Materials Handbook 15th 2010 Part 2 pps
Materials Handbook 15th 2010 Part 2 pps
... as high as 3% TiO 2 . Two kinds of red bauxite are found in Italy, a dark variety containing 54 to 58% Al 2 O 3 , and only 2 to 4 SiO 2 , but having 22 to 26 % Fe 2 O 3 , and 2 to 3 TiO 2 , and a light ... to 60% Al 2 O 3 , 6.7 Fe 2 O 3 , 3 to 5 SiO 2 , and 0.9 to 1 TiO 2 . The large deposits on Ponape and other Pacific islands average 50 to 52% alumina, 3 to 6 silica...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 3 ppsx
... to 393 MPa); 23 ,000 to 38,000 lb/in 2 (159 to 26 2 MPa); and 30 to 45%. And for DQ cold-rolled sheet: RB 32 to 52; 38,000 to 50,000 lb/in 2 (26 2 to 345 MPa); 20 ,000 to 34,000 lb/in 2 (138 to 23 4 MPa); ... 130,000 to 22 0,000 lb/in 2 (896 to 1,517 MPa) but little duc- tility, 4 to 2% elongation, respectively. Low-carbon steels 1018 to 1 025 in cold-drawn bar 0. 625 to 0.875...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 1 pptx
... single crystal. The tensile strength is up to 32, 500 lb/in 2 (22 4 MPa), compressive strength up to 29 0,000 lb/in 2 (2, 000 MPa), and dielectric strength 25 0 V/mil (9.8 ϫ 10 6 V/m). It is used for ... lb/in 2 ( 324 0 to 3310 MPa); and the heat deflection temperature at 26 4 lb/in 2 (1.8 MPa) is 23 0 to 24 8°F (110 to 120 °C). Volan, of the Du Pont Co., is a methacrylate-chromi...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 4 pot
... WI- 52; X-40; J-1650; Haynes 21 and 151; AiResist 13, 21 3, and 21 5; and MAR-M 3 02, 322 , and 918. Their 1,000-h stress-rupture strengths range from about 40,000 lb/in 2 (27 6 MPa) to 70,000 lb/in 2 (483 ... (177°C). Cycom 525 0-4, 526 0, and 527 0-1 are BMIs from Cytec Fiberite. The 525 0-4 and toughened 526 0 have service temperatures to about 350°F (177°C), the 527 0-1 to as high...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 5 potx
... cobalt, 32 chromium, 17 tungsten, 1.5 iron, 1.5 silicon, and up to 2. 7 carbon. The tensile strength is above 100,000 lb/in 2 (689 MPa), and compressive strength is about 325 ,000 lb/in 2 (2, 240 MPa). ... Grade HH, having 120 threads per inch in each direction, is most widely used. A Navy fabric has a weight of 2. 05 oz/yd 2 (0.07 kg/m 2 ) and a ten- sile strength of 38 lb/in 2...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 7 docx
... usually ranging from 21 2 to 3 42 F (100 to 1 72 C). D’Arcet’s alloy, melting at 20 0°F (93°C), con- tains 50% bismuth, 25 tin, and 25 lead. Lichtenberg’s alloy, melting at 198°F ( 92 C), contains 50% ... above 30,000 lb/in 2 (20 6 MPa), a density of 2. 4 to 2. 62, a softening point at 24 60°F (1349°C), and high thermal shock resistance. It is used for molded mechanical and elec- tri...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 8 ppt
... 4 82 to 527 °F (25 0 to 27 5°C). It is a com- plex material, C 41 H 32 O 6 , with four hydroxyl and four methoxyl groups, pine lignin containing 15% methoxyl. The contained lignoceric acid is a C 24 fatty ... lead, 5 to 20 antimony, and 2 to 20 tin have been used for railway 528 LEAD Downloaded from Digital Engineering Library @ McGraw-Hill (www.digitalengineeringlibrary.com) Copyr...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 10 doc
... eliminators and draft-inducing fan wheels. Hastelloy C -22 contains 20 to 22 .5% chromium, 12. 5 to 14.5 molybdenum, 2 to 6 iron, 2. 5 to 3.5 tungsten, 2. 5 maximum cobalt, and small amounts of other elements, ... lb/in 2 (786 MPa) ultimate strength, 52, 000 lb/in 2 (359 MPa) yield strength, 43% elongation, and 28 .5 ϫ 10 6 lb/in 2 (197,000 MPa) modulus. At 1800°F (9 82 C), these...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 12 doc
... of HFC- 125 and HFC-143a, and Du Pont’s Suva HP 62 is a blend of HFC- 125 , HFC-134a (CF 3 CH 2 F), and HFC-143a. Suva Blend-MP is a blend of HFC-152a (CHF 2 CH 3 ), HCFC -22 , and HCFC- 124 . RESINS. ... ultimate tensile strength is typically 32, 000 to 37,000 lb/in 2 (22 1 to 25 5 MPa), yield strength is 10,000 to 17,000 lb/in 2 (69 to 117 MPa), and elongation 25 to 35%. C83300...
Ngày tải lên: 12/08/2014, 03:20
Materials Handbook 15th 2010 Part 15 doc
... contain- ing 20 to 50% columbium, have a tensile strength above 100,000 lb/in 2 (690 MPa) at 129 2°F (700°C), 70,000 lb/in 2 (483 MPa) at 18 32 F (1000°C), and 40,000 lb/in 2 (27 6 MPa) at 21 92 F ( 120 0°C). Vanadium ... loss of three alpha particles of total mass 12, changes to radium 22 6. The lead of old uranium minerals came from Ra 22 6 by the loss of five alpha particles, and...
Ngày tải lên: 12/08/2014, 03:20