RSC Advances View Article Online Published on 14 November 2013 Downloaded by Shantou University on 14/05/2014 08:13:18 PAPER Cite this: RSC Adv., 2014, 4, 6383 View Journal | View Issue Controlled synthesis and characterization of iron oxide nanostructures with potential applications for gas sensors and the environment† Nguyen Viet Long,*abcdef Yong Yang,*a Masayoshi Yuasa,e Cao Minh Thi,f Yanqin Cao,a Thomas Nanng and Masayuki Nogamiah In the present research, large iron oxide microparticles with large sizes in the range of 1–5 mm have been facilely synthesized by a modified polyol method with NaBH4 as a versatile strong reducing agent We found that the highly homogeneous iron oxide microparticles' novel structure is the best pure crystal phase of a-Fe2O3 in terms of polyhedral morphology and shape in existence There are no diffraction peaks of Received 18th October 2013 Accepted 14th November 2013 other crystal phases from impurities in a-Fe2O3 microparticle products in the crystal growth Interestingly, a new method of heat treatment or atomic surface deformation allowed for the discovery of a new large a-Fe2O3 structure with controlled specific a-Fe2O3 oxide grains in the crystal structure The severe surface DOI: 10.1039/c3ra45925j deformation of sharp, polyhedral, large a-Fe2O3 microparticles under a sintering treatment was found to www.rsc.org/advances give un-sharp, polyhedral large a-Fe2O3 microparticles with specific grains and boundaries Introduction Typically, magnetic nanoparticles (MNs) such as nickel (Ni) and cobalt (Co) are used in catalysis, biology and medicine Iron (Fe) based nanoparticles, and magnetic Fe based nanostructures offer increasingly excellent performance in the aforementioned applications due to their great magnetic properties,1–4 such as their previously undiscovered ferromagnetic, antiferromagnetic, and ferrimagnetic magnetism So far, the crystal a State Key Laboratory of High Performance Ceramics and Superne Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Science, 1295, Dingxi Road, Shanghai 200050, China E-mail: nguyenviet_long@yahoo.com; Fax: +86-2152414219; Tel: +86-21-52414321 b Posts and Telecommunications Institute of Technology, km 10 Nguyen Trai, Hanoi, Vietnam Tel: +84 (0)946293304 c Laboratory for Nanotechnology, Ho Chi Minh Vietnam National University, LinhTrung, Thu Duc, Ho Chi Minh, Vietnam d Department of Molecular and Material Sciences, Interdisciplinary Graduate School of Engineering Sciences, Kyushu University, 6-1 Kasugakouen, Kasuga, Fukuoka, 8618580, Japan e Department of Materials Science, Faculty of Engineering Sciences, Kyushu University, Kasuga-koen 6-1, Kasuga-shi, Fukuoka, 816-8580, Japan f Ho Chi Minh City University of Technology, 144/24 Dien Bien Phu, Ward 25, BinhThach, Ho Chi Minh City, Vietnam g Ian Wark Research Institute, ARC Special Research Centre, University of South Australia, Australia h Department of Materials Science and Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya 466-8555, Japan Tel: +81 (0)90-9930-9504 † Electronic supplementary information (ESI) available: SEM images of the very large a-Fe2O3 microparticles produced with a modied polyol method with NaBH4 at 200–300 C for 30 SEM images of the very large a-Fe2O3 microparticles with surface deformations and the grains under the same conditions and microparticle heat treatment See DOI: 10.1039/c3ra45925j This journal is © The Royal Society of Chemistry 2014 nanostructures of various Fe oxides and magnetic Fe oxide nanoparticles have the same specic crystal nanostructures as magnetite (Fe3O4) and maghemite nanoparticles (g-Fe2O3) and hematite (a-Fe2O3).5–10 Recently, scientists and researchers have discovered important practical applications of a-Fe2O3 nanoparticles and nano-structures in lithium ion batteries, energy storage and materials for various gas sensors In recent work, the addition of metal nanoparticles has led to better sensitivity and better selectivity in various oxide sensor devices.11–15,46 In addition, a reduced graphene oxide platelet/Fe2O3 nanoparticle composite can be used in the anode for Li-ion batteries with high-performance as well as high durability and stability.16 In most cases, the characteristics such as size, shape, morphology, and particle composition of the Fe based nanoparticles need to be controlled with the addition of various metals: Ni, Co, Zn, Cu, etc For example, the special nanostructures of modied MFe2O4 ferrite nanoparticles (M ¼ Co, Ni, Zn), or magnetic multimetal oxide nanoparticles, can be potentially used in magnetic resonance imaging (MRI) technology During recent years, super-paramagnetic iron oxide nanoparticles (SPIONs), such as superparamagnetic magnetite Fe3O4 nanoparticles and maghemite g-Fe2O3 nanoparticles under size and morphology control, have been used in drug delivery vehicles.17–20 At present, magnetic iron metal and iron oxide nanoparticles also have important applications in experimental catalysts, high contrast agents for magnetic resonance imaging (MRI), and therapeutic agents for the treatments of dangerous tumors and cancers.17–24 Beside the interesting magnetic properties of iron alloy and iron oxide based nanostructures and nanomaterials, some of the most important characteristics are that iron alloy and iron oxide based nanostructures and nanomaterials have ultra-high RSC Adv., 2014, 4, 6383–6390 | 6383 View Article Online Published on 14 November 2013 Downloaded by Shantou University on 14/05/2014 08:13:18 RSC Advances durability and stability Magnetite Fe3O4 nanoparticles can be used for magnetic hyperthermia, high contrast agents and MRI technology, and targeted drug delivery vehicles.17–24 Due to their high biocompatibility and relatively low toxicity in animals and humans, maghemite g-Fe2O3 nanoparticles can also offer great applications in biomedicine So far, various synthesis and preparation methods of MNs have been utilized to control the size characteristics, the surface shape and morphology characteristics, and the internal characteristics (large and small crystal structures, large and small crystal surfaces, as well as low and high porosity etc.).21–24 In this research, we present a novel synthesis process to control the size, shape and morphology of large polyhedral Fe oxide microparticles with a-Fe2O3 structure in the range of 1– mm Herein, we have successfully used a modied polyol method with the addition of an extra amount of NaBH4 in ethylene glycol (EG) Experimental section 2.1 Chemical For the chemical synthesis processes to make the pure a-Fe2O3 oxide nanoparticles, we used chemicals from Aldrich, SigmaAldrich and Wako These include poly(vinylpyrrolidone) (PVP) (FW ¼ 55 000) as a good protective agent (Aldrich) and FeCl3$4H2O (Aldrich, no 451649 and 236489) In particular, sodium borohydride (NaBH4) was used as a strong reducing agent for the synthesis of a-Fe2O3 microparticles, ethylene glycol (EG) from Aldrich was used as both a solvent and a weak reducing agent, and ethanol, acetone, and hexane were procured from Aldrich or Japanese companies Here, all chemicals were of standard analytical grade and were used without any further purication Deionized and distilled water with high purity prepared by a Milli-Pore purication system available in our laboratory was used for the washing and cleaning of containers during experimental synthesis processes 2.2 Synthesis of a-Fe2O3 oxide microparticles Briey, mL of EG, 1.5 mL of 0.0625 M FeCl3, mL of 0.375 M PVP, and 0.028 g NaBH4 were used for making Sample in a typical process of the controlled synthesis of the large polyhedral a-Fe2O3 oxide microparticles The details and steps of the known process procedures were previously presented.19,25 In general, FeCl3 was completely reduced with the extra amount of NaBH4 in EG at 200–230 C for 30 As a result, black solutions containing polyhedral a-Fe2O3 oxide microparticles with large sizes, shapes and morphologies were obtained as the nal product They have a particle size of 1–5 mm with a polyhedral shape and morphology Similarly to Sample 1, we used the same processes for Sample and Sample for XRD and SEM measurements Sample was also used for XRD and SEM measurement and analysis Sample was heated at 500 C for h for SEM measurement and analysis Sample was heated at 900 C for h for SEM analysis All of the experimental conditions for making Samples 1–3 corresponding to the XRD results are presented in Table and section (Results and discussion) 6384 | RSC Adv., 2014, 4, 6383–6390 Paper 2.3 Material characterization 2.3.1 X-ray diffraction method In the XRD method for crystal analysis, we used the as-prepared products of the black solution containing the PVP-aFe2O3 oxide microparticles (Sample 1) The PVP-aFe2O3 oxide nanoparticles were washed many times in order to obtain clean a-Fe2O3 oxide nanoparticles by our standard procedures with the use of a centrifuge The black solution of Fe based microparticles was dried in order to leave an Fe based nano-powder on the glass substrate for XRD analysis The high heat treatment of our samples was carried out in a gas/air ow (20 mL minÀ1) or a mixture of 10 mL minÀ1 for O2, and 10 mL minÀ1 for air at 500 C and 900 C for h in ovens The X-ray diffraction patterns were recorded by an X-ray diffractometer (Rigaku D/Max 2550V) at 40 kV/200 mA using Cu ˚ Finally, only the crystal phase of Ka radiation (1.54056 A) a-Fe2O3 was found in the pure as-prepared a-Fe2O3 microparticles 2.3.2 Scanning electron microscopy In order to study the size and shape of the as-prepared a-Fe2O3 microparticles (Samples 1–3), we used a eld emission scanning electron microscope (SEM) (JEOL-JSM-634OF) operated at 5, 10, and 15 kV (5–15 kV), with a probe current around 12 mA The SEM images of the as-prepared Fe microparticles were focused by using a suitable ne focus level adjustment To characterize the a-Fe2O3 oxide microparticles with very large sizes of 1–5 mm, copper or copper brass grids containing the a-Fe2O3 microparticles were maintained under vacuum by using a vacuum cabinet Results and discussion Fig and show the SEM images of the as-prepared large a-Fe2O3 oxide microparticles with polyhedral morphologies and shapes of a certain size of about 1–5 mm.19,20 It should be noted that the as-prepared nanoparticles were observed to have polyhedral morphologies, such as cubes, octahedra, and tetrahedra etc This is possibly because sodium borohydride (NaBH4) is a very strong reducing agent, leading to the fast crystal growth of large polyhedral Fe2O3 microparticles Here, the polyhedral a-Fe2O3 microparticles have three large crystal surfaces with crystal planes of (100), (011), and (111) They have large homogeneous sizes and sharp, smooth, polyhedral surfaces In particular, our discovery of a new nano-structure is conrmed from our heat treatment process of the as-prepared Fe oxide microparticles at 900 C (Fig 3(b) and (c), S1 and S2 (ESI†)) but no clear and signicant structural changes at the surfaces of the large a-Fe2O3 microparticles at 500 C (Fig 3(a)) Very interestingly, most large polyhedral a-Fe2O3 oxide microparticles contained smaller a-Fe2O3 nanoparticles in their very large nano-textures All the large a-Fe2O3 crystal surfaces were clearly deformed in the nanoparticle heat treatment at 900 C C1 in Fig 4(c) shows the new micro-nano structure of one as-prepared large polyhedral Fe based microparticle aer heat treatment at about 900 C Although the particle size of this large microparticle was not signicantly changed, all the large crystal surfaces were signicantly changed into the new This journal is © The Royal Society of Chemistry 2014 View Article Online Paper Table RSC Advances Experimental conditions for the preparation of the samples, and their a-Fe2O3 crystal structure Sample Chemicals and precursor solution Experimental Heat treatment Crystal structure by XRD Sample mL of EG 1.5 mL of 0.0625 M FeCl3 mL of 0.375 M PVP 0.028 g NaBH4 mL of EG 1.5 mL of 0.0625 M FeCl3 mL of 0.375 M PVP 0.028 g NaBH4 200–230 C for 30 Drying in air or mixture of oxygen–air a-Fe2O3 (PDF-89-0597) Heated at 500 C in air or mixture of oxygen–air a-Fe2O3 (PDF-89-0597) Heated at 900 C in air or mixture of oxygen–air a-Fe2O3 (PDF-89-0597) Published on 14 November 2013 Downloaded by Shantou University on 14/05/2014 08:13:18 Sample Sample mL of EG 1.5 mL of 0.0625 M FeCl3 mL of 0.375 M PVP 0.028 g NaBH4 Pumping method of stock solutions 200–230 C for 30 Pumping method of stock solutions 200–230 C for 30 Pumping method of stock solutions SEM image of the uniform Fe oxide nanoparticles and large (a)Fe2O3 microparticles synthesized by a modified polyol method (Sample 1) Fig micro-nano surface structures Fig 4(d) and (e) present two models for possibility of very slow crack propagation along the grain boundaries for intergranular fractures (red and blue lines) 35 Ỉ grains or 35 Ỉ small or intermediate nanoparticles were observed in the large crystal surfaces or the crystal planes The various sizes of the nanoparticles were about 100–300 nm for the small a-Fe2O3 nanoparticles, and about 300–500 nm for the intermediate a-Fe2O3 nanoparticles, compared to the very large a-Fe2O3 microparticle of about mm The arrangements in order show that there are six nanoparticles or grains (6 Ỉ 1) in one row, and six nanoparticles or grains (6 Ỉ 1) in one column Therefore, there are 35 Ỉ nanoparticles as a raw estimation Thus, we estimate there are about 266 to 280 small nanoparticles (or grains) in the large microparticle The oxide grains are strongly connected and linked in one large particle as a three dimensional (3D) microparticle In addition, all the Fe2O3 grains clearly exhibited curvature on their surfaces Moreover, each a-Fe2O3 grain is classied as a single a-Fe2O3 crystal by the XRD method However, the boundaries between the grains are also clearly distinguished This journal is © The Royal Society of Chemistry 2014 Fig (a) SEM image of the large uniform and polyhedral Fe oxide nanoparticles and (a)-Fe2O3 microparticles synthesized by a modified polyol method (Sample 1) (b) SEM image of an orthorhombic crystal, and (c) its model The large oxide grains have two categories in normal and abnormal grain-growth regimes.26–32 Certain grains in our new micro-nano structures have both small and large sizes with respect to the abnormal grain-growth regimes They show unsharp curvature boundaries (our results) or sharp boundaries (our proposed model) Thus, there are important mechanisms and processes of recovery, re-crystallization, and development of grain growth in every large a-Fe2O3 crystal Surprisingly, the new 3D structures can be considered to be excellent evidence of 3D grain growth without particle collapse or cracking This is of RSC Adv., 2014, 4, 6383–6390 | 6385 View Article Online Published on 14 November 2013 Downloaded by Shantou University on 14/05/2014 08:13:18 RSC Advances Fig (a) SEM images of a-Fe2O3 nanoparticles with a sharp polyhedral shape and morphology in a sensor device calcined at 500 C with no changes in the a-Fe2O3 nanostructures (Sample 2) (b) and (c) SEM images of a-Fe2O3 nanoparticles with a sharp polyhedral shape and morphology in a sensor device calcined at 900 C (Sample 3) high importance, it is considered to be the “ideal” grain growth in materials optimization,29–31 as well as the recrystallization and annealing phenomena of the nanoparticles being of both technological importance and scientic interest at present.32 At present, 3D metal and oxide structures have been simulated under different grain growth regimes, but experimental evidence has not been shown in a micro- or nano-system Thus, our results are an interesting discovery regarding the structure and synthesis design of new micro-nano sized structures Here, each large a-Fe2O3 microparticle became an oxide nanograin system Clear and complete models of micro-nano surfaces and boundaries of nano-structures were previously proposed for heat treatments at high temperature.26–28,30 The important properties of nano-materials and nano-structures involved in the grain and boundary structure were predicted by modeling and simulation.29 At present, the creation of homogeneous and ne oxide grains in very large oxide microparticles is a big challenge for scientists From our proposed models in Fig S2(e) and (f) (ESI†) and Fig 4, the oxide grains have created large crystal surfaces with various different degrees of concave or convex curvature and roughness In fact, the oxide grains can be split in two categories, the coarse-grain forms and the ne-grain forms These are very crucial to predict the properties of engineered nanostructures in both theory and practice.26–35 Here, we have appropriately selected two temperature points for our method 6386 | RSC Adv., 2014, 4, 6383–6390 Paper Plastic and surface deformation: (a) the various grains and boundaries in one two dimensional (2D) large crystal surface of the grains with round boundaries of large a-Fe2O3 nanoparticles, as in SEM image C1; (b) the configuration of the boundaries in the 2D system observed in SEM image C3; (c)–(e) proposed models for two cases: (c) no heat treatment; (d) and (e) with heat treatment (d) Large 3D particle made up of grains with un-sharp curvature boundaries (our results); (e) or with sharp boundaries (our proposal) as estimated in C3 Fig of nanoparticle heat treatment to produce nanoparticles with an a-Fe2O3 structure the same as the well-known a-FeC equilibrium diagram from 500 to 910 C.33,34 This is an interesting nding for making a-Fe2O3 microparticles with deformed surface states For a given method of nanoparticle heat treatment, it is possibly true that the various pure structures of metal, alloy, and oxide nanoparticles are the same as their equilibrium diagrams in metallurgy Aer annealing, there is the appearance of small and large a-Fe2O3 grains in the large crystal surfaces because of renucleation and recrystallization processes The severe deformation of the large, at, and smooth crystal surfaces into concave, convex, rough, and distorted crystal surfaces of a-Fe2O3 microparticles is very crucial to achieve new nano-textures (Fig 3(b) and (c), S1 and S2 (ESI†), and Fig with models) These Fe2O3 structures may be very stiff and permanent aer nanoparticle heat treatment in the 500–900 C range investigated We suggest that there was plastic deformation in the a-Fe2O3 crystal surfaces of every Fe2O3 microparticle, but also elastic deformation in the a-Fe2O3 microparticles with no signicant changes in the particle size distribution Thus, an appropriate annealing process can control the grain sizes and boundaries among the interfaces of the grains This journal is © The Royal Society of Chemistry 2014 View Article Online Published on 14 November 2013 Downloaded by Shantou University on 14/05/2014 08:13:18 Paper The phenomenon of grain growth has been explained even for metals, alloys and oxides.26–33 The plastic and surface deformation mechanisms and stress–strain behaviors have generally led to various methods to strengthen and regulate the mechanical characteristics of steel (FeC) or ferrite, which are important in metallurgy.29,33 These allow new methods of nanoparticle heat treatment for engineered nanoparticles So far, most annealing and heat treatments have generally led to new structures of metals, alloys, glasses, ceramics and oxides with interesting new (and some already known) discoveries such as higher strength, better toughness, higher durability and stability through small grains, creep resistance and reduction through large grains.32 These are due to the special characteristics of both small grain and large grain systems Plastic and super-plastic deformations were characterized in FeC, Fe oxides, and Fe alloys during steel heat treatment.26,33 However, we also suggest that the curvature boundaries between the grains were possibly due to both plastic and elastic deformation, permanent plastic deformation of the external surface and internal structure, and elastic deformation where the particle size was retained in the elastic recovery of particle shape Furthermore, a-Fe2O3 microparticles with sharp and straight edges (Fig 1, 2, and 3a) were observed in both plastic and elastic deformation processes, but higher localized plastic deformation on all surfaces was also observed (Fig 3(b) and (c) and models (a), (b), (d), and (e) in Fig 4) Our interesting evidence regarding plastic and elastic atomic surface deformation and grain growth is of importance in simulation and modeling at present Although the grain boundaries of the a-Fe2O3 grains are clearly distinguishable on the surface of one large microparticle, it is not difficult to observe possible cracking and propagation cracking in the prepared microparticles The good recovery characteristics of the large shape and morphology of aFe2O3 microparticles was shown aer strong surface deformation and plastic deformation in the formed a-Fe2O3 grains Thus, we can expect that the boundaries of the ne grains in one such large microparticle can be controlled by the nanoparticle sintering process This also illustrates the well ordered arrangement of the small and intermediate a-Fe2O3 oxide nanoparticles with specic ne grain boundaries, and also within the oxide grains on the surfaces annealed at 900 C for h that were evidenced by one as-prepared large a-Fe2O3 oxide microparticle (or large a-Fe2O3 oxide crystal) The boundaries of a-Fe2O3 oxide grains and a-Fe2O3 oxide domains were also observed on the large crystal surfaces and we predict their existence inside the internal structure of the pure large polyhedral a-Fe2O3 oxide microparticles There are two small holes on the crystal surface, which are observed because there is a certain degree of the porosity in the large microparticle Fig S2(b) (ESI†) shows the micro-nano structure of the asprepared large a-Fe2O3 oxide microparticles of about mm with an orthorhombic shape and morphology The crystal a-Fe2O3 oxide grains and grain boundaries of nite sizes can be clearly distinguished The small crystal grains are normally located at the corners of the intermediate a-Fe2O3 oxide grains In the asprepared large a-Fe2O3 oxide microparticles, their shapes and This journal is © The Royal Society of Chemistry 2014 RSC Advances morphologies have at and smooth crystal surfaces Aer an appropriate heat treatment, the Fe based grains (or Fe based nanocrystals) appeared on the surfaces Each large crystal surface will become more coarse because of the concave and convex local regions of a-Fe2O3 oxide grains that are caused So far, our samples are considered to be the best examples of very large a-Fe2O3 microparticles with oxide grains, oxide grain domains, and sharp and un-sharp boundaries for future studies in this eld In addition, Fig S2(c) and (d) (ESI†) show interesting a-Fe2O3 oxide grains in the forms of micro and nano oxide crystals Crystallization and re-crystallization transformations were observed in the deformation of sharp, at, and smooth large oxide crystals into un-sharp, distorted, rough, convex and concave large oxide crystals with specic oxide grains Our latest results regarding the pure a-Fe2O3 oxide microstructures and nanostructures with respect to the structural phase transitions and mechanisms are the most important examples at present Thus, the high roughness of the small and large a-Fe2O3 oxide crystals was caused during heat treatment at 900 C The aFe2O3 oxide grains also appeared at all of the six large crystal surfaces of the as-prepared large polyhedral a-Fe2O3 oxide microparticles The most important thing is that there are no collapses of the nano- and micro-structures of the large as-prepared a-Fe2O3 oxide microparticles in the range between 500 C and 900 C Therefore, the important issues of achieving high stability and durability are possibly dealt with by using higher heat treatments for microsystems and nanosystems Because the a-Fe2O3 nanostructures have very large sizes, we did not characterize them by TEM measurements in our subsequent further investigation As a facile method for the controlled synthesis of Fe oxide based microparticles, we suggest that NaBH4 can be successfully used for the very strong reduction of Fe precursors in various common solvents, such as EG, alcohols and water A moderate addition of control agents such as NaOH, NH4OH, NaI, HCl etc can be carried out during the controlled synthesis By this method, NaBH4 can usually be used in excess amounts for the full reduction of metal precursors.17–24 Here, we suggest that the fast formation of very small Fe metal nanoparticles during the synthetic process occurred at 200–230 C.19 We also suggest that, rst, Fe nanoparticles were formed by the full reduction of Fe precursors such as FeCl3$xH2O (or FeCl2$xH2O) with the addition of NaBH4 Then, the surfaces of the Fe nanoparticles are oxidized in the initial formation of the Fe oxide shells According to the synthesis time, the formation of metal oxide shell can be understood to be a gradual and slow oxidation In general, this can lead to the complete internal structure of the prepared microparticles being completely oxidised As crucial evidence for this, structural transformations among FeO (Wustite), 3-Fe2O3, Fe3O4, g-Fe2O3, and a-Fe2O3 can be carried out through suitable heat treatments.9,36 However, there have been many considerable difficulties encountered when scientists have tried to make large nano-textures from smaller nanoparticles by self-assembly methods It is clear that our asprepared products, the Fe based nanoparticles with the controlled homogeneous features of size, shape, and morphology, can be used in order to meet the very high demands of sensor materials RSC Adv., 2014, 4, 6383–6390 | 6387 View Article Online Published on 14 November 2013 Downloaded by Shantou University on 14/05/2014 08:13:18 RSC Advances The nal formation of the pure a-Fe2O3 structure in EG was done with the long-term stabilization of various PVP polymers by a facile method with the use of NaBH4 as a strong reducing agent for the Fe precursors The successfully controlled synthesis of magnetite nanoparticles has been shown in some recent works These works also tried to focus on the facile synthesis of the crystal phases of MNs, such as Fe3O4, g-Fe2O3, and a-Fe2O3 nanoparticles,37 and on producing a-Fe2O3 nanoparticles for promising applications in lithium ion batteries,38 as well as nanostructured Fe oxide materials for much more durable and stable advanced energy conversion and storage devices, such as nano-sized transition-metal oxides as negative-electrode materials for high performance lithium-ion batteries.39,40 In addition, we have evaluated the crystal structure of the as-prepared samples of large Fe2O3 microparticles Fig shows the typical XRD patterns of one dried sample, and two samples aer calcination at 500 and 900 C Here, the pure a-Fe2O3 oxide microparticles display a rhombohedral crystal structure The prepared large microparticles analysed by the XRD method had sharp and narrow diffraction peaks, which is evidence of the high crystallization of the pure a-Fe2O3 crystal structure produced by the modied polyol method with NaBH4 The a-Fe2O3 crystal structure (hematite system) belonging to the crystallographic space C[167] has lattice constants (a,b,c) equal to 5.039 nm, group R3 Fig XRD powder diffraction patterns of the samples of the Fe based nanoparticles prepared at various temperatures: (a) dried sample (Sample 1), (b) 500 C (Sample 2), and (b) 900 C (Sample 3) The stability and durability of the a-Fe2O3 nanostructure during nanoparticle heat treatment at high temperatures were identified 6388 | RSC Adv., 2014, 4, 6383–6390 Paper 5.039 nm, and 13.770 nm, respectively, with a ratio of c/a ¼ 2.733 (ICDD/JCPDS PDF-89-0597) using the JADE soware (Materials Data) for XRD pattern processing and MDI materials data Table lists the powder pattern indexing of Samples 1–3 For Sample (c/a ¼ 2.730815) and Sample (c/a ¼ 2.733914), the c/a ratios are the same as that of a standard sample (ICDD/JCPDS PDF-89-0597) For Sample 3, the c/a ratio of our sample is equal to 2.726895 at 900 C, which is a little smaller than that of the standard sample The narrow and sharp peaks from the XRD show the very high crystallization of large polyhedral a-Fe2O3 microparticles without any mixture of other phases, such as FeO (Wustite), a-FeOOH, 3-Fe2O3, Fe3O4, g-Fe2O3 etc As shown in Fig 5, the calcination of samples at 500 and 900 C also resulted in the formation of a-Fe2O3 (PDF-89-0597) crystal phase structure Importantly, high crystallization of the pure rhombohedral hematite a-Fe2O3 was obtained between 500 C and 900 C As shown in Fig 2(a)–(c) and S1 and S2 (ESI†), the degree of densication of the prepared oxide microparticles at 500 C is a little smaller than that of the prepared oxide microparticles at 900 C Thus, the as-prepared microparticles are single crystals or monocrystallites because they show a sharp polyhedral shape and morphologies that are continuous and unbroken to the edges and corners of the microparticles in Sample 1, without the existence of any grains or boundaries All the microparticles have sharp, smooth, and at surfaces, as well as sharp rightangled edges and corners In the a-Fe2O3 microparticles aer heat treatment at 500 C (Sample 2) and 900 C (Sample 3), the structures were considerably changed The microparticles were changed in their deformation at 500 C but show no signicant changes in their size and shape in Fig 3(a) They gradually became polycrystals under high heat treatment At an annealing temperature of about 900 C, the microparticles were changed due to their very signicant deformations, with the appearance of grains and boundaries between them The grains have particle sizes in both the microsize range and the nanosize range Additionally, the polycrystalline a-Fe2O3 microparticles or a-Fe2O3 polycrystallites have various crystallites of varying size and orientation Each microparticle became a polycrystal or a polycrystallite Here, each microparticle has much smaller a-Fe2O3 microparticles and a-Fe2O3 nanoparticles, or so-called grains However, each grain can be considered a single crystal or single crystallite because of their continuous shape and morphology At present, the a-Fe2O3 oxide based nanostructures have special signicance for ecosystems and environmental applications,41 a-Fe2O3 tetradecahedra can be used in gas sensing by a facile hydrothermal method with the use of K4Fe(CN)6$3H2O, sodium carboxymethyl cellulose solution, PVP, and N2H4$3H2O solution at room temperature at 200 C for h,42 and other a-Fe2O3 structures also have practical applications in gas sensing.42–45 Interestingly, the important roles of the metal or alloy or oxide grains were known in the signicant reduction of lattice thermal conductivity for an enhanced ZT applied in new thermal nano-structured materials.30 The topic of nanoparticle heat treatment will be an important subject for scientists, and specialists In addition, various methods of nanoparticle heat This journal is © The Royal Society of Chemistry 2014 View Article Online Paper Published on 14 November 2013 Downloaded by Shantou University on 14/05/2014 08:13:18 Table RSC Advances The indexing of powder diffraction patterns of a-Fe2O3 oxide Sample a (nm) b (nm) c (nm) c/a Space group ICDD/JCPDS-PDF Sample Sample Sample 5.056 5.051 5.053 5.056 5.051 5.053 13.807 13.809 13.779 2.730815 2.733914 2.726895 C(161) R3 C(161) R3 C(161) R3 ICDD/JCPDS PDF-89-0597 ICDD/JCPDS PDF-89-0597 ICDD/JCPDS PDF-89-0597 treatment need to be signicantly considered in the development of new nanomaterials with grain and boundary structures.45 Conclusion In this research, we have successfully prepared large a-Fe2O3 microparticles by a modied polyol method with NaBH4 A new a-Fe2O3 microparticle with a-Fe2O3 grains was discovered by chance following external surface deformation, and did not show structural collapse aer nanoparticle heat treatment at 900 C This new structure of a-Fe2O3 microparticles containing micro-grains, nano-grains and boundaries would potentially exhibit good properties in future gas sensors Acknowledgements In this research, we are very grateful to the precious support from the Structural Ceramics Engineering Center, Shanghai Institute of Ceramics, Chinese Academy of Science, Dingxi Road 1295, Shanghai 200050, China This study was also supported in part by a fund from the National Natural Science Foundation of China (NSFC, contract nos 51071167 and 51102266) Lastly, we would like to thank the signicant efforts of Mr Michael Ignatowich (PhD student), California Institute of Technology for checking and editing the manuscript References G Eranna, B C Joshia, D P Runthalaa and R P Guptaa, Crit Rev Solid State Mat Sci., 2004, 29(3–4), 111 O Margeat, F Dumestre, C Amiens, B Chaudret, P Lecante and M Respaud, Prog Solid State Chem., 2005, 33(2–4), 71 G Korotcenkov, Mater Sci Eng., B, 2007, 139(1), S P Mitoff, J Chem Phys., 1961, 35, 882 Y Li, W Wlodarski, K Galatsis, S H Moslih, J Cole, S Russo and N Rockelmann, Sens Actuators, B, 2002, 83, 160 F Hossein-Babaei, M Keshmiri, M Kakavand and T Troczynski, Sens Actuators, B, 2005, 110, 28 P T Moseley, Sens Actuators, B, 1991, 3, 167 C Cantalini, M Faccio, G Ferri and M Pelino, Sens Actuators, B, 1994, 19, 437 N D Chuong, T T Hoa, D Q Khieu, T D Lam, N D Hoa and N V Hieu, J Alloys Compd., 2012, 523, 120 10 Z F Dou, C Y Cao, Q Wang, J Qu, Y Yu and W G Song, ACS Appl Mater Interfaces, 2012, 4, 5698 11 Y Kang, L Wang, Y Wang, H Zhang, Y Wang and D Hong, Sens Actuators, B, 2013, 177, 570 This journal is © The Royal Society of Chemistry 2014 12 C Santilli, J Bonnet, P Dordor, M Onillon and P Hagenmuller, Ceram Int., 1990, 16, 25 13 W B Ingler Jr and S U M Khan, Thin Solid Films, 2004, 461, 301 14 Z Jing, Mater Lett., 2006, 60, 3315 15 V N Mishra and R P Agarwal, Microelectron J., 1998, 29, 861 16 X Zhu, Y Zhu, S Murali, M D Stoller and R S Ruoff, ACS Nano, 2011, 5(4), 3333 17 P Majewski, in Nanomaterials for Water Treatment, ed C S S R Kumar, Wiley, 2006, pp 211–233 18 N T K Thanh, Magnetic Nanoparticles: From Fabrication to Clinical Applications: Theory to Therapy, Chemistry to Clinic, Bench to Bedside, 2012, CRC Press 19 D L Huber, Small, 2005, 1(5), 482 20 S Teja and K P Koh, Prog Cryst Growth Charact Mater., 2009, 55, 22 21 M Colombo, S Carregal-Romero, M F Casula, L Guti´ errez, M P Morales, I B Bă ohm, J T Heverhagen, D Prosperi and W J Parak, Chem Soc Rev., 2012, 41, 4306 22 A Lu, E L Salabas and F Schă uth, Angew Chem., Int Ed., 2007, 46(8), 1222 23 S Laurent, D Forge, M Port, A Roch, C Robic, L V Elst and R N B Muller, Chem Rev., 2008, 108, 2064 24 L H Reddy, J L Arias, J Nicolas and P Couvreur, Chem Rev., 2012, 112(11), 5818 25 N V Long, M Ohtaki, M Uchida, R Jalem, H Hirata, N D Chien and M Nogami, J Colloid Interface Sci., 2011, 359, 339 26 C C Koch, I A Ovid'ko, S Seal and S Verrek, Structural Nanocrystalline Materials Fundamentals and Applications, Oxford, 2005 27 D T Lewellyn and R Hudd, Steels: Metallurgy & Applications, Reed Educational and Professional Publishing Ltd, 3rd edn, 1998 28 J W Christian, The Theory of Transformations in Metals and Alloys (Part I + II), Elsevier Science Ltd, 3rd edn, 2002 29 (a) S Yip, Handbook of Materials Modeling, Part A Methods, ed S Yip, Massachusetts Institute of Technology, Springer, 2005; (b) S Yip, Handbook of Materials Modeling, Part B Models, ed S Yip, Massachusetts Institute of Technology, Springer, 2005 30 Y Lan, A J Minnich, G Chen and Z Ren, Adv Funct Mater., 2010, 20, 357 31 C E Krill III and L Q Chen, Acta Mater., 2002, 50, 3057 32 F J Humphreys and M Hatherly, Recrystallization and related annealing phenomena, Elsevier Ltd., 2nd edn, 2004 33 G E Totten, Steel Heat Treatment Handbook, CRC Press, Taylor & Fracis Group, LLC, 2nd edn, 2007 RSC Adv., 2014, 4, 6383–6390 | 6389 View Article Online Published on 14 November 2013 Downloaded by Shantou University on 14/05/2014 08:13:18 RSC Advances 34 D T LleweUyn and R C Hudd, Steels: Metallurgy and Applications, Reed Educational and Professional Publishing Ltd, 3rd edn, 1998 35 A Mallick, Comput Mater Sci., 2013, 67, 27 36 S Peng, J Kim and S Sun Chemical Synthesis, SelfAssembly and Applications of Magnetic Nanoparticles, Annual Review of Nano Research, ed G Cao and C J Brinker, 2010, vol 3, ch 6, pp 275– 307 37 S Sun and H Zeng, J Am Chem Soc., 2002, 124, 8204 38 M Du, C Xu, J Sun and L Gao, J Mater Chem A, 2013, 1(24), 7154 39 A S Aric` o, P Bruce, B Scrosati, J Tarascon and W Schalkwijk, Nat Mater., 2005, 4, 366 6390 | RSC Adv., 2014, 4, 6383–6390 Paper 40 P Poizot, S Laruelle, S Grugeon, L Dupont and J M Tarascon, Nature, 2000, 407, 496 41 H Guo and A S Barnard, J Mater Chem A, 2013, 1, 27 42 Y Yang, H Ma, J Zhuang and X Wang, Inorg Chem., 2011, 50, 10143 43 C Wu, P Yin, X Zhu, C O Yang and Y Xie, J Phys Chem B, 2006, 110(36), 17806 44 D S Jordan, C J Hull, J M Troiano, S C Riha, A B F Martinson, K M Rosso and F M Geiger, J Phys Chem C, 2013, 117(8), 4040 45 J R Ray, W Wan, B Gilbert and Y Jun, Langmuir, 2013, 29(4), 1069 46 N V Long, Y Yang, M Yuasa, T M Cao, Y Cao, T Nann and M Nogami, RSC Adv., 2013, DOI: 10.1039/c3ra46410e This journal is © The Royal Society of Chemistry 2014 ... 2(a)–(c) and S1 and S2 (ESI†), the degree of densication of the prepared oxide microparticles at 500 C is a little smaller than that of the prepared oxide microparticles at 900 C Thus, the as-prepared... substrate for XRD analysis The high heat treatment of our samples was carried out in a gas/ air ow (20 mL minÀ1) or a mixture of 10 mL minÀ1 for O2, and 10 mL minÀ1 for air at 500 C and 900 C for. .. plastic and elastic deformation, permanent plastic deformation of the external surface and internal structure, and elastic deformation where the particle size was retained in the elastic recovery of