg hộp kg kg kg 3.500.000 70.000 550.000 550.000 110.000 20.500 1.5 1 5.250.000 70.000 550.000 550.000 330.000 20.500 10 11 12 13 14 15 Thép CT3 Axeton Giấy mài độ mịn (400) Al(OH)3 (TQ) H3PO4 (TQ) Epoxy NiCr20 #2mm m2 lít tờ kg lít kg kg 450.000 105.000 58.000 170.000 361.500 231.000 1.780.000 2 10 1 2 900.000 210.000 580.000 170.000 361.500 462.000 3.560.000 Tổng 16.014.000 Giải trình mục chi 7012: Tiền công thành viên thực nhiệm vụ theo chức danh TT Họ tên Dự kiến kết Chức danh Số ngày công làm việc (snc) Hệ số tiền công theo ngày (hstcn) 0,79 955.900 0,25 302.500 Tiền công = snc*hstcn *lcs (đồng) (1) Nội dung nhiệm vụ 1: Viết thuyết minh đề tài Phạm Thị Hà Chủ nhiệm đề tài Phạm Thị Lý Thành viên tham gia Xây dựng 01 thuyết minh đề tài duyệt (2) Nội dung nhiệm vụ 2: Tạo mẫu nghiên cứu - Chế tạo hệ lớp phủ composite Al2O3-40%TiO2; Điều chế phốt phát nhơm có chứa hạt nano Al2O3 với hàm lượng khác 3, 5, 10% theo khối lượng; xử lý nhiệt hệ lớp phủ Chế tạo mẫu, điều chế phốt Phạm Thị Hà Chủ nhiệm đề tài 0.79 4.779.500 phát nhôm Điều chế phốt Phạm Thị Lý Thành viên tham gia 0.25 907.500 phát nhôm Nguyễn Văn Tuấn Thành viên tham gia Xử lý nhiệt 0.25 907.500 (3) Nội dung nhiệm vụ 3: Khảo sát biến thiên theo thời gian thông số E cor, Icor, Rp, phổ tổng trở điện hóa dung dịch NaCl 3,5% lớp phủ Al2O3-40%TiO2 thẩm thấu phốt 11 phát nhôm không chứa hạt nano Al2O3 có hạt nano Al2O3 với hàm lượng 3, 5, 7, 10%; Nghiên cứu thành phần pha, hình thái cấu trúc mặt cắt ngang lớp phủ sau thử nghiệm Khảo sát biến thiên Phạm Thị Hà Chủ nhiệm đề tài 0.79 5.735.400 thông số điện hóa, nghiên cứu thành phần pha, phân tích Phạm Thị Lý Thành viên tham gia 0.25 2.117.500 mặt cắt ngang lớp phủ Khảo sát biến thiên Nguyễn Văn Tuấn Thành viên tham gia 0.25 907.500 thơng số điện hóa (4) Nội dung nhiệm vụ 4: Viết báo cáo tổng kết, viết 01 báo Tổng hợp kết quả, viết báo Phạm Thị Hà Chủ nhiệm đề tài 0,79 2.867.700 cáo, báo cáo tổng kết Phạm Thị Lý Thành viên tham gia 0,25 605.000 Viết báo gửi đăng tạp chí Bảng tổng hợp tiền cơng lao động: TT Chức danh thực nhiệm vụ Họ tên Số ngày cơng làm việc(snc) Thành tiền Cơng thức tính Phạm Thị Hà Chủ nhiệm đề tài 15 14.338.500 1.210.000*0,79*15 Phạm Thị Lý Thành viên tham gia 13 3.932.500 1.210.000*0,25*13 Nguyễn Văn Tuấn Thành viên tham gia 1.815.000 1.210.000*0,25*6 Ngày tháng năm 2017 Chủ nhiệm đề tài Chủ tịch Hội đồng xét duyệt Ths Phạm Thị Hà PGS.TS Đinh Thị Mai Thanh 12 Viện trưởng GS.TS Thái Hoàng ... Trans Nonferrous Met Soc China, Vol 26, pp 1336−1344 (2016) N Hegazy, M Shoeib, Sh Abdel-Samea, H.Abdel-Kader, Effect of Plasma Sprayed Alumina Coating on Corrosion Resistance, 13th International... properties of Al2O3-13% TiO2 coatings sprayed using nanostructured powders, Rare Metals, Vol 26, pp 391– 397 (2007) R Yilmaz, A.O Kurt, A Demir, Z Tatll, Effects of TiO2 on the mechanical properties of... Transactions of Nonferrous Metals Society of China, Vol 25, pp 175–183 (2015) 11 K Jafarzadeh, Z Valefi, B Ghavidel, The effect of plasma spray parameters on the cavitation erosion of Al2O3 –TiO2 coatings,