BS EN 60811-403:2012 BSI Standards Publication Electric and optical fibre cables — Test methods for non-metallic materials Part 403: Miscellaneous tests — Ozone resistance test on cross-linked compounds BRITISH STANDARD BS EN 60811-403:2012 National foreword This British Standard is the UK implementation of EN 60811-403:2012 It is identical to IEC 60811-403:2012 In the UK, the relationship between the supersessions of BS EN 60811 series can be summarized as follows BS EN 60811-100 together with -201, -202, -203, -501 -301, -302, -411, -601, -602, -603, -604 -401, -412 -402, -502, -503, -606 -403, -404, -507 -405, -409 -406, -511, -605, -607 -407, -408, -410, -510, -512, -513 -504, -505, -506 -508, -509 Supersedes BS EN 60811-1-1:1995 BS EN 60811-5-1:2000 BS EN 60811-1-2:1995 BS EN 60811-1-3:1995 BS EN 60811-2-1:1998 BS EN 60811-3-2:1995 BS EN 60811-4-1:2004 BS EN 60811-4-2:2004 BS EN 60811-1-4:1995 BS EN 60811-3-1:1995 Superseded standards are withdrawn The UK participation in its preparation was entrusted by Technical Committee GEL/20, Electric cables, to Subcommittee GEL/20/17, Electric Cables - Low voltage A list of organizations represented on this committee can be obtained on request to its secretary This publication does not purport to include all the necessary provisions of a contract Users are responsible for its correct application © The British Standards Institution 2012 Published by BSI Standards Limited 2012 ISBN 978 580 65313 ICS 29.035.01; 29.060.20 Compliance with a British Standard cannot confer immunity from legal obligations This British Standard was published under the authority of the Standards Policy and Strategy Committee on 31 July 2012 Amendments issued since publication Amd No Date Text affected BS EN 60811-403:2012 EUROPEAN STANDARD EN 60811-403 NORME EUROPÉENNE June 2012 EUROPÄISCHE NORM ICS 29.035.01; 29.060.20 Supersedes EN 60811-2-1:1998 (partially) + A1:2001 (partially) English version Electric and optical fibre cables Test methods for non-metallic materials Part 403: Miscellaneous tests Ozone resistance test on cross-linked compounds (IEC 60811-403:2012) Câbles électriques et fibres optiques Méthodes d'essai pour les matériaux nonmétalliques Partie 403: Essais divers Essai de résistance l'ozone sur les mélanges réticulés (CEI 60811-403:2012) Kabel, isolierte Leitungen und Glasfaserkabel Prüfverfahren für nichtmetallene Werkstoffe Teil 403: Sonstige Prüfungen Prüfung der Ozonbeständigkeit für vernetzte Mischungen (IEC 60811-403:2012) This European Standard was approved by CENELEC on 2012-04-16 CENELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CENELEC member This European Standard exists in three official versions (English, French, German) A version in any other language made by translation under the responsibility of a CENELEC member into its own language and notified to the CEN-CENELEC Management Centre has the same status as the official versions CENELEC members are the national electrotechnical committees of Austria, Belgium, Bulgaria, Croatia, Cyprus, the Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, the Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom CENELEC European Committee for Electrotechnical Standardization Comité Européen de Normalisation Electrotechnique Europäisches Komitee für Elektrotechnische Normung Management Centre: Avenue Marnix 17, B - 1000 Brussels © 2012 CENELEC - All rights of exploitation in any form and by any means reserved worldwide for CENELEC members Ref No EN 60811-403:2012 E BS EN 60811-403:2012 EN 60811-403:2012 -2- Foreword The text of document 20/1287/FDIS, future edition of IEC 60811-403, prepared by IEC/TC 20 "Electric cables" was submitted to the IEC-CENELEC parallel vote and approved by CENELEC as EN 60811-403:2012 The following dates are fixed: • • latest date by which the document has to be implemented at national level by publication of an identical national standard or by endorsement latest date by which the national standards conflicting with the document have to be withdrawn (dop) 2013-01-16 (dow) 2015-04-16 This document supersedes Clause of EN 60811-2-1:1998 + A1:2001 (partially) Full details of the replacements are shown in Annex A of EN 60811-100:2012 There are no technical changes with respect to EN 60811-2-1:1998 + A1:2001, but see the Foreword to EN 60811-100:2012 This standard is to be read in conjunction with EN 60811-100 Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights CENELEC [and/or CEN] shall not be held responsible for identifying any or all such patent rights This standard covers the Principle Elements of the Safety Objectives for Electrical Equipment Designed for Use within Certain Voltage Limits (LVD - 2006/95/EC) Endorsement notice The text of the International Standard IEC 60811-403:2012 was approved by CENELEC as a European Standard without any modification -3- BS EN 60811-403:2012 EN 60811-403:2012 Annex ZA (normative) Normative references to international publications with their corresponding European publications The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application For dated references, only the edition cited applies For undated references, the latest edition of the referenced document (including any amendments) applies NOTE When an international publication has been modified by common modifications, indicated by (mod), the relevant EN/HD applies Publication Year Title EN/HD Year IEC 60811-100 2012 Electric and optical fibre cables - Test methods for non-metallic materials Part 100: General EN 60811-100 2012 IEC 60811-501 - Electric and optical fibre cables - Test methods for non-metallic materials Part 501: Mechanical tests - Tests for determining the mechanical properties of insulating and sheathing compounds EN 60811-501 - –2– BS EN 60811-403:2012 60811-403 IEC:2012 CONTENTS INTRODUCTION Scope Normative references Terms and definitions Test method 4.1 4.2 4.3 4.4 4.5 4.6 4.7 4.8 Test General Apparatus Pre-conditioning of the samples Sampling and preparation of test pieces 4.4.1 Sampling of insulation 4.4.2 Sampling of sheath 4.4.3 Preparation of test pieces from insulation 4.4.4 Preparation of test pieces from sheath Conditioning and deformation procedure of test pieces 4.5.1 Test pieces of insulation 4.5.2 Test pieces of sheath Exposure to ozone Evaluation of results Determination of ozone concentration 4.8.1 Chemical analysis 4.8.2 Direct measurement with an ozone meter 10 report 11 Bibliography 12 Table – Mandrel diameters BS EN 60811-403:2012 60811-403 IEC:2012 –5– INTRODUCTION The IEC 60811 series specifies the test methods to be used for testing non-metallic materials of all types of cables These test methods are intended to be referenced in standards for cable construction and for cable materials NOTE Non-metallic materials are typically used for insulating, sheathing, bedding, filling or taping within cables NOTE These test methods are accepted as basic and fundamental and have been developed and used over many years principally for the materials in all energy cables They have also been widely accepted and used for other cables, in particular optical fibre cables, communication and control cables and cables for ships and offshore applications –6– BS EN 60811-403:2012 60811-403 IEC:2012 ELECTRIC AND OPTICAL FIBRE CABLES – TEST METHODS FOR NON-METALLIC MATERIALS – Part 403: Miscellaneous tests – Ozone resistance test on cross-linked compounds Scope This Part 403 of IEC 60811 specifies the method for the ozone resistance test, which typically applies to cross-linked compounds Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application For dated references, only the edition cited applies For undated references, the latest edition of the referenced document (including any amendments) applies IEC 60811-100:2012, Electric and optical fibre cables – Test methods for non-metallic materials – Part 100: General IEC 60811-501, Electric and optical fibre cables – Test methods for non-metallic materials – Part 501: Mechanical tests – Tests for determining the mechanical properties of insulation and sheathing compounds Terms and definitions For the purposes of this document, the terms and definitions given in IEC 60811-100 apply 4.1 Test method General This part of IEC 60811 shall be used in conjunction with IEC 60811-100 WARNING Attention is drawn to the toxicity of ozone Precautions should be taken to minimize exposure of personnel to it at all times and the concentration in the workroom environment should not be allowed to exceed 1×10 -5 % by volume, or the value in the current industrial hygienic standard, whichever is the lower Unless otherwise specified, tests shall be carried out at room temperature 4.2 Apparatus The following apparatus shall be used: a) a device for generating a controlled amount of ozone; b) a means for circulating ozonized air under controlled conditions of humidity and temperature through a chamber containing the test pieces to be tested; c) a means for determination of ozone concentration; d) a suitable device for the clamping and elongation of test pieces; e) cylindrical mandrels consisting of wood or metal; BS EN 60811-403:2012 60811-403 IEC:2012 f) –7– a desiccator filled with silica gel or equivalent material; g) an accurate laboratory balance reading to 0,1 mg 4.3 Pre-conditioning of the samples All the tests shall be carried out not less than 16 h after the extrusion or cross-linking, if any, of the insulating or sheathing compounds If the test is carried out at ambient temperature, the test pieces shall be kept for at least h at a temperature of (23 ± 5) °C 4.4 4.4.1 Sampling and preparation of test pieces Sampling of insulation Whether the cable is single or multicore, only one core needs to be tested Sufficient length of core shall be cut from a position not less than 1,5 m from the end of the length of cable to provide two test pieces, unless the core has an extruded semi-conductor layer on the outside, in which case sufficient length for four test pieces shall be taken Any sample that shows signs of mechanical damage shall not be used for the tests 4.4.2 Sampling of sheath One sample of the cable or cord to be tested, or of the sheath removed from the cable, shall be taken of sufficient size to provide a minimum of two test pieces Any sample that shows signs of mechanical damage shall not be used for the tests 4.4.3 Preparation of test pieces from insulation Any protective coverings present on the core shall be removed without damaging the insulation, unless they were applied directly to the insulation prior to vulcanization and are adherent to it If the core has a semi-conducting layer in the form of tape on the outside, this shall be removed If the core has an extruded semi-conducting screen on the outside, this shall be removed from two test pieces and left in position on the other two 4.4.4 Preparation of test pieces from sheath Two dumb-bell test pieces shall be prepared in accordance with IEC 60811-501 The minimum test piece thickness shall be 0,6 mm In the case of cables of such small size that it is not possible to prepare dumb-bell test pieces, the test method used shall be that specified for insulation 4.5 4.5.1 Conditioning and deformation procedure of test pieces Test pieces of insulation If the core does not have an extruded semi-conducting screen, one test piece shall be bent in the direction and plane of its existing curvature, without twisting, for one complete turn around a mandrel, and bound with twine or tape where the ends cross, and a second test piece of the same core shall be bent similarly in the plane of its existing curvature but in the opposite direction BS EN 60811-403:2012 60811-403 IEC:2012 –8– If the core as manufactured has an extruded core screen on the outside, two test pieces, one with the semi-conducting layer removed and one with the semi-conducting layer left in position, shall be bent, as above, in each direction The bending shall be carried out at temperature 20 °C to 28 °C using a brass, aluminium or suitably treated wooden mandrel with a diameter according to Table Table – Mandrel diameters Outside diameter of insulated core d mm Mandrel diameter (as a multiple of the outside diameter of insulated core) d ≤12,5 ±0,1 12,5