Volume 09 - Metallography and Microstructures Part 6 ppt
Volume 09 - Metallography and Microstructures Part 6 ppt
... Precipitation-hardenable grades 63 0 (1 7-4 PH) 0.07 15.5 0-1 7.50 3. 0-5 .0 1.0 1.0 0.040 0.030 3. 0-3 .5Cu, 0.1 5-0 .45Nb + Ta 63 1 (1 7-7 PH) 0 .09 16. 0 0-1 8.00 6. 5-7 .75 1.0 1.0 0.040 0.030 0.7 5-1 .50Al 63 3 ... (AM-350) 0.0 7- 0.11 16. 0 0-1 7.00 4.0 0-5 .00 0. 5-1 .25 0.5 0.040 0.030 2. 5-3 .25Mo, 0.0 7-0 .13N 63 4 (AM355) 0.1 0-...
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 16 ppt
... shape, and orientation with all (c) Approximate percentage of <100> component: Al, Pb, Co-10Fe, Cu-8Al (< 10%); Au (15%); Ni, 4Mo-79Ni-17Fe, Cu, Cu-2Al, Cu-4Al, Co- 35Ni(2 5-3 5%); Co-40Ni ... (Co,Cu) 5 Ce [0001] tet, β-Sn <110> rhom, Bi <111> D8 5 Fe 7 W 6 hR13 D8 6 Cu 15 Si 4 cI 76 D8 8 Mn 5 Si 3 hP 16 D8 9 Co 9 S 8 cF68 D8 10 Al 8 Cr 5 h...
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 17 ppt
... t β β α β χ Ψψ Ω ω
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 1 pps
... obtained, as shown in Fig. 65 , 66 , and 67 , with the change from a phenolic (Fig. 65 ) to an allyl (Fig. 66 ) to a polyvinyl formal (Fig. 67 ) mounting plastic. Metals such as chromium and tungsten, which ... fixed-abrasive lap before polishing. As-polished. 250× magnification 60 60×) of surface layers that were abraded on 220-grit silicon carbide paper. Fig. 5 and 6: resu...
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 3 ppsx
... 1.0000 1.000 0-0 .63 10 2 0.7943 0 .63 1 0-0 .3981 3 0 .63 10 0.398 1-0 .2512 4 0.5012 0.251 2-0 .1585 5 0.3981 0.158 5-0 .1000 6 0.3 162 0.100 0-0 . 063 1 7 0.2512 0. 063 1-0 .0398 8 0.1995 0.039 8-0 .0251 9 0.1581 ... A/A max Sections per mm 2 , (N A ) i 1 0. 063 1-0 .0501 1.000 0-0 .63 10 104 2 0.050 1-0 .0398 0 .63 1 0-0 .3981 161 3 0.039...
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 4 pdf
... 0.20C-1.0Mn steel, as- quenched. The structure is pearlite (dark), martensite (light), and ferrite (white). 10% Na 2 S 2 O 5 . 1000×. (M. Scott) Fig. 109 Steel specimen (Fe-0.22C-0.88Mn-0.55Ni-0.50Cr- 0.35Mo) ... (1255 °F), and held 48 h. Structure is spheroidized carbide particles and lamellar pearlite in a ferrite matrix. Picral. 1000× Fig. 203 Hot-rolled alloy steel bar (1.2...
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 5 pot
... Composition Application AI-7 Macroetch 50 mL HCl and 50 mL H 2 O Dip at 7 0-8 0 °C ( 16 0- 175 °F) Nital General-purpose etch for iron and steels 2-1 0 mL HNO 3 and 9 0-9 8 mL ethanol or methanol ... boundaries and annealing and deformation twins Electrolytic etch: 20% HCl solution in methanol 0.2 5-0 .5 A/cm 2 (1. 6- 3 .2 A/in. 2 ) at 4 -6 for 30 s. For polis...
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 7 ppsx
... 1978, p 56 1-5 68 71. A. Raman, The μ Phases, Z. Metallkd., Vol 57, April 1 966 , p 30 1-3 05 72. H.J. Beattie and F.L. Ver Snyder, A New Complex Phase in a High-Temperature (Iron - Nickel - Chromium ... ASM, Vol 60 , 1 967 , p 22 8-2 41 Atlas of Microstructures for Wrought Heat-Resistant Alloys Fig. 1 Alloy A-2 86 (AISI 66 0, 195 HV), solution annealed 2 h...
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 8 ppsx
... Al-3.5Cu -6 . 0Si A332 (A132) Al-12.0Si-0.8Cu-1.2Mg-2.5Ni 354 (354) Al-9.0Si-1.8Cu-0.5Mg 355 (355) Al-1.3Cu-5.0Si-0.5Mg 3 56 (3 56) Al-7.0Si-0.3Mg A3 56 (A3 56) Al-7.0Si-0.3Mg-0.2Fe max A357 (A357) Al-7.0Si-0.5Mg-0.15Ti ... Wall and R.L. Snyder) Aluminum alloy filler metals and brazing alloys ER2319 Al -6 . 2Cu-0.30Mn-0.15Ti ER4043 Al-5.2Si ER53 56 Al-0.12Mn-5.0Mg-0.12Cr-0....
Ngày tải lên: 10/08/2014, 12:22
Volume 09 - Metallography and Microstructures Part 9 pps
... Grades of vacuum hot-pressed beryllium Chemical composition S -6 5 B S-200F I-220A I-400
Ngày tải lên: 10/08/2014, 12:22