Journal of Science: Advanced Materials and Devices (2018) 371e379 Contents lists available at ScienceDirect Journal of Science: Advanced Materials and Devices journal homepage: www.elsevier.com/locate/jsamd Original Article Mechanical behaviour and damping properties of Ni modified CueZneAl shape memory alloys Kenneth Kanayo Alaneme*, Shaibu Umar Department of Metallurgical and Materials Engineering, Federal University of Technology, Akure PMB 704, Nigeria a r t i c l e i n f o a b s t r a c t Article history: Received 26 February 2018 Received in revised form 18 May 2018 Accepted 25 May 2018 Available online June 2018 The microstructure, mechanical behaviour and damping properties of Cue18Zne7AlexNi alloys (where x ¼ 0.1, 0.2, 0.3 and 0.4) were investigated The CueZneAl alloys were produced by casting and then subjected to a homogenization e cold rolling e annealing treatment scheme Optical-, scanning electron-microscopy and X-ray diffraction analysis were utilized for structural characterization of the alloys, while tensile test, fracture toughness, and hardness measurement were used to assess the mechanical properties The results show that all the alloy compositions consisted of the predominating CuZn phase Sharp edged elongated grain structures were observed in the unmodified and the 0.4% Ni modified CuZnAl alloys, while the 0.1, 0.2 and 0.3 %Ni modified CuZnAl alloy compositions, had more of granular/curved/round grain edges and smaller grain widths The hardness of the unmodified CuZnAl alloy (294.5 ± 2.08 VHN) was lower than that of the Ni modified CuZnAl ones with an increase in hardness ranging between 23.5 and 38.4% The tensile strength, the percentage elongation (10.7e14.3%) and the fracture toughness of the 0.1, 0.2 and 0.3% Ni modified CuZnAl alloys were observed to be higher than those of the unmodified and the 0.4 %Ni modified CuZnAl alloys The 0.2% Ni modified CuZnAl alloy had the highest damping capacity among all compositions under investigation, while the 0.4% Ni modified one showed the least capacity to serve as a damping material © 2018 The Authors Publishing services by Elsevier B.V on behalf of Vietnam National University, Hanoi This is an open access article under the CC BY license (http://creativecommons.org/licenses/by/4.0/) Keywords: CuZnAl alloys Shape memory capacity Micro-alloying Mechanical behaviour Damping properties Structural characterization Introduction There is a growing attention to the problems created by mechanical, structural and noise vibrations in the environment on the account of industrial processes, seismic events, excavation, construction, mining, and exploration activities [1e3] These vibration sources can generate diverse effects ranging from mild discomfort and general machinery inefficiencies to collapse of structures, loss of investments, lives and properties [3,4] In order to mitigate the potential hazards which could arise from such vibrations, there is growing interest in the development of damping materials for vibration control in engineering structures and systems [4e6] Damping materials possess the inherent capacity of attenuating vibrations by dissipating the energy absorbed during the vibration to a safe mode such as heat, usually by hysteretic actions [7] There is a wide range of engineering materials with damping ability * Corresponding author E-mail address: kalanemek@yahoo.co.uk (K.K Alaneme) Peer review under responsibility of Vietnam National University, Hanoi among which shape memory alloys (SMAs) have been found extremely useful [8,9] Shape memory alloys are known principally for their shape memory effect and pseudoelastic properties, but have also been observed to possess high damping capacity e which makes them attractive for the design of vibration control devices [10,11] The high damping capacity observed in SMAs has been attributed to the high internal friction occurring during martensitic transformation, which manifests in the loss of energy by the movement between the martensite variant interfaces and the parent martensite habit planes [12,13] These remarkable damping properties have been observed principally in NiTi and Cu based SMAs CuZnAl based SMAs are however the focus of this research because of its relatively cheaper processing cost and its relatively superior strain recovery compared to other Cu based SMAs [14] The damping properties of CuZnAl based SMAs have been the subject of several investigations [15,16] Nai-chao [17] showed that the damping performance of CuZnAl SMAs is dependent on whether it is in martensitic or austenitic state The area enclosed by the hysteretic loop e which is a measure of the damping capacity e was observed to be larger in the martensitic state than in the https://doi.org/10.1016/j.jsamd.2018.05.002 2468-2179/© 2018 The Authors Publishing services by Elsevier B.V on behalf of Vietnam National University, Hanoi This is an open access article under the CC BY license (http://creativecommons.org/licenses/by/4.0/) 372 K.K Alaneme, S Umar / Journal of Science: Advanced Materials and Devices (2018) 371e379 austenitic state The former was thus better suited for vibration control application Wu et al [18], studied the damping characteristics of the inherent and intrinsic internal friction of CuZnAl SMAs containing varied Zn content It was reported that the damping capacity was sensitive to the Zn composition of the alloys Compositions containing 7.5e8.5 wt.% Zn were found to have higher damping capacities compared to compositions containing wt.% Zn (Cu7Zn11Al), because the g0 martensite phase they are characterized which possesses a 2H type structure with abundant movable twin boundaries Cimpoesu et al [19] studied the effect of stress on damping capacity of CuZnAl SMAs It was observed that the internal friction peak in these SMAs, is influenced by the temperature and deformation Also lean amounts of elements like iron, lead, and nickel present in the CuZnAl alloy, helped improve the damping capacity of the alloy The role of these elements (iron, lead and nickel) when used independently as additions to the CuZnAl alloy was however not covered by the study It is recalled that the use of elements such as Fe, B, Ni, Ti, among others as micro-alloying additions in Cu based SMAs, have been reported to modify the grain structure; and consequently, improve the toughness and the overall mechanical performance of the SMAs [14] Ni in particular, has been reported to help raise the transformation temperature of Cu based alloys, but its impact on mechanical and damping behaviour when used as micro-alloying addition in CuZnAl alloys has not received comprehensive reportage in literature This happens to be the focus of the present study, which aims at assessing the potentials of Ni modified CuZnAl SMAs for structural and damping applications where there is a growing quest for functional and cheap alternatives to NiTi based SMAs Experimental 2.1 Materials preparation Conventional liquid metallurgy route was utilized for the production of the Ni modified CuZnAl alloys following procedures in accordance with Alaneme [20] Five compositions of the alloys were produced containing: Cu18Zn7Al as base alloy composition, 0.1, 0.2, 0.3 and 0.4 wt.% Ni additions to four different heats of the Cu18Zn7Al alloy e for the production of the four Ni modified alloy compositions A crucible furnace was used for the melting operation, and the melts cast into cast iron metallic moulds The chemical compositions of the five CuZnAl based alloys produced were determined by SEM-EDS analysis, and are presented with their respective sample designations in Table A homogenization treatment performed at 800 C for h followed with air cooling, was undertaken to improve the chemical and microstructural homogeneity in the alloys produced They were subsequently cold deformed to 10% reduction of the original thickness, using a miniature cold rolling machine; and thereafter, annealed at 450 C for h followed by air cooling to eliminate cold deformation induced internal stresses developed in the samples The samples for mechanical and damping tests, microstructural and phase analysis, were then machined to standard specifications before a final Table Chemical composition of the unmodified and Ni modified CuZnAl alloys Sample Approximate composition Cu Zn Al Ni A B C D E Cue18Zne7Al Cue18Zne7Ale0.1Ni Cue18Zne7Ale0.2Ni Cue18Zne7Ale0.3Ni Cue18Zne7Ale0.4Ni 74.77 74.75 74.64 74.59 74.56 18.15 18.20 18.06 18.03 18.08 7.08 6.95 7.10 7.12 6.96 e 0.1 0.2 0.3 0.4 annealing at 400 C for h followed by water quenching at room temperature, was performed to eliminate machining stresses on the samples 2.2 Microstructure and phase characterization The structures of the produced alloys were characterized using optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffractometry (XRD) in accordance with Alaneme et al [21] The microstructures of the CuZnAl alloys produced were studied using a Zeiss optical microscope The samples were prepared to metallographic finish using a series of grinding and polishing processes The mirror finish surface produced on each sample was etched by swabbing for 10e20 s using a solution containing g ferric chloride, 10 ml HCl, and 95 ml ethanol, after which microstructural analysis was performed on the samples The optical microscopy analysis was complemented with detailed microstructural and compositional studies using a TESCAN VEGA3 thermionic emission scanning electron microscope system with accessories for energy dispersive spectroscopy (EDS) The SEM analysis entailed the use of back scattered electron (BSE) and secondary electron (SE) modes imaging for assessing the phase and the grain distribution, while SEM-EDS analysis was used for the determination of the chemical compositions of the CuZnAl alloys XRD analysis was finally utilised for the phase characterization of the CuZnAl alloys produced The samples for the analysis were prepared following standard procedures The crystalline phases present and their peak intensities were determined using a PANanalytical Empyrean diffractometer with PIXCEL detector and Fe filtered Co-Ka radiation source was used for the analysis The analysis was performed from diffraction 2q angle spectral range of 0 to 120 while the phases were identified using the X'Pert Highscore plus software The crystal structures of the phases identified were determined by analyzing the pattern of the diffracting crystal planes (hkl) for the entire range of the 2q diffraction angles [22] 2.3 Mechanical testing A Vickers hardness scale was used for the evaluation of the hardness of the alloys, using a hardness testing machine The samples were prepared with fine finished plane parallel surface, while the testing procedure was in accordance with the ASTM E9217 standard [23] The hardness test was performed using a 30 kgf load for a dwell time of 10 s The hardness indentation was repeated for a minimum of five times and readings within the margin of 2% were taken for the determination of the average hardness values The tensile testing was performed on the as-produced CuZnAl alloys using a universal testing machine The samples for the test were machined to tensile test specification of mm diameter and 30 mm gauge length The test samples were mounted on the testing platform and pulled in tension to fracture at a strain rate of 10À3/s The samples preparation, testing procedure and data analysis were performed following the recommendations of ASTM E8/E8M-15a [24] standard Three repeated tests were performed for each CuZnAl alloy composition produced to guarantee the reliability and to assure the reproducibility of the test results The ultimate tensile strength and strain to fracture were evaluated from the stressestrain curves developed from the test conducted The fracture toughness values of the CuZnAl alloys were evaluated using the circumferential notch tensile (CNT) testing approach in accordance with Alaneme [25] The CuZnAl alloy samples were machined to the test specifications: gauge length of 27 mm, gauge diameter of mm (D), notch diameter of 4.2 mm (d), K.K Alaneme, S Umar / Journal of Science: Advanced Materials and Devices (2018) 371e379 and notch angle of 60 The samples were mounted on the testing stage and subjected to tensile loading to fracture using a universal testing machine operated at a strain rate of 10À3/s The fracture loads (Pf) obtained from the CNT samples' load e extension plots were used to evaluate the fracture toughness of the alloys based on the relation [26]: Pf D = KIC ¼ D À 1:27 1:72 d (1) where D and d are the specimen diameter and the diameter of the notched section, respectively The results were validated for plane strain condition required for valid fracture toughness determination using the relations in accordance with Nath and Das [27]: D! K1C sy 2 (2) Three repeated tests were performed for each CueZneAl alloy composition to ensure that generated results are consistent and hence reliable 2.4 Damping behaviour The temperature dependence of the damping properties of the CuZnAl alloys were assessed on a dynamic mechanical analyzer, using the three-point bending deformation mode in accordance with the ASTME756-05 [28] standard Rectangular bar samples with dimensions of 40 mm  mm  0.9 mm, were prepared for the damping properties tests For the measurements of the temperature dependent damping properties, the test conditions were set to strain amplitude (ε) of 10 mm, vibration frequency ( f ) of and Hz, temperature range (t) from room temperature to 250 C, and heating rate 00 (T0 ) of C/min The loss modulus (E ) and the storage modulus (E0 ) were determined from the test, and the damping capacity measured from the loss tangent (tan d), using the relation [29]: 00 tand ¼ E E0 (3) Results and discussion 3.1 Microstructure and phase analysis of the CueZneAl alloys 3.1.1 Optical microscopy The optical micrographs of the unmodified and Ni modified CuZnAl alloys are presented in Fig Fig 1a shows the optical micrograph of the unmodified CuZnAl alloy, which is observed to contain sharp edged directionally solidified grains The elongated grain feature is very common in CuZnAl shape memory alloys within the composition range considered in this research, and specifically matches the structural features reported in [30e32] The CuZn Al alloy composition modified with 0.1% Ni (Fig 1b), shows a significantly modified grain morphology from the sharp edged feature observed for the unmodified CuZnAl alloy to mostly granular/polygonal shaped grain structure The round shaped grains appear smaller in size compared to those in the unmodified CuZnAl alloy For the 0.2% Ni modified CuZnAl alloy (Fig 1c), the grain structure consists of finer and sparsely distributed elongated grains The 0.3% Ni modified CuZnAl alloy (Fig 1d), also shows a directionally solidified grain structure, but with some curve/round edged grain features The 0.4% Ni modified CuZnAl alloy (Fig 1e), 373 equally contains dominantly elongated grains although the longitudinal lengths of the grains are seen slightly shorter than those observed for the unmodified CuZnAl alloy (Fig 1a) Table shows the average grain width (transversal axis thickness) of the unmodified and Ni modified CuZnAl alloys It is observed that the average grain width decreases from 7.9 mm for the unmodified CuZnAl alloy to as low as 3.8 mm for the 0.2% Ni modified CuZnAl alloy, which corresponds to approximately 52% decrease in the grain width The increase in the Ni content above 0.2%, is observed to result in a marginal grain refinement and in the grain width coarsening for the 0.3% and 0.4% Ni modified CuZnAl alloys, respectively Grain width increase as high as 22.7% was observed with the 0.4% Ni addition in comparison to the base CuZnAl alloy The analyses from Fig and Table show that the amount of Ni used as micro-alloying addition in CuZnAl alloy significantly affects its solidification patterns Grain modification was more pronounced and distinct for the 0.1% Ni modified CuZnAl alloy where a dramatic transformation from sharp edged elongated grain structure to a predominantly granular structure was observed The 0.2% Ni addition resulted in the finest size and least predominant presence of the needle-like structures and the 0.3% Ni addition only induces slight changes in the grain edge morphology, while the 0.4% Ni modified CuZnAl alloy composition shows changes in both grain growth and in grain edge morphology 3.1.2 SEM observations Representative secondary electron mode images of the unmodified and selected modified CueZneAl alloys are presented in Fig They all demonstrate profoundly identical structure features as observed in the corresponding optical micrographs of the investigated alloys (Fig 1) As it is seen in Fig 2a, the unmodified alloy microstructure consists of predominantly elongated grains with sharp edges In Fig 2b, the micrograph of the 0.2% Ni modified CuZnAl alloy shows predominantly a finer structure with a few needle-like precipitated features, while in Fig 2c the 0.4% Ni modified CuZnAl alloy is seen to consist of slightly elongated larger size grains compared to the unmodified one These results confirm the observations from the optical microscopy investigation that the presence of Ni in the CuZnAl alloys significantly alters their solidification patterns with essentially varied grain morphology This sort of influence of Ni as micro-alloy addition, has also been reported for several other micro-alloying elements [14,33,34] Fig with representative EDS spectra confirms the presence of Cu, Zn, Al and Cu, Zn, Al, Ni for the unmodified and the 0.4% Ni modified CuZnAl alloy, respectively 3.1.3 Analysis of X-ray diffraction The X-ray diffraction analysis of the unmodified and Ni modified CuZnAl alloys is presented in Fig As it is observed from the patterns, all samples consist essentially of CuZn phase despite the differences in grain morphology (see Figs and 2) There are slight shifts in the peak positions for each of the alloy compositions (although less than 2 ) which is a common feature in alloys with slightly altered alloying composition (due to the difference in lattice parameters) The analysis of the pattern of the diffracting crystal planes for the entire 2q diffraction angles and the lattice parameters confirm the CuZn phase to be the b e phase, which from studies has been shown to be martensitic and displays shape memory capacity [35] There are very small peaks of CuAl and NiAl phases observed from the XRD scan for the Ni modified compositions These peaks are, however, not well resolved in the plots because of the small intensities The predominance of the CueZn peaks in the difractograms as analyzed is in agreement with the EDS results presented in Fig 374 K.K Alaneme, S Umar / Journal of Science: Advanced Materials and Devices (2018) 371e379 Fig Optical micrographs of (a) unmodified CueZneAl alloy, and (b) 0.1 wt.% Ni-, (c) 0.2 wt.% Ni-, (d) 0.3 wt.% Ni-, and (e) 0.4 wt.% Ni-modified CueZneAl alloys Table Average lath martensite transverse axis thickness in the CuZnAl alloys produced Sample designation Composition Average lath martensite thickness (mm) A B C D E Cue18Zne7Al Cue18Zne7Ale0.1Ni Cue18Zne7Ale0.2Ni Cue18Zne7Ale0.3Ni Cue18Zne7Ale0.4Ni 7.9 7.0 3.8 7.1 9.7 ± ± ± ± ± 0.04 0.02 0.02 0.02 0.04 K.K Alaneme, S Umar / Journal of Science: Advanced Materials and Devices (2018) 371e379 375 Fig Representative SEM secondary electron mode micrographs of (a) unmodified CueZneAl alloy, (b) 0.2 wt.% Ni-, and (c) 0.4 wt.% Ni-modified CueZneAl alloys 3.2 Mechanical behaviour 3.2.1 Hardness The hardness values of the unmodified and Ni modified CuZnAl alloys are presented in Fig It is observed that the hardness values of the CuZnAl alloys with Ni addition, are basically greater than that of the unmodified CuZnAl alloy The maximum increase is obtained in the 0.2% Ni modified CuZnAl alloy, which corresponds to a 38.4% increase in hardness The hardness, however, is found decreased with the further increase of the Ni addition, albeit not congruently with Ni concentration The improved hardness observed in the Ni modified CuZnAl alloys, is attributed to the presence of Ni as micro-alloying addition, which resulted in the reduction of the elongated grain width (i.e grain thickness) and the modification of grain edge morphology The 0.2% Ni modified CuZnAl alloy has the highest hardness value, as it is seen in Fig and Table 2, this sample also contains the finest size grain structure with the smallest grain width, respectively This improved resistance to indentation with the decreased grain size is in agreement with the HallePetch relation [36] 3.2.2 Tensile properties The stressestrain plots of the unmodified and Ni modified CuZnAl alloys are presented in Fig 6, while the ultimate tensile strength and percentage elongation plots are presented in Figs and 8, respectively As it can be seen in Fig 7, the ultimate tensile strength (UTS) of the unmodified and the 0.4% Ni modified CuZnAl alloys show values of 450.85 MPa and 452.62 MPa, respectively; which are lower than the UTS values of the other Ni modified CuZnAl alloys Compared to the unmodified CuZnAl alloy, tensile strength increases of 9.8, 12.1, 13.7, and 0.4% were obtained with the use of 0.1, 0.2, 0.3, and 0.4 wt.% Ni, respectively The low tensile strength of the unmodified and 0.4 wt.% Ni modified CuZnAl alloys can be linked to the relatively larger width of the elongated grains in these samples Also the sharp edges of the grain structure for both samples is another important factor Sharp tip grain edges usually serve as stress concentration sites which would suggest that the nominal stress acting on the material is considerably amplified to values exceeding its maximum stress bearing capacity at the grain tips [37] Accordingly, the improved tensile strength of the 0.1, 0.2, and 0.3 wt.% Ni modified CuZnAl alloys, is linked to the finer elongated grain width coupled with the change in the grain morphology to the granular structure (for the 0.1% Ni modified alloy), and the round/elliptical grain edges (for the 0.3% Ni modified alloy) The finer grain structure, round/elliptical grain edges and granular structures observed in these Ni modified CuZnAl alloys, reduce the 376 K.K Alaneme, S Umar / Journal of Science: Advanced Materials and Devices (2018) 371e379 Fig Representative SE mode images and EDS profiles of (a) unmodified CueZneAl alloy, and (b) 0.4 wt.% Ni modified CueZneAl alloy Fig X-ray diffractograms of the unmodified and Ni modified CueZneAl alloys tendency of the grain edges to serve as stress concentration sites Consequently, the nominal applied stress on the alloys must be high to attain the maximum stress bearing capacity values for the process of micro-crack formation and fracture to be heralded in the alloys The significance of the results is that the addition of between 0.1 and 0.3 wt.% Ni to CuZnAl alloy can enhance the stress transmission/bearing capacity of the alloy The percentage elongation of the unmodified and Ni modified CuZnAl alloys are presented in Fig It is observed that the elongation values of the unmodified and 0.4 wt.% Ni modified CuZnAl K.K Alaneme, S Umar / Journal of Science: Advanced Materials and Devices (2018) 371e379 Fig Hardness values of the unmodified and Ni modified CueZneAl alloys 377 Fig Percentage elongation of the unmodified and Ni modified CueZneAl alloys exhibit less ductility [36] In the case of the 0.1, 0.2 and 0.3 wt.% Ni modified CuZnAl alloys, the development of a granular structure, fewer sharp edged grains, and curved/elliptical grain edges, respectively; are responsible for the high plastic strain sustaining capacity of these alloys Fig Stressestrain curves of the unmodified and Ni modified CueZneAl alloys 3.2.3 Fracture toughness The fracture toughness of the unmodified and the Ni modified CuZnAl alloys are presented in Fig It is clearly seen that all the Ni modified CuZnAl alloys except the 0.4% Ni modified composition, show fracture toughness values that are higher than that of the unmodified one The fracture toughness increase of 13.4, 28, and 12% are obtained for the 0.1, 0.2 and 0.3% Ni modified CuZnAl alloys, respectively, while a 4% decrease in fracture toughness is observed for the 0.4% Ni modified one These observations imply that the 0.1e0.3% Ni microalloying addition in the CuZnAl alloy improves its resistance to crack propagation, while the 0.4% Ni microalloying addition, is detrimental to the toughness of the CuZnAl alloys The same reasons attributed to the improved ductility are valid for the improvement in the fracture toughness e that is, the change in the grain edge shape from sharp edged to round/elliptical shape for the 0.1 and 0.3 Ni modified CuZnAl alloys and to the fewer elongated grain structure in the 0.2% Ni modified one A preponderance of sharp edge grains is known to facilitate the triaxial stress state at the grain tip which suppresses yielding and accentuates brittle fracture susceptibility [21] Fig Ultimate tensile strength of unmodified and Ni modified CueZneAl alloys alloys are almost at the same level (8.5e8.6%) But there is an improvement in the elongation values for the other Ni modified CuZnAl alloys ranging between 10.7e14.3% The CuZnAl alloy modified with 0.3 wt.% Ni, shows the highest elongation value of 14.3% This implies that the addition of 0.1e0.3 wt.% Ni can result in improved ductility in CuZnAl alloys and hence enhanced plastic workability of these The reasons for the lower percentage elongation of the unmodified and 0.4% Ni modified CuZnAl alloys, is tied to the sharp tip grain edges, which can restrain plastic deformation due to the triaxial stress state created at such sites The plasticity restraint makes the alloys more resistant to yielding and hence Fig Fracture toughness of the unmodified and Ni modified CueZneAl alloys 378 K.K Alaneme, S Umar / Journal of Science: Advanced Materials and Devices (2018) 371e379 3.3 Damping properties Fig 10 shows the damping capacity, storage modulus, and loss modulus of the unmodified and Ni modified CuZnAl alloys As it is seen in Fig 10a, at Hz test frequency only the 0.2% Ni modified CuZnAl alloy shows higher damping capacity values than the unmodified one for the test temperature range of 25 Ce250 C The 0.4% Ni modified CuZnAl alloy exhibits the least damping capacity of all the alloys under investigation The Peak internal friction of 0.43 was obtained at 75 C for the 0.2% Ni modified CuZnAl alloy, while the unmodified, the 0.1 and 0.3% Ni modified CuZnAl alloys show less obvious damping peaks A peak internal friction of 0.026 was observed for the 0.4% Ni modified CuZnAl alloy at 225 C; but this alloy maintains a constant low value of 0.001 from room temperature to about 200 C The same trend is observed for Hz frequency (Fig 10b) where also the 0.2% Ni modified CuZnAl alloy shows the highest damping capacity for the test temperature range of 25 Ce250 C However, a peak internal friction of 0.034, which is lower than 0.043 at Hz is obtained at 50 C for this 0.2% Ni modified CuZnAl composition The unmodified alloy exhibits the next highest damping capacity among other alloy compositions, while the 0.4% Ni sample again exhibits the least damping capacity Damping capacity is associated with the movement and reorientation of martensite variants and Fig 10 (a) Damping capacity of the unmodified and Ni modified CueZneAl alloys at Hz test frequency; (b) Damping capacity of the unmodified and Ni modified CueZneAl alloys at Hz test frequency; (c) Storage modulus of the unmodified and Ni modified CueZneAl alloys at Hz test frequency; (d) Storage modulus of the unmodified and Ni modified CueZneAl alloys at Hz test frequency; (e): Loss modulus of the unmodified and Ni modified CueZneAl alloys at Hz test frequency; and (f) Loss modulus of the unmodified and Ni modified CueZneAl alloys at Hz test frequency K.K Alaneme, S Umar / Journal of Science: Advanced Materials and Devices (2018) 371e379 interfaces [14] The results described above, thus, imply that such movement and orientation of the martensite variants are better facilitated in the 0.2% Ni modified CuZnAl alloy than in others The low damping capacity of the 0.4% Ni modified CuZnAl alloy will accordingly be linked to the restriction of the movement of the parent phase/martensite interfaces and the martensite variants [18] This may be on the account of the population of the Ni solute atoms which can wield a pinning effect on the boundaries and interfaces This is why smaller internal friction peaks are observed for this composition It should be noted that at Hz, the 0.1 and 0.3% Ni modified alloys show peak internal frictions of about 0.015 and 0.013, respectively, at 225 C The E’ “storage modulus” (see Fig 10c and d) as a measure of the capacity of a material to absorb and to store energy induced by vibrations [29] is observed to be stable for the temperature range of 25 Ce250 C for all alloy compositions, with the exception of the 0.4% Ni modified one, which is observed to exhibit a drastic drop in storage modulus (energy absorption capacity) at about 200 C The 0.1% Ni modified CuZnAl alloy shows the highest storage modulus of 130,300 MPa, while the 0.2% modified one has the least storage modulus of averagely 4500 MPa It is noted that the storage modulus was not affected by the frequency (either or Hz) The E” “loss modulus” (see Fig 10e and f) meaning the energy dissipation capacity in form of heat of the material [29] shows an intermittent variability in the temperature range of 25 Ce200 C, but beyond this temperature, there is continuous increase in the loss modulus with the increase in temperature The 0.1 and 0.2% Ni modified compositions exhibit higher loss modulus values compared with the others above 200 C It is noted that at about 200 C, there is a dramatic and significant drop in the loss modulus of the 0.4% Ni modified CuZnAl alloy This suggests that this composition may not be suitable for damping applications Conclusion The microstructure, mechanical behaviour and damping properties of unmodified and 0.1e0.4 Ni modified Cue18Zne7Al alloys were investigated Sharp edged elongated grain structures synonymous with the directional solidifications were observed in the unmodified and the 0.4% Ni modified CuZnAl alloys The grain structure was, however, significantly altered in the 0.1, 0.2 and 0.3 % Ni modified CuZnAl alloys, where granular structure, small grain width with fewer sharp edge grains, and curved/round grain edges, respectively, were observed The mechanical properties of the unmodified and the 0.4% Ni modified CuZnAl alloys were generally lower than those of the 0.1 and 0.3% Ni modified ones The 0.4% modified CuZnAl alloy showing the lowest damping capacity, does not seem, thus, suitable to serve as a damping material, while the 0.2% Ni modified one exhibits the highest damping capacity among all the CuZnAl alloy compositions References [1] A.S Elnashai, L.D Sarno, Fundamentals of Earthquake Engineering, Publisher, State, 2008 [2] J.V Farahani, Man-made major hazards like earthquake or explosion; case study, Turkish mine explosion, Iran J Public Health 43 (10) (2014) 1444e1450 [3] H Guo, Understanding global natural disasters and the role of earth observation, Int J Digit Earth (3) (2010) 221e230 [4] F.P Santos, Vibration Control with Shape-memory Alloys in Civil Engineering Structures, PhD thesis, Faculty of Science and Technology, Nova University of Lisbon, 2011 [5] B.F Spencer, S Nagarajaiah, State of the art of structural control, J Struct Eng 129 (2003) 845e856 [6] H Qian, H Li, G Song, W Guo, Recentering shape memory alloy passive damper for structural vibration control, Hindawi Publishing Corporation, Math Probl Eng (2013) 13, 963530 379 [7] O.E Ozbulut, S Hurlebaus, R Desroches, Seismic response control using shape memory alloys: a review, J Intell Mater Syst Struct 22 (2011) 1531e1549 [8] H Mevada, D Patel, Experimental determination of structural damping of different materials, Procedia Eng 144 (2016) 110e115 [9] A Treviso, B Van Genechten, D Mundo, M Tournour, Damping in composite materials: properties and models, Compos Part B Eng 78 (2015) 144e152 [10] K.C Atli, The effect of tensile deformation on the damping capacity of NiTi shape memory alloy, J Alloys Compds 679 (2016) 260e267 [11] A.G Shivasiddaramaiah, U.S Mallik, L Shivaramu, S Prashantha, Evaluation of shape memory effect and damping characteristics of Cu-Al-Be-Mn shape memory alloys, Persp Sci (2016) 244e246 [12] J.V Humbeeck, S Kustov, Active and passive damping of noise and vibrations through shape memory alloys: applications and mechanisms, Smart Mater Struct 14 (2005) S171eS181 [13] N Koeda, T Omori, Y Sutou, H Suzuki, M Wakita, R Kainuma, K Ishida, Damping properties of ductile Cu-Al-Mn based shape memory alloys, Mater Trans 46 (1) (2005) 118e122 [14] K.K Alaneme, E.A Okotete, Reconciling viability and cost-effective shape memory alloy options e a review of copper and iron based shape memory metallic systems, Eng Sci Technol Int J (2016), https://doi.org/10.1016/ j.jestch.2016.05.010 [15] V Torra, A Isalgue, F.C Lovey, M Sade, Damping via Cu-Zn-Al shape memory alloys (SMA): the action of diffusive effects on the macroscopic description, in: Proc SPIE 4696, Smart Structures and Materials 2002: Smart Systems for Bridges, Structures, and Highways, 28 June 2002, https://doi.org/10.1117/12.472554 [16] S Ceresara, A Giarda, G Tiberi, F Mazzolai, B Coluzzi, Damping characteristics of Cu-Zn-Al shape memory alloys, J Phys IV Colloq 01 (C4) (1991) C4e235-C4-240 [17] S Nai-chao, S Ke-qing, S Shao-chun, L Hai-xia, Damping performance of CuZn-Al shape memory alloys in engineering structures, J Cent S Univ Technol 11 (3) (2004) 246e251 [18] S.K Wu, W.J Chan, S.H Chang, Damping characteristics of inherent and intrinsic internal friction of Cu-Zn-Al shape memory alloys, Metals (2017) 397, https://doi.org/10.3390/met7100397 [19] N Cimpoesu, S Stanciu, M Mayer, I Ionita, R.H Cimpoesu, Effect of stress on damping capacity of a shape memory alloy CuZnAl, J Optoelectroni Adv Mater 12 (2) (2010) 386e391 [20] K.K Alaneme, Indentation resistance and corrosion behaviour of FeeMn modified CueAl alloys in selected industrial and biological fluids, Acta Metall Slov 20 (4) (2014) 366e374 [21] K.K Alaneme, E.A Okotete, N Maledi, Phase characterization and mechanical behaviour of Fe-B modified Cu-Zn-Al shape memory alloys, J Mater Res Technol (2) (2017) 136e146 [22] C Richard Brundle, Charles A Evans Jr., Shaun Wilson, Encyclopedia of Materials Characterization: Surfaces, Interfaces, Thin Films, ButterworthHeinemann, USA, 1992 [23] ASTM E92-17, Standard Test Methods for Vickers Hardness and Knoop Hardness of Metallic Materials, ASTM International, West Conshohocken, PA, 2017 www.astm.org [24] ASTM E8/E8M-15a, Standard Test Methods for Tension Testing of Metallic Materials, ASTM International, West Conshohocken, PA, 2015 www.astm.org [25] K.K Alaneme, Fracture toughness (K1C) evaluation for dual phase medium carbon low alloy steels using circumferential notched tensile (CNT) specimens, Mater Res 14 (2) (2011) 155e160, https://doi.org/10.1590/S151614392011005000028 [26] G.E Dieter, Mechanical Metallurgy, McGraw-Hill, Singapore, 1988 [27] S.K Nath, U.K Das, Effect of microstructure and notches on the fracture toughness of medium carbon steel, J Naval Architect Mar Eng (2006) 15e22 [28] ASTM E756-05, Standard Test Method for Measuring Vibration-damping Properties of Materials, ASTM International, West Conshohocken, PA, 2017 www.astm.org [29] K.P Menard, Dynamic Mechanical Analysis: A Practical Introduction, CRC Press, Boca Raton, Florida, USA, 1999 [30] W Xu, Effects of Gd addition on microstructure and shape memory effect of CueZneAl alloy, J Alloys Compds 448 (2008) 331e335 [31] H.W Kim, A study of the two-way shape memory effects in Cu-Zn-Al alloys by the thermomechanical cycling method, J Mater Process Technol 146 (2004) 326e329 [32] K.K Alaneme, E.A Okotete, M.O Bodunrin, Microstructural analysis and corrosion behaviour of Fe-B modified Cu-Zn-Al shape memory alloys, Cor Rev 35 (1) (2017) 3e12, https://doi.org/10.1515/corrrev-2016-0053 [33] F.J Gil, J.M Guilemany, Effect of Cobalt addition on grain growth kinetics in Cu-Zn-Al shape memory alloys, Intermetallics (1998) 445e450 [34] A.M Furlani, M Stipcich, R Romero, Phase decomposition in a CueZneAleTieB shape memory alloy, Mater Sci Eng A 392 (2005) 386e393 [35] L.G Bujoreanu, On the influence of austenitization on the morphology of ephase in tempered CueZneAl shape memory alloys, Mater Sci Eng A 481e482 (2008) 395e403 [36] T.W Courtney, Mechanical Behaviour of Materials, second ed., Overseas Press, India, 2006 [37] N.E Dowling, Mechanical Behaviour of Materials, fourth ed., Prentice Hall, 2012 ... unmodified and Ni modified CuZnAl alloys Sample Approximate composition Cu Zn Al Ni A B C D E Cue18Zne 7Al Cue18Zne7Ale0. 1Ni Cue18Zne7Ale0. 2Ni Cue18Zne7Ale0. 3Ni Cue18Zne7Ale0. 4Ni 74.77 74.75 74.64 74.59... the CuZnAl alloys produced Sample designation Composition Average lath martensite thickness (mm) A B C D E Cue18Zne 7Al Cue18Zne7Ale0. 1Ni Cue18Zne7Ale0. 2Ni Cue18Zne7Ale0. 3Ni Cue18Zne7Ale0. 4Ni 7.9... 00 tand ¼ E E0 (3) Results and discussion 3.1 Microstructure and phase analysis of the CueZneAl alloys 3.1.1 Optical microscopy The optical micrographs of the unmodified and Ni modified CuZnAl alloys