0000000000000000000000
ARTICLE pubs.acs.org/JPCC Comparison of Two Synthesis Routes to Obtain Gold Nanoparticles in Polyimide Katrien Vanherck,† Thierry Verbiest,‡ and Ivo Vankelecom*,† † ‡ K.U Leuven, Centre for Surface Chemistry and Catalysis, Kasteelpark Arenberg 23, 3001 Heverlee, Belgium K.U Leuven, Molecular and Nanomaterials, Celestijnenlaan 200D, 3001 Heverlee, Belgium ABSTRACT: Gold nanoparticle containing polymer materials find applications in catalysis, facilitated transport, sensing, and separations In this study, two routes to obtain stable gold nanoparticles in a polymer matrix, namely, in situ chemical reduction of a gold salt and the use of preformed poly(vinylpyrrolidone) protected gold nanoparticles, were followed to prepare gold containing polyimide hybrid membranes The influence of the synthesis method on the nanoparticle size, dispersion, and surface plasmon behavior was investigated by transmission electron microscopy, UVvis spectroscopy, and diffuse reflectance spectroscopy Significant differences were found concerning the dispersion and aggregation of the nanoparticles The influence of the synthesis method on the membrane structure and performance was also studied by scanning electron microscopy and in filtrations of dye solutions in ethanol and isopropanol The filtrations were repeated while the gold nanoparticles were plasmonically heated by a green Argon ion laser beam, resulting in localized heating of the membrane and increased fluxes ’ INTRODUCTION To obtain stable metal nanoparticles (NP) in a solid polymeric matrix, two routes are commonly followed First, the NPs can be presynthesized in a solvent that is then used to prepare the polymer matrix In this case, the NPs are usually protected by a ligand to avoid their aggregation Second, the NPs can be formed in situ, by (photo)chemical reduction inside the solid matrix These two methods to prepare NPpolymer composites have been studied for a variety of polymer matrices and gold nanoparticles (GNPs).117 Overall, the first method has been shown to allow a better control of the size of the NPs while the second method strongly reduces the incidence of NP aggregation.4,6 Such problems with aggregation during the incorporation of preformed nanoparticles into a solid matrix may be avoided by surface-modifying the nanoparticles with a suitable agent.4,6,15 A direct comparison of the two methods has so far only been done by Dammer et al for GNPs synthesized in poly([2-methoxy5-(2-ethylhexyloxy)-1,4-phenylene]vinylene).13 However, polymer degradation occurring in the case of in situ reduction, through oxidation by the GNP precursor (H[AuCl4]/tetraoctylammonium bromide/tetraoctylammonium bromide (TOAB) complex), did not allow for a proper comparison Polymeric membranes containing gold nanoparticles have been prepared for various applications, such as (electro)catalysis,8,1719 facilitated transport,14,20 protein separation,21 and sensing,2224 and have potential applications in other areas such as drug delivery When preparing GNPs inside a polymer membrane matrix, it can be expected that both methods will have a different influence on the nanoparticle size and dispersion in the membrane but also on the membrane structure and hence the membrane performance To our knowledge, no comparison r 2011 American Chemical Society between the two methods has been made for a nanofiltration membrane Solvent resistant nanofiltration (SRNF) involves the separation of an organic mixture down to a molecular level by simply applying a pressure gradient over a membrane.25 It has some important advantages compared to other industrial separation processes, such as its energy and waste efficiency To turn SRNF into a viable industrial process, excellent membranes should become available, combining chemical, mechanical, and thermal stability with good rejections and sufficiently high fluxes However, most commercially available membranes for SRNF combine high rejections for low molecular weight (MW) compounds with low fluxes Recently, we have studied the effects of plasmonic heating of GNPs incorporated into nanofiltration membranes on the membrane performance, showing an overall increase of the membrane permeability without affecting its rejection of a low MW dye.26,27 Plasmonic heating is a method more commonly employed in imaging and sensing, drug release, and biomedicine (tumor destruction).6,2833 In most membrane processes, developing a membrane with a higher selectivity is coupled to a loss in permeability and visa versa Photothermal heating of GNP containing membranes is thus of high interest as a potential route to overcome this traditional flux-selectivity trade-off In this paper, two common synthesis routes were used to obtain composite GNPpolyimide phase inversion membranes with varying gold content Polyimide (PI) is a well-known polymer Received: July 29, 2011 Revised: November 17, 2011 Published: November 23, 2011 115 dx.doi.org/10.1021/jp207244y | J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE Table Membrane Compositions (Weight in g in the Casting Solution) for Reference and GNP Containing Membranes Prepared by Two Methods (PRE and ISR) HAuCl4 3H2O [g] membrane method matrimid [g] DMA [g] THF [g] ISR-0 ISR 2.2 4.5 3.3 0 ISR-1 ISR-2 ISR ISR 2.2 2.2 4.5 4.5 3.3 3.3 0.044 0.088 0 0 ISR-3 ISR 2.2 4.5 3.3 0.132 0 ISR-4 ISR 2.2 4.5 3.3 0.176 0 PRE-0 PRE 2.2 4.5 3.3 0.268 PRE-1 PRE 2.2 4.5 3.3 0.044 0.134 0.02 PRE-2 PRE 2.2 4.5 3.3 0.088 0.268 0.04 PRE-3 PRE 2.2 4.5 3.3 0.132 0.45 0.06 PRE-4 PRE 2.2 4.5 3.3 0.176 0.536 0.08 for producing SRNF membranes.25 PI membranes containing GNPs have been prepared by adding presynthesized PVPprotected GNPs by Mertens et al.,8 but they have never before been prepared by in situ reduction of the GNPs It can be anticipated that the two different NP incorporation strategies to be studied will also strongly influence the surface plasmon resonance behavior of the GNPs and thus further change the membrane performance The polymer composites were characterized by UVvis spectroscopy and diffuse reflection spectroscopy (DRS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) The photothermal effect of the selected GNPs on the temperature and flux behavior of the membranes was compared by irradiating the membrane with continuous green laser light during solvent filtrations PVP [g] NaBH4 [g] was obtained The solutions were then allowed to stand until air bubbles had disappeared and were cast onto a nonwoven support material that had been saturated with DMA An automated casting knife (250 μm slid) was used, and the resulting polymer films were immediately immersed into a water bath The reference membrane was yellow, and the membranes containing GNPs were light pink to red-brown in color The membranes were then stored in an IPA bath for h and transferred to an IPA/glycerol bath (volume ratio 60:40) for three days, before being dried in an oven at 60 °C The membranes will further be referred to as PRE-0, PRE-1, PRE-2, PRE-3, and PRE-4, respectively corresponding with the membrane containing 0, 1.0, 2.0, 3.0, and 4.0 wt % GNPs For the in situ chemical reduction (ISR) method, based on Huang et al.,21 HAuCl4 3H2O was added to a PI solution prepared in a mixture of DMA and THF to obtain casting solutions with gold to polymer weight ratios of 1.0, 2.0, 3.0, and 4.0 wt % A similar polymer solution PI was prepared without HAuCl4 3 H2O, as a reference The exact membrane compositions are given in Table The solutions were stirred until homogeneous and cast onto the nonwoven support material After a solvent evaporation step (30s), they were immersed into a water coagulation bath After the immersion, the membranes were moved immediately into a solution of NaBH4 in water to reduce the gold to nanoparticles, upon which the membrane color turned from yellow to dark red The membranes were further kept in IPA and IPA:glycerol and then dried as in Method A The membranes will further be referred to as ISR-0, ISR-1, ISR-2, ISR-3 and ISR-4, respectively corresponding with the membrane containing 0, 1.0, 2.0, 3.0, and 4.0 wt % GNPs Membrane Characterization Diffuse reflectance spectra (DRS) were taken of the membrane surfaces by a PerkinElmer Lambda 40 spectrophotometer with deuterium and wolfram lamps A piece of each membrane was redissolved in DMA, and these GNP solutions were characterized by a PerkinElmer UVvis spectrophotometer Membrane pieces were immersed and broken in liquid nitrogen The cross sections were studied with a Philips XL 30 FEG SEM, a semi-in-lens type SEM with a cold field-emission electron source All SEM samples were first coated with a 1.52 nm Au layer to reduce sample charging under the electron beam using a Cressington HR208 high resultion sputter coater To study the size of the GNPs in the membranes, the cross sections were examined by TEM The membranes were dried and then embedded into Araldite resin Semithin sections for light microscopy with a thickness of μm were made with a Reichert Ultracut E microtome Finally, cubic samples of ’ EXPERIMENTAL SECTION Materials Matrimid9725 PI was obtained from Huntsman (Switzerland) The polyethylene/polypropylene nonwoven fabric Novatexx 2471 was kindly provided by Freudenberg (Germany) Hydrogen tetrachloroaurate(III) trihydrate(HAuCl4 3H2O) and sodium borohydrid (NaBH4, >98.5%) were obtained from SigmaAldrich Poly(vinylpyrrolidone) (10 000 g mol1), N,N0 -dimethylacetamide (99.5%, DMA), tetrahydrofuran (99.5%, THF), isopropanol (99.5%, IPA), and absolute ethanol (EtOH) were obtained from Acros All used water was desionized Membrane Synthesis Membranes were synthesized according to two different methods For the incorporation of presynthesized GNPs (PRE), PVP-protected GNPs were prepared in DMA similar to the synthesis methods described by Teranishi et al.58 and Mertens et al.8 Solutions of HAuCl4 3H2O (0.05, 0.1, and 0.2 mmol) and an amount of PVP (molar ratio monomeric units of PVP/gold = 12) were prepared in DMA (6 g) Then, a freshly prepared NaBH4 solution in DMA (2 g) was added under vigorous stirring (molar ratio NaBH4/gold = 5), and immediately, a color change from yellow to dark red occurred in the solution, indicating the reduction of gold into nanoparticles The solution was characterized by a PerkinElmer UVvis spectrophotometer, and the typical dark red color showed as a large peak at 530 nm, corresponding to the plasmon absorbance band of the GNPs.58 PI was added to the GNP solutions in DMA resulting in four casting solutions with different gold/PI weight ratios (1.0, 2.0, 3.0, and 4.0%) A similar PVP containing polymer solution PI in DMA and THF without GNPs was prepared as a reference The compositions are given in Table The solutions were stirred at room temperature until a homogeneous mixture 116 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE Figure Chemical structures of dye rose bengal (1017 Da) and methyl orange (327 Da) The irradiation improvement factor (IIF) is calculated as the percentual increase in permeance or rejection when the membrane is irradiated, as follows: Figure Schematic representation of a dead-end filtration cell equipped for laser irradiation of the GNP containing membrane during separations about mm side were obtained Double stained 70 nm thin sections were examined in a Zeiss EM900 electron microscope Chemicals and procedures for sample treatments were obtained from the Laboratory for Entomology of the K.U Leuven, Leuven, Belgium The particle size distributions of the GNPs were measured from the TEM pictures using ImageJ software (Image Processing and Analysis in Java59) Dead-End Filtrations Dead-end membrane filtrations were carried out in a specially made glass filtration cell (Figure 1) A transparent glass window was built in the top to allow a laser beam to pass and illuminate 40% of the active membrane surface (0.001736 m2) For each filtration, a membrane was mounted in the cell and sealed off with a Viton O-ring In some filtrations, a sealing flat plate was used to reduce the active membrane surface to equal the illuminated part Before each filtration, the membranes were immersed in isopropanol for at least one day Filtrations were carried out with dilute ethanol and isopropanol based methyl orange (MO, 327 Da, 35 μM) and rose bengal solutions (RB, 1017 Da, 17 μM) at bar with and without laser irradiation The chemical structures of the dyes are given in Figure A continuous green argon laser beam (514 nm) was used to illuminate the membrane The laser intensity was measured as the laser power divided by the illuminated surface, also calculating the minor loss of intensity in the laser pathway The laser was set at an intensity of 0.2 W/cm2 Permeances were calculated as the amount of solvent (V) that passed through the membrane per unit of time (t), membrane surface (A), and applied pressure (ΔP) so that Permeance ¼ V t 1 A1 ΔP1 ð1Þ 3ị IIFR ẳ 100 RL RC ị RC 1 ð4Þ where PC and RC are the conventual permeance and rejection (measured without laser irradiation) and PL and RL are the permeance and rejection measured when the membrane is irradiated ’ RESULTS AND DISCUSSION Since the size, distribution, aggregation, and dielectric environment all have a strong influence on the surface plasmon resonance behavior of the GNPs,29,3440 the GNPs inside the PI membranes were thoroughly characterized In the ISRmembranes, the GNPs are formed inside the solid membrane matrix by chemical reduction of a gold salt, wherein the membrane polymer itself acts as a stabilizer In the PRE-membranes, PVP-stabilized GNPs are present in the polymer solution before the membrane is cast and solidified by phase inversion The preformed GNPs may have an influence on the membrane structure, as it has been previously shown that adding (nano)particles to a polymer solution can cause significant changes in the resulting phase inversion membrane structure.4145 However, the addition of salt to a membrane casting solution may also influence the membrane morphology For example, Park et al have shown that polyetherimide (PEI) membranes containing ZnCl2 have thicker and denser top layers.46 It has been shown for lithium salts in poly(vinylidene fluoride) (PVDF) that the addition of the salts increases the viscosity of the casting solution and affects the phase inversion process.4749 Similar effects may be found for the addition of HAuCl4 3H2O, where the salt will later be reduced to GNPs Influence of Gold Content and Synthesis Method on the Polyimide Membrane Morphology The cross sections of where V is the collected permeate volume in a time t, A is the active membrane surface area, and ΔP is the applied pressure Rejections were calculated as the percentage of the feed concentration that was retained: Rejection ẳ 100ẵ1 Cp Cf 1 ị IIFP ¼ 100 ðPL PC Þ PC 1 the upper part of the reference membranes PRE-0 and ISR-0 are given in Figure Both membranes have an asymmetric structure and show a densification of the matrix toward the upper part of the cross section, which is typical for an asymmetric membrane prepared by phase inversion Larger pores are visible in the substructure of PRE-0, probably due to the presence of PVP in the membrane casting solution PVP increases the viscosity of a polymer solution, and it can generally be used as a pore former.5055 Since the PVP-protected GNPs are synthesized in a DMA solution containing an excess amount of PVP to ensure the NP stability, ð2Þ where Cp is the permeate concentration and Cf is the feed concentration of the dye All permeances and rejections shown are averages of three measurements with a standard deviation below 10% When necessary, measurements were repeated more than three times, to obtain a standard deviation below 10% 117 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE Figure SEM pictures of ISR-0 and PRE-0 cross sections, magnified at 20000 Figure SEM pictures magnified at 20000 of the cross sections of membranes ISR-1, ISR-2, ISR-3, and ISR-4 it can be expected that a similar porous structure will be found in the other PRE-membranes (see further below) SEM Pictures for ISR-Membranes The cross sections of ISR-1 to ISR-4 are given in Figure The membranes containing increasing weight percent of GNPs have rather similar structures as the reference membrane, although the roughness of the cross section increases Some effects of salt addition to the casting solution on the membrane morphology have been reported in literature for PEI and PVDF membranes.46,49 For these ISR membranes, there seems to have been no large influence of the addition of the chloroauric acid to the polymer solution on the membrane morphology However, the resolution of SEM is not high enough to fully characterize the structure SEM Pictures for PRE-Membranes The PRE-membranes (Figure 5), cast from a solution containing PVP-protected GNPs, have a structure that is clearly different from the ISR-membranes The pictures of PRE-1 and PRE-2 show a porous substructure similar to the reference membrane PRE-0 For PRE-3 and PRE-4, the pores reach almost to the very top of the membrane Since the GNP content of PRE-3 and PRE-4 is higher, the excess amount of PVP will be higher as well, which can explain these more porous structures PVP is known to increase the membrane porosity, as it may leach from the membrane during its immersion in water, the final step in the phase inversion synthesis process The cross sections are a lot smoother than those obtained for the ISR membranes Since the resolution of SEM is not high enough, TEM pictures were made of the top layer and substructure of the cross sections to gain information on the size and dispersion of the GNPs in the membranes Influence of the Synthesis Method on the GNP Properties An important parameter of GNPs for purposes such as sensing and photothermal heating is the surface plasmon resonance wavelength A surface plasmon is a collective movement of the outer band electrons circling a GNP This electron gas moves at a certain wavelength, and when light of this same wavelength is aimed at the nanoparticle, it is strongly absorbed and turned into thermal energy The wavelength at which surface plasmon resonance occurs is strongly dependent on the size and shape of 118 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE Figure SEM pictures magnified at 20000 of the cross sections of membranes PRE-1, PRE-2, PRE-3, and PRE-4 This indicated that, regardless the gold concentration, the size and dispersion of GNPs in the membrane top layer were similar The wavelength found by UVvis spectroscopy increased from to wt % gold and stabilized further A higher SPR wavelength may indicate a larger GNP size Alternatively, since the GNPs were formed in a solid membrane matrix, the rise in gold concentration may have resulted in a stronger aggregation of the GNPs For the PRE membranes, both the DRS and the UVvis wavelength are clearly increasing for increasing gold concentration This indicates that, both in the top and sublayer, larger GNPs may have been formed at higher gold concentrations It may also indicate that the GNPs have been insufficiently stabilized at the higher concentrations in the DMA solution during the membrane synthesis This would lead to an aggregation of GNPs already in the membrane casting solution Since the DRS and UVvis data are purely indicative and provide no real data on the size and dispersion of the GNPs in the PI membranes, the membrane cross sections were also investigated by TEM Transmission Electron Microscopy The TEM pictures of the cross sections of the skin layers and the porous substructures of the membranes are given in Figures 69 In Figures and 8, the top of the membrane is shown, with the skin layer slowly blending into the substructure toward the bottom of the photo For both methods, the mean particle size is around 35 nm, depending on the gold content of the membrane There is one clear difference between the IRS and PRE membranes, namely, in the aggregation of the GNPs In the ISR membranes, hardly any aggregation of GNPs is visible neither in the top layer nor in the substructure, at any concentration of gold In the PRE membranes, clustering of GNPs occurs both in the skin layer and the substructure The aggregation is moderate at the lowest GNP Table Maximum Absorption Wavelengths Obtained in DRS and UVVis Spectroscopy for GNP Containing PI Membranes Prepared by PRE and ISR Methods membrane DRS wavelength [nm] UVvis wavelength [nm] ISR-1 556 556 ISR-2 556 556 ISR-3 555 555 ISR-4 562 562 PRE-1 533 533 PRE-2 545 545 PRE-3 552 552 PRE-4 558 558 the GNPs and on the dielectric environment.29,3537,56,57 For GNPs, the resonance wavelength will generally be at 520 nm or higher The two preparation methods have a different influence on the GNP size and dispersion in the membrane and will thus affect the SPR behavior differently Spectroscopy Measurements To estimate the dispersion and aggregation of the GNPs in the membrane, DRS and UVvis spectra were obtained Since DRS is a surface characterization technique, these measurements will give information solely on the GNPs found in the top layer of the membrane, near the surface To obtain information on the GNPs found in the entire membrane, a piece of each membrane was redissolved in DMA and analyzed by UVvis spectroscopy The wavelength where the maximal absorbance is found is given in Table For the ISR membranes, the SPR wavelength found by DRS was stable for 13 wt % gold and increased slightly for wt % gold 119 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE Figure TEM pictures and particle size distributions of the GNPs in the skin layer of ISR membranes containing 14 wt % GNPs Figure TEM pictures and particle size distributions of the GNPs in the porous substructure of ISR membranes containing 14 wt % GNPs concentration but aggregates at the higher concentrations In membranes PRE-3 and PRE-4, the GNP clusters are dominant, and there are hardly any well-dispersed particles visible These results are in accordance with literature, also indicating that the in situ synthesis methods often lead to a better dispersion and less aggregation of the GNPs compared to the use of presynthesized GNPs.4,6 For the ISR membranes, the amount of GNPs in the top layer was higher than in the substructure This is probably due to size restrictions in the denser top layer, where the GNPs would remain smaller and did not have the chance to grow closely together In the more porous substructure, the GNPs have room to grow larger Since gold nanoparticles are visibly present in the entire cross section of the membrane, it may be assumed that the NaBH4 reducing agent was able to penetrate into the entire bulk of the membrane These TEM data provide an explanation for the spectroscopic data mentioned above In the skin layer of ISR membranes, the mean particle diameter is nm for ISR-1 to ISR-3, rising to nm in ISR-4 The DRS data, giving information on the membrane surface and thus mostly on the skin layer, clearly reflect this; the SPR wavelengths remains stable for ISR-1 to ISR-3, slightly rising for ISR-4 In the substructure of ISR membranes, the nm particles are still present, but many larger particles are also visible Since the UVvis data were taken for redissolved membranes, these larger particles are also taken into account The amount of larger particles rises at higher gold concentration, and this is reflected in the rise of the SPR wavelength for the higher gold concentrations The systematically higher wavelengths observed in DRS compared to the UVvis data may be due to the difference in environment: the solid PI versus the DMA solution The UVvis data seem to better reflect the size range of the GNPs, since 35 nm GNPs in solution have been indicated to have wavelengths around 530 nm.18,58 SPR wavelengths obtained for membranes containing increasing gold concentrations are higher, especially for PRE-3 and PRE-4 This is caused by the increasing aggregation of the GNPs that is abundantly clear on the TEM pictures The TEM pictures also indicate that the lower DRS wavelengths obtained for PRE compared to ISR membranes may not be interpreted as an indication of smaller GNPs, since the mean particle size is nm in both cases However, this difference in wavelength more probably reflects the difference in immediate environment of the GNPs, that are protected by PVP in the PRE membranes and by PI in the ISR membranes Overall, the TEM pictures prove that higher gold contents in the membranes lead to broader particle size distributions but that the mean particle size remains constant up to wt % gold, regardless the incorporation method It also shows that the presynthesized GNPs are more prone to aggregation, as was expected from literature.4,6 During the PRE membrane synthesis, there are many steps in which this aggregation may occur, for example, while adding the polymer to the GNP solution, or during the casting and solidification of the membrane These TEM images indicate that, even though PVP blends well with PI, it did not improve the dispersion of GNPs in the PI membranes It is possible that, while the PI was added to the GNP solution, the increasing viscosity resulted in an entanglement of the GNPs between the 120 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE (520 nm) visible in the top 500 nm of the membrane PRE-1 and larger pores (50100 nm) in PRE-2 to PRE-4 In the ISR membranes, a denser top layer is seen, which may partially be a result of the higher viscosity in the casting solution, induced by the addition of the gold salt A higher viscosity in the casting solution will generally lead to a denser membrane top layer due to a delayed demixing in the phase inversion synthesis process.46 Influence of Gold on Membrane Filtration Performance Due to the changes in membrane morphology, the gold content should also have an influence on the membrane performance, even in absence of laser irradiation This was studied by carrying out IPA and ethanol filtrations with dyes rose bengal (1017 Da) and methyl orange (324 Da) The permeance and rejection for the ISR membranes and the PRE membranes are given in Figure 10 For the ISR membranes, an overall slight increase in membrane permeance was found for higher gold contents In IPA, the rejection of both dyes was higher than 95%, and the rejection did not depend on the gold content of the membrane In ethanol, however, the permeances were higher than in IPA and the rejection lowered somewhat For the PRE membranes, the permeance depends strongly on the gold content in the membrane, showing an overall decrease at increasing gold content This seems to contradict the increasing porosity clearly seen on the TEM pictures in the top layer An explanation may be that the very thin (∼nm) skin layer of these membranes is still very dense, thus resulting in such a low permeance It is commonly supposed that this skin layer has the largest influence on the membrane separation performance However, it is expected to be only a couple of nanometers thick and cannot be differentiated on the SEM or TEM pictures Similar to the ISR membranes, there was no strong influence on the rejection in the case of the isopropanol filtrations for the PRE membranes At the lower gold content, the permeance was higher for PRE membranes than for ISR membranes, which is in accordance with the TEM pictures showing a higher porosity in the skin layer for the PRE membranes At the higher gold contents, ISR-3 and ISR-4 had higher permeances compared to PRE-3 and PRE-4, which again seems to contradict the very high porosity seen on TEM pictures for the latter For both methods, it is clear that the incorporation of GNPs and the method used to so has a strong influence on the membrane structure and performance The method of incorporation also has a clear effect on the GNP size and dispersion in the membrane matrix and on their SPR wavelength Effect of Light-Induced Local Photothermal Heating of Membrane on Filtration Behavior The effect of plasmonic heating of the GNPs in the membranes on the membrane performance was finally tested as a possible application for these membranes Dead-end filtrations of methyl orange in ethanol were repeated for the PRE and ISR membranes under laser irradiation The laser irradiation of the GNPs induces plasmonic heating inside the membrane matrix As our previous studies has indicated, this local heating of the membrane can have a positive effect on the membrane permeance without affecting the membrane selectivity.26,27 The performance under laser irradiation was compared to the original performance of the membranes in Figure 11 For both the ISR and the PRE membranes, the IRR in permeance induced by plasmonic heating increased at higher gold contents The absolute differences in permeance are similar for Figure TEM pictures and particle size distributions of the GNPs in the skin layers of PRE membranes containing 14 wt % GNPs Figure TEM pictures of the porous substructure of PRE membranes containing 14 wt % GNPs No accurate size distributions of the GNPs could be measured due to the strong aggregation PI chains, preventing a good dispersion of the GNPs in the casting solution The effect of PVP as a pore-former on the membrane structure was also visualized on the TEM pictures There are small pores 121 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE Figure 10 Isopropanol and ethanol permeance and rejection of dyes rose bengal and methyl orange for membranes prepared by ISR (A) and PRE (B) Figure 12 Temperature increase upon laser irradiation for a PI reference membrane and GNP containing ISR and PRE PI membranes wetted by ethanol (ambient temperature 20 °C) Figure 11 Irradiation improvement factors for permeance and rejection of ethanol + methyl orange mixtures obtained by laser irradiation for PRE and ISR membranes followed by the increasing percentual difference in permeance However, for both methods, the temperature stabilizes at wt % of gold, which is not reflected in the filtration results Higher temperatures are obtained for the ISR membranes compared to the PRE membranes, which is probably due to the problems with aggregation in the PRE membranes, diminishing the photothermal effect of the GNPs However, this difference in temperature is not reflected in the filtration data It should be kept in mind that the heating experiments were carried out in a static system, while during the filtrations there is heat dissipation to a flowing solvent stream involved, leading to a more complicated mass and heat transfer process During filtrations, the heat produced by the both methods The rejection is in neither case affected by the laser irradiation, and the differences fall within the expected experimental error This also indicates that there was no unwanted influence of the laser heating on the membrane material, such as melting In previous works, it was already shown that no defects were induced by heating the GNP containing membranes at low laser intensities, since the membrane performance returned to the original state after turning off the laser.26,27 When these data are compared to the measured temperature increase in the ethanol-wetted membrane under laser irradiation (Figure 12), it is clear that the rising temperature trend is 122 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE Figure 13 Combined data taken from this study ()), reference 26 () and reference 60 (() comparing the conventional and laser-irradiated permeance and rejection for different GNP containing membranes in filtrations of IPA and ethanol dye solutions GNPs inside the membrane is dissipated in the medium, including the permeating solvent It was shown previously that the permeating solvent may have a cooling effect, the extent of which depends on the intrinsic permeability of the membrane.27 Since the ISR membranes at the higher gold contents have a higher intrinsic ethanol flux than the PRE membranes (see Figure 10), the solvent cooling effect will be stronger If the solvent cooling effect is large enough, it may result in a lower IIF (Figure 11) even though these membranes reached higher temperatures under static conditions To fully comprehend the mechanism involving the flux increase by plasmonic heating, more data should still be collected The continuous green argon laser beam used in these experiments emits light at wavelength of 514 nm, which is lower than the actual surface plasmon wavelength of the GNPs (see Table 1) but close enough to expect a heating effect Also, the illuminated membrane surface was only 40% of the active membrane surface Due to both these parameters, the experiments were carried out at a suboptimal level, and even stronger increases in permeance can be expected when the laser is at the exact SPR wavelength and when the membrane is illuminated entirely Also, some losses in laser intensity are expected when the laser beam travels through the dye feeds, for example, due to reflection by impurities In upscaled filtration units, the light should be transferred to the membrane more efficiently, for example, by use of optical fibers incorporated into the membrane support In Figure 13, the new data are combined with the previously obtained data.26,27 The added dashed line indicates the 1:1 data, where the irradiated permeance and rejection are equal to the nonirradiated results It is clear that, while the rejection data fluctuate around this 1:1 line, the permeance data are consistently above this line This confirms that overall rejections are not significantly influenced by the irradiation while permeances are always increased To increase fluxes of a given membrane without lowering its selectivity is a highly desired but rarely found effect in membrane technology.27 ’ CONCLUSIONS Two methods to prepare GNP containing polymeric solids were compared, namely, the incorporation of preformed PVPprotected GNPs into a PI membrane and the in situ synthesis of GNPs inside a PI membrane matrix In both cases, GNPs are obtained with an average size of nm in the top layer of the membrane However, there is a clear difference in the membrane behavior and the GNP distribution When preformed GNPs are used, the excess of PVP in the casting solution induces a higher porosity in the membrane, and the GNPs are more prone to aggregation It is possible that PVP is not the optimal GNP stabilizer during the specific PI membrane synthesis procedure reported here When the GNPs are synthesized in situ, the GNPs are dispersed very well, with smaller nanoparticles formed in the dense top layer of the membrane and larger nanoparticles in the porous sub layer, where more space is available The better dispersion also resulted in a stronger heating of the composite material upon laser irradiation The permeance of GNP containing PI membranes in SRNF could thus be increased by plasmonic heating of the GNPs in the membrane by means of a green argon ion laser Higher IIFs were found for higher gold contents, regardless the synthesis method The aggregation of the preformed PVP-protected GNPs in the membrane unexpectedly did not have a large influence on the photothermal filtration behavior of the membranes These data further confirm that localized photothermal heating of a membrane during a filtration process can significantly enhance the separation, by inducing an increased permeance without lowering rejections, a most remarkable combination The GNP containing PI membranes may also be used for other applications, such as combined catalysis and membrane separation processes ’ AUTHOR INFORMATION Corresponding Author *E-mail: ivo.vankelecom@biw.kuleuven.be; fax: 32 1632 1998; phone: 32 1632 1549 ’ ACKNOWLEDGMENT K.V acknowledges the Fund of Scientific Research Flanders (FWO-Vlaanderen) for financial support as a research assistant This research was done in the framework of an I.A.P.-PAI grant (IAP 6/27) sponsored by the Belgian Federal Government, of a GOA grant from K.U Leuven and of long-term structural fundingMethusalem funding by the Flemish Government Professor J Billen of the Laboratory for Entomology of K.U Leuven, Leuven, Belgium, is kindly acknowledged for assisting with TEM measurements ’ REFERENCES (1) Porel, S.; Venkatram, N.; Rao, D N.; Radhakrishnan, T P In situ synthesis of metal nanoparticles in polymer matrix and their optical limiting applications J Nanosci Nanotechnol 2007, (6), 1887–1892 123 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE incorporating redox mediator Electrochem Commun 2006, (10), 1665–1670 (20) Pontie, M.; Cowache, P.; Klein, L H.; Maurice, V.; Bedioui, F Preparation and characterization of an electronically conductive and chemically modified ultrafiltration type membrane J Membr Sci 2001, 184 (2), 165–173 (21) Huang, S S.; Yin, Y F.; Wang, K M.; He, X X.; Zhong, T S A new biochemical method for protein separation based on gold nanotubule membrane Chem J Chin Univ.-Chin 2004, 25 (12), 2238–2241 (22) Lee, K Y.; Kim, D W.; Heo, J.; Kim, J S.; Yang, J K.; Cheong, G W.; Han, S W Novel colorimetric sensing of anion with gold nanoparticles-embedded plasticized polymer membrane Bull Korean Chem Soc 2006, 27 (12), 2081–2083 (23) Jiang, C Y.; Markutsya, S.; Pikus, Y.; Tsukruk, V V Freely suspended nanocomposite membranes as highly sensitive sensors Nat Mater 2004, (10), 721–728 (24) Fibbioli, M.; Bandyopadhyay, K.; Liu, S G.; Echegoyen, L.; Enger, O.; Diederich, F.; Gingery, D.; Buhlmann, P.; Persson, H.; Suter, U W.; Pretsch, E Redox-active self-assembled monolayers for solidcontact polymeric membrane ion-selective electrodes Chem Mater 2002, 14 (4), 1721–1729 (25) Vandezande, P.; Gevers, L E M.; Vankelecom, I F J Solvent resistant nanofiltration: separating on a molecular level Chem Soc Rev 2008, 37 (2), 365–405 (26) Vanherck, K.; Verbiest, T.; Vankelecom, I Improving fluxes of polyimide membranes containing gold nanoparticles by photothermal heating J Membr Sci 2011, 373 (1-2), 5–13 (27) Vanherck, K.; Hermans, S.; Verbiest, T.; Vankelecom, I Using the photothermal effect to improve membrane separations via localised heating J Mater Chem 2011, 21, 6079–6087 (28) Patra, C R.; Bhattacharya, R.; Mukhopadhyay, D.; Mukherjee, P Application of gold nanoparticles for targeted therapy in cancer J Biomed Nanotechnol 2008, (2), 99–132 (29) Jain, P K.; Huang, X H.; El-Sayed, I H.; El-Sayed, M A Noble metals on the nanoscale: optical and photothermal properties and some applications in imaging, sensing, biology, and medicine Acc Chem Res 2008, 41 (12), 1578–1586 (30) Sperling, R A.; Rivera gil, P.; Zhang, F.; Zanella, M.; Parak, W J Biological applications of gold nanoparticles Chem Soc Rev 2008, 37 (9), 1896–1908 (31) Boisselier, E.; Astruc, D Gold nanoparticles in nanomedicine: preparations, imaging, diagnostics, therapies and toxicity Chem Soc Rev 2009, 38 (6), 1759–1782 (32) Cobley, C M.; Xia, Y N Gold and nanotechnology Elements 2009, (5), 309–313 (33) Khlebtsov, N G.; Dykman, L A Optical properties and biomedical applications of plasmonic nanoparticles J Quant Spectrosc Radiat Transfer 2010, 111 (1), 1–35 (34) Ghosh, S K.; Nath, S.; Kundu, S.; Esumi, K.; Pal, T Solvent and ligand effects on the localized surface plasmon resonance (LSPR) of gold colloids J Phys Chem B 2004, 108 (37), 13963–13971 (35) Lee, K S.; El-Sayed, M A Gold and silver nanoparticles in sensing and imaging: Sensitivity of plasmon response to size, shape, and metal composition J Phys Chem B 2006, 110 (39), 19220–19225 (36) Miller, M M.; Lazarides, A A Sensitivity of metal nanoparticle surface plasmon resonance to the dielectric environment J Phys Chem B 2005, 109 (46), 21556–21565 (37) Noguez, C Surface plasmons on metal nanoparticles: The influence of shape and physical environment J Phys Chem C 2007, 111 (10), 3806–3819 (38) Rooney, P.; Rezaee, A.; Xu, S.; Manifar, T.; Hassanzadeh, A.; Podoprygorina, G.; Bohmer, V.; Rangan, C.; Mittler, S Control of surface plasmon resonances in dielectrically coated proximate gold nanoparticles immobilized on a substrate Phys Rev B 2008, 77 (23), 235446–235454 (39) Toderas, F.; Baia, M.; Farcau, V.; Astilean, S.; Ulinici, S Tuning of gold nanoparticles plasmon resonances by experiment and simulation J Optoelectron Adv Mater 2008, 10 (12), 3265–3269 (2) Zhang, Q.; Xu, J J.; Liu, Y.; Chen, H Y In-situ synthesis of poly(dimethylsiloxane)-gold nanoparticles composite films and its application in microfluidic systems Lab Chip 2008, (2), 352–357 (3) Lan, Y.; Mao, B D.; Wang, E B.; Song, Y H.; Kang, Z H.; Wang, C L.; Tian, C G.; Zhang, C.; Xu, L.; Li, Z In-situ fabrication of hybrid polyoxometalate nanoparticles composite films Thin Solid Films 2007, 515 (78), 3397–3401 (4) Caseri, W R Nanocomposites of polymers and inorganic particles: preparation, structure and properties Mater Sci Technol 2006, 22 (7), 807–817 (5) Lu, J X.; Moon, K S.; Wong, C P Development of novel silver nanoparticles/polymer composites as high K polymer matrix by in-situ photochemical method, Proceedings of the 56th Electronic Components & Technology Conference; 2006; Vol and 2, pp 18411846 (6) Perez-Juste, J.; Pastoriza-Santos, I.; Liz-Marzan, L M.; Mulvaney, P Gold nanorods: Synthesis, characterization and applications Coord Chem Rev 2005, 249 (1718), 1870–1901 (7) Wilson, J L.; Poddar, P.; Frey, N A.; Srikanth, H.; Mohomed, K.; Harmon, J P.; Kotha, S.; Wachsmuth, J Synthesis and magnetic properties of polymer nanocomposites with embedded iron nanoparticles J Appl Phys 2004, 95 (3), 1439–1443 (8) Mertens, P G N.; Bulut, M.; Gevers, L E M.; Vankelecom, I F J.; Jacobs, P A.; De Vos, D E Catalytic oxidation of 1,2-diols to alpha-hydroxy-carboxylates with stabilized gold nanocolloids combined with a membrane-based catalyst separation Catal Lett 2005, 102 (12), 57–61 (9) Wang, S H.; Wang, C.; Zhang, B.; Sun, Z Y.; Li, Z Y.; Jiang, X K.; Bai, X D Preparation of Fe3O4/PVA nanofibers via combining insitu composite with electrospinning Mater Lett 2010, 64 (1), 9–11 (10) Zhang, Z P.; Zhang, L D.; Wang, S X.; Chen, W.; Lei, Y A convenient route to polyacrylonitrile/silver nanoparticle composite by simultaneous polymerization-reduction approach Polymer 2001, 42 (19), 8315–8318 (11) Ramesh, G V.; Porel, S.; Radhakrishnan, T P Polymer thin films embedded with in situ grown metal nanoparticles Chem Soc Rev 2009, 38 (9), 2646–2656 (12) D’Britto, V.; Sandeep, C S S.; Philip, R.; Prasad, B L V Optical limiting properties of hydrophobic poly(etherimide) membranes embedded with isolated and aggregated gold nanostructures Colloids Surf., A 2009, 352 (13), 79–83 (13) Dammer, O.; Vlckova, B.; Prochazka, M.; Bondarev, D.; Vohlidal, J.; Pfleger, J Effect of preparation procedure on the structure, morphology, and optical properties of nanocomposites of poly[2methoxy-5-(2-ethylhexyloxy)-1,4-phenylenevinylene] with gold nanoparticles Mater Chem Phys 2009, 115 (1), 352–360 (14) Kang, S W.; Hong, J.; Park, J H.; Mun, S H.; Kim, J H.; Cho, J.; Char, K.; Kang, Y S Nanocomposite membranes containing positively polarized gold nanoparticles for facilitated olefin transport J Membr Sci 2008, 321 (1), 90–93 (15) Kuo, S W.; Wu, Y C.; Lu, C H.; Chang, F C Surface modification of gold nanoparticles with polyhedral oligomeric silsesquioxane and incorporation within polymer matrices J Polym Sci., Part B: Polym Phys 2009, 47 (8), 811–819 (16) Chang, S.; Singamaneni, S.; Kharlampieva, E.; Young, S L.; Tsukruk, V V Responsive hybrid nanotubes composed of block copolymer and gold nanoparticles Macromolecules 2009, 42 (15), 5781– 5785 (17) Mertens, P G N.; Vandezande, P.; Ye, X.; Poelman, H.; De Vos, D E.; Vankelecom, I F J Membrane-occluded gold-palladium nanoclusters as heterogeneous catalysts for the selective oxidation of alcohols to carbonyl compounds Adv Synth Catal 2008, 350 (9), 1241–1247 (18) Huang, Y J.; Li, D.; He, P.; Sun, C Y.; Wang, M J.; Li, J H Semipermeable membrane embodying noble metal nanoparticles and its electrochemical behaviors J Electroanal Chem 2005, 579 (2), 277–282 (19) Crespilho, F N.; Ghica, M E.; Florescu, M.; Nart, F C.; Oliveira, O N.; Brett, C M A A strategy for enzyme immobilization on layer-by-layer dendrimer-gold nanoparticle electrocatalytic membrane 124 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 The Journal of Physical Chemistry C ARTICLE (59) Rasband, W S ImageJ; U.S National Institutes of Health: Bethesda, Maryland, 19972009; http://rsb.info.nih.gov/ij/ (40) Link, S.; El-Sayed, M A Shape and size dependence of radiative, non-radiative and photothermal properties of gold nanocrystals Int Rev Phys Chem 2000, 19 (3), 409–453 (41) Chen, W J.; Su, Y L.; Zhang, L.; Shi, Q.; Peng, J M.; Jiang, Z Y In situ generated silica nanoparticles as pore-forming agent for enhanced permeability of cellulose acetate membranes J Membr Sci 2010, 348 (12), 75–83 (42) Maximous, N.; Nakhla, G.; Wong, K.; Wan, W Optimization of Al2O3/PES membranes for wastewater filtration Sep Purif Technol 2010, 73 (2), 294–301 (43) Soroko, I.; Livingston, A Impact of TiO2 nanoparticles on morphology and performance of crosslinked polyimide organic solvent nanofiltration (OSN) membranes J Membr Sci 2009, 343 (12), 189–198 (44) Yang, Y N.; Zhang, H X.; Wang, P.; Zheng, Q Z.; Li, J The influence of nano-sized TiO2 fillers on the morphologies and properties of PSFUF membrane J Membr Sci 2007, 288 (12), 231–238 (45) Aerts, P.; Kuypers, S.; Genne, I.; Leysen, R.; Mewis, J.; Vankelecom, I F J.; Jacobs, P A Polysulfone-ZrO2 surface interactions The influence on formation, morphology and properties of Zirfonmembranes J Phys Chem B 2006, 110 (14), 7425–7430 (46) Park, J S.; Kim, S K.; Lee, K H Effect of ZnCl2 on formation of asymmetric PEI membrane by phase inversion process J Ind Eng Chem 2000, (2), 93–99 (47) Lin, D J.; Chang, C L.; Huang, F M.; Cheng, L P Effect of salt additive on the formation of microporous poly(vinylidene fluoride) membranes by phase inversion from LiClO4/water/DMF/PVDF system Polymer 2003, 44 (2), 413–422 (48) Yeow, M L.; Liu, Y T.; Li, K Preparation of porous PVDF hollow fibre membrane via a phase inversion method using lithium perchlorate (LiClO4) as an additive J Membr Sci 2005, 258 (12), 16–22 (49) Kurdi, J.; Tremblay, A Y Preparation of defect-free asymmetric membranes for gas separations J Appl Polym Sci 1999, 73 (8), 1471–1482 (50) Chakrabarty, B.; Ghoshal, A K.; Purkait, A K Preparation, characterization and performance studies of polysulfone membranes using PVP as an additive J Membr Sci 2008, 315 (12), 36–47 (51) Kim, Y K.; Park, H B.; Lee, Y M Gas separation properties of carbon molecular sieve membranes derived from polyimide/polyvinylpyrrolidone blends: effect of the molecular weight of polyvinylpyrrolidone J Membr Sci 2005, 251 (12), 159–167 (52) Mosqueda-Jimenez, D B.; Narbaitz, R M.; Matsuura, T Effects of preparation conditions on the surface modification and performance of polyethersulfone ultrafiltration membranes J Appl Polym Sci 2006, 99 (6), 2978–2988 (53) See-Toh, Y H.; Ferreira, F C.; Livingston, A G The influence of membrane formation parameters on the functional performance of organic solvent nanofiltration membranes J Membr Sci 2007, 299 (12), 236–250 (54) Yoo, S H.; Kim, J H.; Jho, J Y.; Won, J.; Kang, Y S Influence of the addition of PVP on the morphology of asymmetric polyimide phase inversion membranes: effect of PVP molecular weight J Membr Sci 2004, 236 (1), 203–207 (55) Ismail, A F.; Hassan, A R Effect of additive contents on the performances and structural properties of asymmetric polyethersulfone (PES) nanofiltration membranes Sep Purif Technol 2007, 55 (1), 98–109 (56) Eustis, S.; El-Sayed, M A Why gold nanoparticles are more precious than pretty gold: Noble metal surface plasmon resonance and its enhancement of the radiative and nonradiative properties of nanocrystals of different shapes Chem Soc Rev 2006, 35 (3), 209–217 (57) Daniel, M C.; Astruc, D Gold nanoparticles: Assembly, supramolecular chemistry, quantum-size-related properties, and applications toward biology, catalysis, and nanotechnology Chem Rev 2004, 104 (1), 293–346 (58) Teranishi, T.; Kiyokawa, I.; Miyake, M Synthesis of monodisperse gold nanoparticles using linear polymers as protective agents Adv Mater 1998, 10 (8), 596–599 125 dx.doi.org/10.1021/jp207244y |J Phys Chem C 2012, 116, 115–125 ... substructures of the membranes are given in Figures 69 In Figures and 8, the top of the membrane is shown, with the skin layer slowly blending into the substructure toward the bottom of the photo For... situ synthesis methods often lead to a better dispersion and less aggregation of the GNPs compared to the use of presynthesized GNPs.4,6 For the ISR membranes, the amount of GNPs in the top layer... incorporation of preformed PVPprotected GNPs into a PI membrane and the in situ synthesis of GNPs inside a PI membrane matrix In both cases, GNPs are obtained with an average size of nm in the top layer of