Volume 06 - Welding, Brazing and Soldering Part 10 pps

TABLE 3 COMPOSITION OF SELECTED MECHANICALLY ALLOYED MATERIALS ALLOY Fe Cr Al Ti Ni C Y 2 O 3 . . . . . . 0.3 MA 6000 . . . 15.0 4.5 2.5 BAL 0.5 0.6 . . . TABLE 4 PROPERTIES OF SELECTED MECHANICALLY ALLOYED MATERIALS DENSITY YOUNG'S MODULUS TENSILE STRENGTH (A) YIELD STRENGTH (A) 100 H ALLOY G/CM 3 LB/IN. 3 GPA 10 6 PSI MPA KSI MPA KSI ELONGATION AT FRACTURE, % (A) MPA KSI MPA 13.6 7.4 . . . MA 6000 (B) 8.11 0.293 203 29.4 222 32.2 192 27.8 9 131 19 127 18.5 REPAIR OF TURBINE BLADES AND VANES, [...]... THERMAL EXPANSION(A), 1 0-6 /K THERMAL CONDUCTIVITY W/M2·K BTU/FT2 H · °F · ELECTRICAL RESISTIVITY, 1 0-8 Ω/M • • • WELD J., WELD J., WELDING RESEARCH COUNCIL SYMPOSIUM ON EFFECTS OF MINOR ELEMENTS ON THE WELDABILITY OF HIGH-NICKEL ALLOYS, PROC FIFTH BOLTON LANDING CONF., TABLE 3 TYPICAL ANNEALING TEMPERATURES FOR CORROSION-RESISTANT NICKEL, NICKELCOPPER, NICKEL-CHROMIUM, AND NICKEL-CHROMIUM-IRON ALLOYS ALLOY... REFRACTORY METALS AND THEIR INDUSTRIAL APPLICATIONS, RHENIUM ALLOYS, INT MATER REV., Corrosion, ASM Handbook, J MET., • • • • • J MET., TABLE 1 COMPOSITIONS OF SELECTED NICKEL-BASE CORROSION-RESISTANT ALLOYS ALLOY COMPOSITION, WT% Ni Cr Fe Cu C0 NICKEL ALLOYS Si NICKEL-COPPER ALLOY NICKEL-CHROMIUM ALLOYS NICKEL-CHROMIUM-IRON ALLOYS Al Ti Mo TABLE 2 PROPERTIES OF SELECTED NICKEL-BASE CORROSION-RESISTANT ALLOYS... PROCEDURES FOR SELECTED NICKEL-BASE CORROSION-RESISTANT ALLOYS ALLOYS 200 AND 201 FOR CAUSTIC SERVICE ALLOY 600 FOR CAUSTIC SERVICE ALLOY 400 FOR HYDROFLUORIC ACID SERVICE TABLE 5 WELDING PRODUCTS FOR DISSIMILAR-METAL JOINTS BETWEEN NICKEL-BASE CORROSION-RESISTANT ALLOYS AND OTHER METALS NICKELBASE ALLOY WELDING PRODUCT FOR DISSIMILAR-METAL JOINT WITH STAINLESS STEEL CARBON AND LOW-ALLOY STEEL ELECTRODE FILLER... Cu NICKEL-BASE OTHERS N CORROSION, CORROSION, ALLOYS FOR THE EIGHTIES, TABLE 2 PHYSICAL PROPERTIES OF NICKEL-BASE MOLYBDENUM-BEARING CORROSIONRESISTANT ALLOYS RELATIVE TO CARBON STEEL AND STAINLESS STEELS MATERIAL MELTING TEMPERATURE RANGE DENSITY THERMAL CONDUCTIVITY COEFFICIENT OF THERMAL EXPANSION ELECTRICAL RESISTIVITY, 1 0-8 Ω · M °C °F g/cm3 lb/in.3 w/m · k btu in./ft2 · h · °f 1 0-6 /K 1 0-6 / °F •... METAL 5-9 % NI STEEL ELECTRODE COPPER FILLER METAL ELECTRODE NICKEL-COPPER FILLER METAL ELECTRODE FILLER METAL WELD J., WELD J., WELDING RESEARCH COUNCIL SYMPOSIUM ON EFFECTS OF MINOR ELEMENTS ON THE WELDABILITY OF HIGH-NICKEL ALLOYS, PROC FIFTH BOLTON LANDING CONF., TABLE 1 NOMINAL COMPOSITION CORROSION-RESISTANT ALLOYS ALLOY TYPE ALLOY UNS NO OF SELECTED COMPOSITION, WT % Ni Co Fe Cr Mo W MOLYBDENUM-BEARING . Cu C0 Si Al Ti Mo NICKEL ALLOYS NICKEL-COPPER ALLOY NICKEL-CHROMIUM ALLOYS NICKEL-CHROMIUM-IRON ALLOYS TABLE 2 PROPERTIES OF SELECTED NICKEL-BASE CORROSION-RESISTANT ALLOYS MELTING RANGE THERMAL. METALS AND THEIR INDUSTRIAL APPLICATIONS, RHENIUM ALLOYS, INT. MATER. REV., Corrosion, ASM Handbook, J. MET., • • • • • J. MET., TABLE 1 COMPOSITIONS OF SELECTED NICKEL-BASE CORROSION-RESISTANT. G/CM 3 °C °F COEFFICIENT OF THERMAL EXPANSION (A) , 10 -6 /K W/M 2 ·K BTU/FT 2 · H · °F ELECTRICAL RESISTIVITY, 10 -8 Ω/M