000450U006 2008a SECTION II, PART A SA 1017/SA 1017M SPECIFICATION FOR PRESSURE VESSEL PLATES, ALLOY STEEL, CHROMIUM MOLYBDENUM TUNGSTEN SA 1017/SA 1017M (Identical with ASTM Specification A 1017/A 10[.]
2008a SECTION II, PART A SA-1017/SA-1017M SPECIFICATION FOR PRESSURE VESSEL PLATES, ALLOY STEEL, CHROMIUM-MOLYBDENUMTUNGSTEN SA-1017/SA-1017M (Identical with ASTM Specification A 1017/A 1017M-07.) Scope 1.1 This specification covers Chromium-MolybdenumTungsten alloy steel plates intended primarily for welded boilers and pressure vessels designed for elevated temperature service A 577 /A 577M Specification for Ultrasonic Angle-Beam Examination of Steel Plates General Requirements 3.1 Material supplied to this material specification shall conform to Specification A 20 /A 20M Such requirements outline the testing and retesting methods and procedures, permissible variations in dimensions and weight [mass], quality and repair of defects, marking, loading, and so forth 1.2 Plates are available under this specification in three grades having different alloy contents as follows: Grade 23 911 122 Nominal Chromium Content, % Nominal Molybdenum Content, % Nominal Tungsten Content, % 2.25 9.00 12.00 0.20 1.00 0.40 1.60 1.00 2.00 3.2 Specification A 20 /A 20M also establishes the rules for the ordering information that should be complied with when purchasing material to this specification 3.3 In addition to the basic requirements of this specification, certain supplementary requirements are available when additional control, testing, or examination is required to meet end use requirements The purchaser is referred to the listed supplementary requirements in this specification and to the detailed requirements in Specification A 20 /A 20M 1.3 The maximum thickness of plates is limited only by the capacity of the composition to meet the specified mechanical property requirements 1.4 The specification is expressed in both inch-pound units and in SI units However, unless the order specifies the applicable “M” specification designation (SI units), the material shall be furnished to inch-pound units 1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard Within the text, the SI units are shown in brackets The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other 3.4 If the requirements of this specification are in conflict with the requirements of Specification A 20 /A 20M, the requirements of this specification shall prevail Referenced Documents 2.1 ASTM Standards: A 20 /A 20M Specification for General Requirements for Steel Plates for Pressure Vessels A 435 /A 435M Specification for Straight-Beam Ultrasonic Examination of Steel Plates Materials and Manufacture 4.1 Steelmaking Practice — The steel shall be killed Heat Treatment 5.1 Except as allowed by 5.2 and 5.3, all plates shall be normalized at 1900 to 1975°F [1040 to 1080°C] Plates for Grades 23 and 122 shall be tempered at 1350 to 1470°F [730 to 800°C] Grade 911 plates shall be tempered at 1365 to 1435°F [740 to 780°C] 1633 Copyright ASME International Provided by IHS under license with ASME No reproduction or networking permitted without license from IHS Licensee=Chevron Corp/5912388100 Not for Resale, 08/28/2008 11:18:04 MDT A08 SA-1017/SA-1017M 2008a SECTION II, PART A 5.2 If permitted by the purchaser, plates for Grades 23 and 122 may be austenitized at 1900 to 1975°F [1040 to 1080°C], subjected to accelerated cooling from the austenitizing temperature by air blasting or liquid quenching, and then tempered at 1350 to 1470°F [730 to 800°C] 5.3 Plates ordered without the heat treatment required by either 5.1 or 5.2 shall be furnished in either the stressrelieved or annealed condition, and the purchaser shall be responsible for the heat treatment of such plates to conform to either 5.1 or 5.2 Chemical Composition 6.1 The steel shall conform to the requirements for chemical composition given in Table Mechanical Properties 7.1 Tension Test: 7.2 Hardness Test: 7.2.1 Grade 23 plates shall have a hardness not exceeding 220 HB [97HRB] 7.2.2 Grade 122 plates shall have a hardness not exceeding 250 HB [25HRC] Marking 8.1 In addition to the marking required in Specification A 20/A 20M, each plate shall be legibly stamped or stenciled, dependent upon the ordered thickness, with the letter “N” for normalized and tempered, “Q” for accelerated cooled and tempered, “S” for stress relieved, or “A” for annealed, whichever is applicable 7.1.1 The material as represented by the tension test specimens shall conform to the applicable requirements given in Table Keywords 9.1 alloy steel; alloy steel plate; pressure containing parts; pressure vessel steels; steel plates; steel plates for pressure vessels 1634 Copyright ASME International Provided by IHS under license with ASME No reproduction or networking permitted without license from IHS Licensee=Chevron Corp/5912388100 Not for Resale, 08/28/2008 11:18:04 MDT 2008a SECTION II, PART A SA-1017/SA-1017M TABLE CHEMICAL REQUIREMENTS Composition % Element Carbon Heat Analysis Product Analysis Manganese Heat Analysis Product Analysis Phosphorus, max Heat Analysis Product Analysis Sulfur, max Heat Analysis Product Analysis Silicon Heat Analysis Product Analysis Chromium Heat Analysis Product Analysis Molybdenum Heat Analysis Product Analysis Nickel, max Heat Analysis Product Analysis Vanadium Heat Analysis Product Analysis Columbium Heat Analysis Product Analysis Boron Heat Analysis Product Analysis Nitrogen Heat Analysis Product Analysis Aluminum, max Heat Analysis Product Analysis Tungsten Heat Analysis Product Analysis Copper Heat Analysis Product Analysis Titanium, max Heat Analysis Product Analysis Zirconium, max Heat Analysis Product Analysis Grade 23 Grade 911 0.04–0.10 0.03–0.10 0.09–0.13 0.08–0.14 0.07–0.14 0.05–0.17 0.10–0.60 0.09–0.66 0.30–0.60 0.25–0.66 0.70 max 0.77 max 0.030 0.030 0.020 0.025 0.020 0.025 0.010 0.012 0.010 0.012 0.010 0.012 0.50 max 0.50 max 0.10–0.50 0.08–0.56 0.50 max 0.56 max 1.90–2.60 1.78–2.72 8.5–9.5 8.4–9.7 10.0–11.5 9.9–11.6 0.05–0.30 0.04–0.35 0.90–1.10 0.85–1.15 0.25–0.60 0.20–0.65 0.40 0.43 0.50 0.54 0.20–0.30 0.18–0.33 0.18–0.25 0.16–0.27 0.15–0.30 0.13–0.32 0.02–0.08 0.02–0.10 0.06–0.10 0.05–0.11 0.04–0.10 0.03–0.11 0.0005–0.006 0.0004–0.007 0.0003–0.006 0.0002–0.007 0.005 max 0.006 max 0.030 max 0.030 max 0.04–0.09 0.035–0.095 0.04–0.10 0.03–0.11 0.03A 0.04A 0.02 0.02 0.02 0.02 1.45–1.75 1.40–1.80 0.90–1.10 0.85–1.15 1.50–2.50 1.40–2.60 0.30–1.70 0.20–1.80 0.01 0.01 0.01 0.01 0.01 0.01 0.01 0.01 NOTE — Where “ .” appears in this table there is no requirement A Acid Soluble Aluminum 1635 Copyright ASME International Provided by IHS under license with ASME No reproduction or networking permitted without license from IHS Grade 122 Licensee=Chevron Corp/5912388100 Not for Resale, 08/28/2008 11:18:04 MDT SA-1017/SA-1017M 2008a SECTION II, PART A TABLE TENSILE REQUIREMENTS Tensile Strength, ksi [MPa] Yield Strength, ksi [MPa] Elongation in in % ```,,,,,,``,`,``,,`````,`,`,``-`-`,,`,,`,`,,` - Copyright ASME International Provided by IHS under license with ASME No reproduction or networking permitted without license from IHS Grade 23 Grade 911 Grade 122 74 to 100 [510 to 690] 58 [400] 20 90 to 120 [620 to 840] 64 [440] 18 90 [620] 58 [400] 20 1636 Licensee=Chevron Corp/5912388100 Not for Resale, 08/28/2008 11:18:04 MDT 2008a SECTION II, PART A SA-1017/SA-1017M SUPPLEMENTARY REQUIREMENTS Supplementary requirements shall not apply unless specified in the order A list of standardized supplementary requirements for use at the option of the purchaser is included in Specification A 20/A 20M Several of those considered suitable for use with this specification are listed below by title Other tests may be performed by agreement between the supplier and the purchaser S1 Vacuum Treatment S2 Product Analysis S3 Simulated post-weld heat treatment of mechanical test coupons S4.1 Additional Tension Test S8 Ultrasonic Examination in accordance with Specification A 435/A 435M S9 Magnetic Particle Examination S11 Ultrasonic Examination in accordance with Specification A 577/A 577M S5 Charpy V-notch impact test S6 Drop Weight Test (for Material 0.625 in [16 mm] and Over in Thickness) S12 Ultrasonic Examination in accordance with Specification A 578/A 578M S7 High-Temperature Tension Test S17 Vacuum Carbon Deoxidized Steel 1636.1 Copyright ASME International Provided by IHS under license with ASME No reproduction or networking permitted without license from IHS Licensee=Chevron Corp/5912388100 Not for Resale, 08/28/2008 11:18:04 MDT INTENTIONALLY LEFT BLANK 1636.2 Copyright ASME International Provided by IHS under license with ASME No reproduction or networking permitted without license from IHS Licensee=Chevron Corp/5912388100 Not for Resale, 08/28/2008 11:18:04 MDT