Li ce ns ed C op y P ua n M s N or ha ya ti, P et ro lia m N as io na l B er ha d, 3 1 Ju ly 2 00 2, U nc on tr ol le d C op y, ( c) B S I BRITISH STANDARD BS EN 10113 1 1993 Hot rolled products in we[.]
Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI British Standard A single copy of this British Standard is licensed to Puan Ms Norhayati 31 July 2002 This is an uncontrolled copy Ensure use of the most current version of this document by searching British Standards Online at bsonline.techindex.co.uk BRITISH STANDARD Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI Hot-rolled products in weldable fine grain structural steels — Part 1: General delivery conditions The European Standard EN 10113-1:1993 has the status of a British Standard UDC 669.14.018.29.018.62-122.4-4:620.1 BS EN 10113-1:1993 BS EN 10113-1:1993 Cooperating organizations Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI The European Committee for Standardization (CEN), under whose supervision this European Standard was prepared, comprises the national standards organizations of the following countries: This British Standard, having been prepared under the direction of the Iron and Steel Standards Policy Committee, was published under the authority of the Standards Board and comes into effect on 15 September 1993 © BSI 12-1998 The following BSI references relate to the work on this standard: Committee reference ISM/12 Draft for comment 90/42740 DC ISBN 580 21332 Austria Oesterreichisches Normungsinstitut Belgium Institut belge de normalisation Denmark Dansk Standardiseringsraad Finland Suomen Standardisoimisliito, r.y France Association franỗaise de normalisation Germany Deutsches Institut für Normung e.V Greece Hellenic Organization for Standardization Iceland Technological Institute of Iceland Ireland National Standards Authority of Ireland Italy Ente Nazionale Italiano di Unificazione Luxembourg Inspection du Travail et des Mines Netherlands Nederlands Normalisatie-instituut Norway Norges Standardiseringsforbund Portugal Instituto Portugèus da Qualidade Spain Asociación Espola de Normalización y Certificación Sweden Standardiseringskommissionen i Sverige Switzerland Association suisse de normalisation United Kingdom British Standards Institution Amendments issued since publication Amd No Date Comments BS EN 10113-1:1993 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI Contents © BSI 12-1998 Cooperating organizations National foreword Page Inside front cover ii Foreword Text of EN 10113-1 National annex NA (informative) Committees responsible National annex NB (informative) Cross-references Inside back cover Inside back cover i BS EN 10113-1:1993 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI National foreword This British Standard has been prepared under the direction of the Iron and Steel Standards Policy Committee and is the English language version of EN 10113-1:1993 Hot rolled products in weldable fine grain structural steels — Part 1: General delivery conditions, published by the European Committee for Standardization (CEN) Together with BS EN 10113-2, BS EN 10113-3 and BS EN 10155, it partially supersedes BS 4360:1990 which will be withdrawn in due course The other Parts of BS EN 10113 are as follows: BS EN 10113-2, Hot-rolled products in weldable fine grain structural steels — Part 2: Delivery conditions for normalized/normalized rolled steels BS EN 10113-3, Hot-rolled products in weldable fine grain structural steels — Part 3: Delivery conditions for thermomechanical rolled steels A British Standard does not purport to include all the necessary provisions of a contract Users of British Standards are responsible for their correct application Compliance with a British Standard does not of itself confer immunity from legal obligations Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, the EN title page, pages to 16, an inside back cover and a back cover This standard has been updated (see copyright date) and may have had amendments incorporated This will be indicated in the amendment table on the inside front cover ii © BSI 12-1998 EUROPEAN STANDARD EN 10113-1 NORME EUROPÉENNE EUROPÄISCHE NORM March 1993 UDC 669.14.018.29.018.62-122.4-4:620.1 Descriptors: Iron and steel products, hot-rolled products, structural steels, welded construction, delivery, designation, quality classes, chemical composition, grades, quality, mechanical properties, inspection, tests, marking Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI Hot-rolled products in weldable fine grain structural steels — Part 1: General delivery conditions Produits laminés chaud en aciers de construction soudable grains fins Partie 1: Conditions générales de livraison Warmgewalzte Erzeugnisse aus schweissgeeigneten Feinkornbaustählen Teil 1: Allgemeine Lieferbedingungen This European Standard was approved by CEN on 1993-03-05 CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member This European Standard exists in three official versions (English, French, German) A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions CEN members are the national standards bodies of Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom CEN European Committee for Standardization Comité Européen de Normalisation Europäisches Komitee für Normung Central Secretariat: rue de Stassart 36, B-1050 Brussels © 1993 Copyright reserved to CEN members Ref No EN 10113-1:1993 E EN 10113-1:1993 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI Foreword This European Standard has been drawn up by ECISS/TC 10 “Structural Steel — qualities” whose Secretariat is held by NNI This European Standard replaces EURONORM 113-72 Special quality weldable structural steel grades and quality General provisions The Technical Committee ECISS/TC 10 met in June 1991 in Brussels and agreed on the text for circulation for formal vote within CEN The following countries were represented in that meeting: Austria, Belgium, Denmark, Finland, France, Germany, Italy, Luxembourg, Netherlands, Spain, Sweden and UK This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 1993, and conflicting national standards shall be withdrawn at the latest by September 1993 This European Standard has been adopted and in accordance with the CEN/CENELEC Internal Regulations, the following countries are bound to implement this European Standard: Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom Contents Foreword Scope Normative references Definitions Information to be supplied by the purchaser 4.1 General 4.2 Options Dimensions, mass and tolerances 5.1 Dimensions and tolerances 5.2 Mass of steel Classification of qualities; designation 6.1 Classification of qualities 6.2 Designation Page 3 5 5 5 5 Technical requirements 7.1 Steel manufacturing process 7.2 Delivery condition 7.3 Chemical composition 7.4 Mechanical properties 7.5 Technological properties 7.6 Surface finish 7.7 Internal defects Inspection and testing 8.1 General 8.2 Sampling 8.3 Test units 8.4 Verification of chemical composition 8.5 Mechanical tests 8.6 Test methods 8.7 Retests and resubmission for testing 8.8 Inspection documents Marking for flat and long products 10 Complaints after delivery 11 Options 11.1 All products 11.2 Flat products 11.3 Long products Annex A (normative) Location of samples and test pieces (see EURONORM 18) Annex B (informative) List of national standards which correspond to EURONORMS referenced Annex C (informative) List of corresponding former designations Figure A.1 — Beams, channels, angles, T sections and Z sections Figure A.2 — Bars Figure A.3 — Flat products Table — Permissible deviations of the product analysis from the specified limits of the ladle analysis Table B.1 — EURONORMS with corresponding national standards Table C.1 — List of corresponding former designations Page 5 5 6 7 7 7 7 9 9 9 9 11 14 16 11 12 13 10 14 16 © BSI 12-1998 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI EN 10113-1:1993 Scope Normative references 1.1 This European Standard specifies requirements for long products and flat products of hot-rolled weldable fine grain structural quality and special steels Part of this European Standard specifies the general delivery conditions Part of this European Standard specifies the delivery conditions for normalized steels in the grades and qualities given in Table (chemical composition) and Table and Table (mechanical properties) of Part This European Standard incorporates by dated or undated reference, provisions from other publications These normative references are cited at the appropriate places in the text and the publications are listed hereafter For dated references, subsequent amendments to or revisions of any of these publications apply to this European Standard only when incorporated in it by amendment or revision For undated references the latest edition of the publication referred to applies 2.1 General standards EN 10020, Definition and classification of grades of steel EN 10027-1, Designation systems for steel — Part 1: Steel names principal symbols EN 10027-2, Designation systems for steel — Part 2: Numerical system EN 10079, Definitions of steel products EN 10163, Delivery requirements for surface condition of hot-rolled steel plates, wide flats and sections — Part 1: General requirements; Part 2: Plates and wide flats; Part 3: Sections EN 10204, Metallic products — Types of inspection documents EN 10021, General technical delivery requirements for steel and iron products prEN 100521), Vocabulary of heat treatment terms for ferrous products EURONORM 162 (1981)2), Cold-rolled sections — Technical conditions of delivery EURONORM 168 (1986)2), Iron and steel products — Inspection documents — Contents ECCS IC (1983)2), Weldable fine-grained structural steels — Recommendations for processing, in particular for welding ECISS IC 10, Designation systems for steel — Additional symbols for steel names 2.2 Standards on dimensions and tolerances EN 10029, Hot-rolled plates mm thick or above — Tolerances on dimensions, shape and mass EN 10051, Continuously hot-rolled uncoated sheet and strip of non-alloy and alloy steels — Tolerances on dimensions and shape prEN 100341), Structural steel I and H sections — Tolerances on shape and dimensions prEN 10056-21), Structural steel equal and unequal leg angles — Tolerances on shape and dimensions NOTE Whenever normalized is mentioned, normalized rolled is also covered (see 7.2 of Part 2) Part of this European Standard specifies the delivery conditions for thermomechanical rolled steels in the grades and qualities given in Table (chemical composition) and Table and Table (mechanical properties) of Part The steels specified in this European Standard are especially intended for use in heavily loaded parts of welded structures such as, bridges, flood gates, storage tanks, water supply tanks, etc., for service at ambient and low temperatures 1.2 This European Standard does not apply to products for which other EURONORMS exist or European Standards dealing with steels for general structural applications are being prepared: — Hot-rolled products of non-alloy structural steels (see EN 10025) — Semi-finished products for forging in general purpose structural steels (see EURONORM 30) — Weathering steels for structural purposes (see EN 10155) — Plates and wide flats made of weldable fine-grained structural steels in the quenched and tempered condition (see prEN 10137) — Flat products in high yield strength steels for cold forming — wide flats, sheet/plate, wide and narrow strip (see prEN 10149) — Steels for shipbuilding — normal and high strength qualities (see EURONORM 156) — Hot finished structural hollow sections (see prEN 10210-1) 1) Draft is under discussion 2) Until these EURONORMS are transformed into European Standards, they can either be implemented or reference made to the corresponding national standards, the list of which is given in Annex B to this European Standard © BSI 12-1998 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI EN 10113-1:1993 EURONORM 19 (1957)3), IPE beams: parallel–flanged beams EURONORM 24 (1962)3), Standard beams and channel sections — Tolerances EURONORM 48 (1984)3), Specification for hot-rolled narrow steel strip — Tolerances on dimensions, shape and mass EURONORM 53 (1962)3), Wide-flanged beams with parallel flanges EURONORM 54 (1980)3), Small hot-rolled steel channels EURONORM 55 (1980)3), Hot-rolled equal flange tees with radiused root and toes in steel EURONORM 56 (1977)3)4), Hot-rolled equal angles (with radiused root and toes) EURONORM 57 (1978)3)4), Hot-rolled unequal angles (with radiused root and toes) EURONORM 58 (1978)3), Hot-rolled flats for general purposes EURONORM 59 (1978)3), Hot-rolled square bars for general purposes EURONORM 60 (1977)3), Hot-rolled round bars for general purposes EURONORM 61 (1982)3), Hot-rolled steel hexagons EURONORM 65 (1980)3), Hot-rolled round steel bars for screws and rivets EURONORM 66 (1967)3), Hot-rolled half-rounds and flattened half-rounds EURONORM 67 (1978)3), Hot-rolled bulb flats EURONORM 91 (1981)3), Hot-rolled wide flats — Tolerances on dimensions, shape and mass 2.3 Standards on testing EN 10002-1, Metallic materials — Tensile testing — Part 1: Method of test (at ambient temperature) EN 10045-1, Metallic materials — Charpy impact test — Part 1: Test method EN 10164, Steel products with improved deformation properties perpendicular to the surface of the product — Technical delivery conditions EURONORM 18 (1979)3), Selection and preparation of samples and test pieces for steel and iron and steel products EURONORM 103 (1971)3), Microscopic determination of the ferritic and austenitic grain size of steel EURONORM 160 (1985)3), Manual ultrasonic testing of plate in thicknesses $ mm (reflection method) EURONORM 186 (1987)3), Ultrasonic testing of broad flanged beams with parallel flanges and IPE beams ISO 2566/1 (1984), Steel — Conversion of elongation values — Part 1: Carbon and low alloy steels Definitions For the purposes of this European Standard the following definitions apply 3.1 non-alloy quality steel and alloy special steel as defined in EN 10020 3.2 long products and flat products (plate, sheet, narrow strip, wide strip and wide flats) as defined in EN 10079 3.3 heat treatment terms as defined in prEN 10052 3.4 fine grained steels steels with fine grain structure with an equivalent index of ferritic grain size $ determined in accordance with EURONORM 103 3.5 normalizing rolling a rolling process in which the final deformation is carried out in a certain temperature range leading to a material condition equivalent to that obtained after normalizing so that the specified values of the mechanical properties are retained even after normalizing the abbreviated form of this delivery condition is N NOTE In international publications for both the normalizing rolling, as well as the thermomechanical rolling, the expression “controlled rolling” may be found However in view of the different applicability of the products a distinction of the terms is necessary 3.6 thermomechanical rolling a rolling process in which the final deformation is carried out in a certain temperature range leading to a material condition with certain properties which cannot be achieved or repeated by heat treatment alone the abbreviated form of this delivery condition is M NOTE Subsequent heating above 580 °C may lower the strength values If temperatures above 580 °C are needed reference shall be made to the supplier 3) Until these EURONORMS are transformed into European Standards, they can either be implemented or reference made to the corresponding national standards, the list of which is given in Annex B to this European Standard 4) EURONORM 56 and 57 are added because they contain the nominal dimensions © BSI 12-1998 EN 10113-1:1993 NOTE Thermomechanical rolling leading to the delivery condition M can include processes with an increasing cooling rate with or without tempering including self-tempering but excluding direct quenching and quenching and tempering Information to be supplied by the purchaser Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI 4.1 General The following information shall be supplied by the purchaser at the time of enquiry and order: a) details of the product form and relevant quantities; b) reference to this European Standard; c) nominal dimensions and tolerances (see 5.1); d) the grade, quality and delivery condition of the steel (see Parts and of this European Standard); e) the type of inspection document (see 8.8) Where no specific choice is made by the purchaser concerning points a), b), c), d) and e) the supplier shall refer back to the purchaser 4.2 Options A number of options is specified in clause 11 In the event that the purchaser does not indicate his wish to implement any of these options, the supplier shall supply in accordance with the basic specification Dimensions, mass and tolerances 5.1 Dimensions and tolerances Dimensions and tolerances shall be in accordance with the relevant European Standards and EURONORMS (see 2.2) 5.2 Mass of steel The calculated mass shall be determined using a volumetric mass of 7,85 kg/dm3 — with specified minimum values of impact energy at temperatures not lower than – 20 °C; — with specified minimum values of impact energy at temperatures not lower than – 50 °C 6.2 Designation 6.2.1 For the steel grades covered by this European Standard the steel names are allocated in accordance with EN 10027-1 and ECISS IC 10; the steel numbers are allocated in accordance with EN 10027-2 NOTE For a list of corresponding former national designations and the former designation from EURONORM 113 (1972) see Annex C, Table C.1 6.2.2 The designation shall consist of: — the number of this European Standard (EN 10113-2 or EN 10113-3); — the symbol S; — the indication of the minimum specified yield strength for thicknesses # 16 mm expressed in N/mm2; — the delivery condition (N or M) (see Parts and of this European Standard); — the capital letter L for the quality with specified minimum values of impact energy at temperatures not lower than – 50 ° C Technical requirements 7.1 Steel manufacturing process 7.1.1 The steel manufacturing process shall be at the manufacturer’s option If specified at the time of the enquiry and order the steel manufacturing process shall be reported to the purchaser Option 7.1.2 The steels shall have a fine grain structure containing nitrogen binding elements in amounts sufficient to bind the available nitrogen Classification of qualities; designation 7.2 Delivery condition 6.1 Classification of qualities The delivery condition for normalized steel for flat and long products as defined in clause is given in Part of this European Standard 6.1.1 Classification Classification shall be in accordance with Parts and of this European Standard which specify steel grades that are non-alloy quality steels or alloy special steels according to EN 10020 6.1.2 Grades and qualities The steel designations for flat products and long products specified in Parts and of this European Standard are subdivided in grades on the basis of the minimum specified yield strength at ambient temperature All the grades can be delivered in the following qualities as specified at the time of the enquiry and order: © BSI 12-1998 7.2.1 Normalized steel 7.2.2 Thermomechanical rolled steel The delivery condition for thermomechanical rolled steel for flat and long products as defined in clause is given in Part of this European Standard 7.3 Chemical composition 7.3.1 The chemical composition determined by ladle analysis shall comply with the values in Parts and of this European Standard Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI EN 10113-1:1993 7.3.2 The values for the chemical composition as specified in Parts and of this European Standard are the permitted limits or ranges, between which the various steel grades are delivered The manufacturer shall inform the purchaser at the time of the enquiry and order which of the alloying elements appropriate to the steel grade required will be deliberately added to the material to be delivered 7.3.3 If agreed at the time of the enquiry and order a maximum carbon equivalent value in accordance with the values indicated in Table of Part and Part shall apply The following formula shall be used: Cr + Mo + V Ni + Cu + - + CEV = C + Mn 15 Option 7.3.4 The product analysis shall be carried out when specified at the time of the enquiry and order Option The permissible deviations of the product analysis from the specified limits of the ladle analysis shall be as given in Table 7.4.2.2 If agreed at the time of the enquiry and order another temperature (as given in Table and Table of Parts and 3) can be agreed Option 7.4.2.3 If agreed at the time of the enquiry and order transverse impact values as given in Table of Parts and of this European Standard shall apply instead of longitudinal values Option 7.4.2.4 If the nominal product thickness is not sufficient for the preparation of full size impact test pieces, test pieces of smaller width shall be taken (see 8.5.2.3) and the applicable values shall be decreased proportionally NOTE Impact tests are not required for nominal thickness < mm 7.4.3 Improved deformation properties perpendicular to the surface If agreed at the time of the order flat and long products shall comply with the improved deformation properties perpendicular to the surface (see EN 10164) Option 7.4 Mechanical properties 7.5 Technological properties 7.4.1 General 7.5.1 Weldability 7.4.1.1 Under the inspection and testing conditions as specified in clause and in the delivery condition as specified in 7.2 the mechanical properties and the impact properties at the verification test temperature shall comply with the relevant requirements of Parts and of this European Standard The steels specified in this European Standard shall be suitable for welding processes in current use NOTE Stress relief annealing at more than 580 °C or for over h may lead to a deterioration of the mechanical properties If the purchaser intends to stress relief anneal the products at higher temperatures or for longer times the minimum values of the mechanical properties after such a treatment should be agreed at the time of the enquiry and order 7.4.1.2 For flat products the nominal thickness shall apply For long products of irregular section the nominal thickness of that part from which the samples are taken shall apply (see Annex A) 7.4.2 Impact test 7.4.2.1 The verification of the impact energy value shall be carried out, unless otherwise agreed (see 7.4.2.2 and 7.4.2.3) with longitudinal test pieces for: — N and M at – 20 °C; — NL and ML at – 50 °C 5) NOTE With increasing product thickness and strength level cold cracking can occur Cold cracking is caused by the following factors in combination: — the amount of diffusible hydrogen in the weld metal; — a brittle structure of the heat affected zone; — significant tensile stress concentrations in the welded joint NOTE When using recommendations as laid down, for example in ECCS Information Circular IC 25) or any relevant national standard, the recommended welding conditions and the various welding ranges of the steel grades can be determined depending on the product thickness, the applied welding energy, the design requirements, the electrode efficiency, the welding process and the weld metal properties 7.5.2 Formability NOTE Recommendations regarding hot and cold forming are laid down in ECCS Information Circular IC 7.5.2.1 Hot forming The suitability for hot forming is specified in Parts and of this European Standard Will be transformed into EN Recommendations for arc welding of ferritic steels © BSI 12-1998 EN 10113-1:1993 7.5.2.2 Cold forming Inspection and testing 7.5.2.2.1 Flangeability 8.1 General If specified at the time of the enquiry and order plate, sheet, strip and wide flats shall be suitable for flanging without cracking as given in Parts and of this European Standard Option 11 8.1.1 The products shall be supplied with specific inspection and testing with respect to their compliance with this European Standard 8.1.2 The purchaser shall specify the type of the inspection document at the time of the enquiry and order (see 4.1 and 8.8) 8.1.3 The specific inspection and testing shall be carried out in accordance with 8.2 to 8.7 8.1.4 Unless otherwise agreed at the time of the enquiry and order inspection of surface condition and dimensions shall be carried out by the manufacturer Option Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI 7.5.2.2.2 Roll forming If specified at the time of the enquiry and order plate and strip shall be suitable for the production of sections through cold forming without cracking as given in Parts and of this European Standard (for example according to EURONORM 162) Option 12 NOTE The products suitable for roll forming are also suitable for the manufacture of cold-finished square and rectangular hollow sections 7.5.3 Other requirements 7.5.3.1 If specified at the time of the enquiry and order the grades S275 and S355 shall be suitable for hot-dip zinc coating and shall comply with the relevant product quality requirements Option 7.5.3.2 If agreed at the time of the enquiry and order the material shall be suitable for slitting of heavy sections Option 15 7.6 Surface finish 7.6.1 Strip The surface condition shall not impair an application appropriate to the steel grade if adequate processing of the strip is applied 7.6.2 Plates, wide flats and long products EN 10163 applies for the permissible surface discontinuities and for the repair of surface defects by grinding and/or welding Unless otherwise agreed previously with the purchaser repair by welding is not allowed Option 7.7 Internal defects The products shall be free from internal defects which would exclude them from being used for the usual purpose Ultrasonic testing may be agreed at the time of the enquiry and order (see 8.6.3) Option 13 (for flat products) Option 16 (for long products) © BSI 12-1998 8.2 Sampling The verification of the mechanical properties shall be by cast 8.3 Test units The test unit shall contain products of the same form and grade and of the same thickness range as given in Table of Part and Table of Part of this European Standard for the yield strength For verifying the mechanical properties the test units specified in Parts and of this European Standard shall apply 8.4 Verification of chemical composition 8.4.1 For ladle analysis determined for each cast, the values reported by the manufacturer shall apply 8.4.2 Product analysis shall be carried out if agreed at the time of the enquiry and order The purchaser shall specify the number of samples and the elements to be determined Option 8.5 Mechanical tests 8.5.1 Preparation of samples 8.5.1.1 The following samples shall be taken from one sample product of each test unit: — one sample for tensile testing; — one sample sufficient for one set of six impact test pieces 8.5.1.2 The sample product can be any product within the test unit 8.5.1.3 For plates, sheet, wide strip and wide flats the samples shall be taken approximately midway between the edge and centre line of the products For wide strip the sample shall be taken at an adequate distance from the end of the coil EN 10113-1:1993 Mechanical tests shall be carried out in the temperature range 10 °C to 35 °C, except where a specific temperature is specified for impact tests (see 7.4.2.1 and 7.4.2.2) 8.5.2 Preparation of test pieces 8.6.2.1 Tensile tests 8.5.2.1 General The requirements of EN 10002-1 as appropriate shall apply Test pieces may be non-proportional but in cases of dispute proportional test pieces having a gauge length Lo = 5,65 √ So shall be used (see 8.6.2.1) For flat products with a nominal thickness < mm the test pieces shall always have a gauge length Lo = 80 mm and a width of 20 mm (test piece EN 10002-1) The tensile test shall be carried out in accordance with EN 10002-1 For the specified yield strength in Table of Part and Table of Part of this European Standard the upper yield strength (ReH) shall be determined If a yield phenomenon is not present, the 0,2 % proof strength (Rp0,2) or the Rt0,5 shall be determined; in cases of dispute the 0,2 % proof strength (Rp0,2) shall be determined If a non-proportional test piece is used for products with a thickness $ mm the percentage elongation value obtained shall be converted to the value for a gauge length Lo = 5,65 √ So using the conversion tables given in ISO 2566/1 8.5.2.3 Impact test pieces 8.6.2.2 Impact tests The requirements of EURONORM 18 shall apply (see Annex A) 8.5.2.2 Tensile test pieces Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI 8.6.2 Mechanical tests For narrow strip (< 600 mm wide) the sample shall be at an adequate distance from the end and at one third of the width 8.5.1.4 For long products EURONORM 18 shall apply (see Annex A) The test pieces shall be machined and prepared in accordance with EN 10045-1 In addition the following shall apply a) For nominal thickness > 12 mm, standard 10 mm × 10 mm test pieces shall be machined in such a way that one side is not further away than mm from a rolled surface (see Figure A.3) b) For nominal thickness # 12 mm, when test pieces with reduced widths are used, the minimum width shall be $ mm (see 7.4.2.4) c) Impact test pieces shall be taken from ¼ T position for plates with nominal thickness $ 40 mm 8.5.2.4 Chemical analysis samples The preparation of samples for product analysis shall be in accordance with EURONORM 18 8.6 Test methods 8.6.1 Chemical analysis For the determination of the chemical composition the corresponding European Standards or EURONORMS (see footnote of clause 2) shall apply in cases of dispute NOTE Until these EURONORMS are transformed into European Standards, they can either be implemented or reference made to the corresponding national standards The impact test shall be carried out in accordance with EN 10045-1 The average value of the three test results shall meet the specified requirement One individual value may be below the minimum average value specified, provided that it is not less than 70 % of that value Three additional test pieces shall be taken from the same sample in accordance with 8.5.1 and tested in any one of the following cases: — if the average of three impact values is lower than the minimum average value specified; — if the average value meets the specified requirement, but two individual values are lower than the minimum average value specified; — if any one value is lower than 70 % of the minimum average value specified The average value of the six tests shall be not less than the minimum average value specified Not more than two of the individual values may be lower than the minimum average value specified and not more than one may be lower than 70 % of this value 8.6.3 Ultrasonic testing If specified at the time of enquiry and order (see 7.7), ultrasonic testing shall be carried out: — for plate in thicknesses $ mm in accordance with EURONORM 160; — for broad flanged beams with parallel flanges and IPE beams in accordance with EURONORM 186 © BSI 12-1998 EN 10113-1:1993 8.7 Retests and resubmission for testing 11 Options (see 4.2) EN 10021 shall apply in respect of all retests and resubmission for testing In the case of strip retests on a rejected coil shall be carried out after the cutting of an additional longitudinal section of sufficient length to remove the coil end effect with a maximum of 20 m 11.1 All products Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI 8.8 Inspection documents One of the inspection documents mentioned in EN 10204 for specific testing shall be supplied In these documents the information groups A, B and Z and the code numbers C01 — C03, C10 — C13, C40 — C43 and C71 — C92 according to EURONORM 168 shall be included Marking for flat and long products 9.1 The products shall be marked by a suitable endurable method such as painting, stamping, endurable adhesive labels or attached tags with the following: — the grade, quality and delivery condition indicated by its abridged designation (e.g S355M); — a number by which the cast and the sample can be identified; — the manufacturer’s name or trademark; — the mark of the external inspection body (where applicable) 9.2 Marking shall be at a position close to one end of each product or on the end cut face at the manufacturer’s discretion 9.3 If specified at the time of the enquiry and order there shall be either no steel stamping or only steel stamping in positions indicated by the purchaser Option 10 9.4 If light products are to be supplied in securely tied bundles, the marking shall be on a label attached to the bundle or on the top product of the bundle 10 Complaints after delivery EN 10021 shall apply in respect of complaints after delivery and their processing © BSI 12-1998 1) Whether the steel manufacturing process should be indicated (see 7.1.1) 2) Whether a maximum carbon equivalent value is required (see 7.3.3) 3) Whether product analysis should be carried out and if so the number of samples and the elements to be determined (see 7.3.4 and 8.4.2) 4) At which temperature other than indicated in 7.4.2.1 the impact value should be verified (see 7.4.2.2) 5) Whether transverse impact values are required (see 7.4.2.3) 6) Whether the products should comply with the improved deformation properties perpendicular to the surface of EN 10164 (see 7.4.3) 7) Whether the material of grades S275 or S355 should be suitable for hot-dip zinc coating (see 7.5.3.1) 8) Whether repair by welding is allowed (see 7.6.2) 9) Whether the purchaser wishes to carry out inspection of surface condition and dimensions at the manufacturer’s works by himself or by his authorized representative (see 8.1.4) 10) Whether steel stamping is not allowed or the position for steel stamping as indicated by the purchaser (see 9.3) 11.2 Flat products 11) Whether plate, sheet, strip and wide flats are suitable for flanging (see 7.5.2.2.1) 12) Whether plate, sheet, strip and wide flats are suitable for roll forming (see 7.5.2.2.2) 13) Whether for plate in thickness $ mm internal defects should be tested in accordance with EURONORM 160 (see 7.7 and 8.6.3) 14) Whether for flat products of nominal thickness > 30 mm a round test piece may be used for the tensile test (see Figure A.3) 11.3 Long products 15) Whether a suitability for slitting of heavy sections is required (see 7.5.3.2) 16) Whether for broad flanged beams with parallel flanges and IPE beams internal defects should be tested in accordance with EURONORM 186 (see 7.7 and 8.6.3) EN 10113-1:1993 Table — Permissible deviations of the product analysis from the specified limits of the ladle analysis Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI Element Maximum content in Permissible deviation the ladle analysis of the product analysis % from specified limits for the ladle analysis % C # 0,20 + 0,02 Si # 0,60 + 0,05 Mn # 1,70 – 0,05 + 0,10 P # 0,035 + 0,005 S # 0,030 + 0,005 Nb # 0,05 + 0,010 V # 0,20 + 0,02 Ti # 0,05 + 0,01 Cr # 0,30 + 0,05 Ni # 0,80 + 0,05 Mo # 0,20 + 0,03 Cu # 0,35 > 0,35 # 0,70 + 0,04 + 0,07 N # 0,025 + 0,002 Altotal $ 0,02 – 0,005 10 © BSI 12-1998 EN 10113-1:1993 Annex A (normative) Location of samples and test pieces (see EURONORM 18) Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI The following three categories of products are covered: — beams, channels, angles, T sections and Z sections (Figure A.1) — bars (Figure A.2) — flat products (Figure A.3) Figure A.1 — Beams, channels, angles, T sections and Z sections 1) 2) By agreement, the sample can be taken from the web, at a quarter of the total height Test pieces are taken from the sample as indicated in Figure A.3 For sections with inclined flanges, the inclined surface may be machined in order to make it parallel to the other surface © BSI 12-1998 11 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI EN 10113-1:1993 Figure A.2 — Bars 1) For products with small dimensions (d or b # 25 mm) the test piece, if possible, consists of an unmachined full section of the product 2) For the products of diameter or thickness # 40 mm the manufacturer may either apply: — the rules specified for products of diameter or thickness # 25 mm, or — take the test piece at a location nearer the centre than indicated in the figure 3) For products of round cross-section, the axis of the notch is approximately a diameter; for products with rectangular cross-section, the axis of the notch is perpendicular to the greatest rolled surface 12 © BSI 12-1998 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI EN 10113-1:1993 Figure A.3 — Flat products 1) In case of doubt or dispute, for products of thickness greater than or equal to mm use proportional test pieces of gauge length Lo = 5,65 √ So For normal testing, for reasons of economy, test pieces of a constant measuring length may be used provided the result obtained for elongation after breaking is converted by a recognized formula (see, for example, ISO 2566 Conversion of elongation values) For products of thickness greater than 30 mm a round test piece may be used if agreed between the parties Option 14 2) The axis of the notch shall be perpendicular to the surface of the product © BSI 12-1998 13 EN 10113-1:1993 Annex B (informative) List of national standards which correspond to EURONORMS referenced Until the following EURONORMS are transformed into European Standards, they may be either implemented or reference made to the corresponding national standards as listed in Table B.1 Table B.1 — EURONORMS with corresponding national standards EURONORM Corresponding national standard in Germany 18 France United Kingdom NF A 03 111 BS 4360 Spain UNE 36-300 Italy UNI–EU 18 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI UNE 36-400 19 DIN 1025 T5 NF A 45 205 — UNE 36-526 UNI 5398 24 DIN 1025 T1 NF A 45 210 BS UNE 36-521 UNI 5679 UNE 36-522 UNI 5680 DIN 1026 48 DIN 1016 NF A 46 100 BS 1449 UNE 36-553 UNI 6685 53 DIN 1025 T2 NF A 45 201 BS UNE 36-527 UNI 5397 54 DIN 1025 T3 UNE 36-528 DIN 1025 T4 UNE 36-529 DIN 1026 NF A 45 007 55 DIN 1024 NF A 45 56 DIN 1028 57 DIN 1029 BS UNE 36-525 UNI-EU 54 BS UNE 36-533 UNI-EU 55 NF A 45 009 a BS 4848 UNE 36-531 UNI-EU 56 NF A 45 010 a BS 4848 UNE 36-532 UNI-EU 57 005a 58 DIN 1017 T1 NF A 45 59 DIN 1014 T1 60 DIN 1013 T1 008a BS 4360 UNE 36-543 NI-EU 58 NF A 45 004 a BS 4360 UNE 36-542 UNI-EU 59 NF A 45 003 a BS 4360 UNE 36-541 UNI-EU 60 BS 970 UNE 36-547 UNI 7061 BS 3111 UNE 36-546 UNI 7356 61 DIN 1015 NF A 45 65 DIN 59 130 NF A 45 075 66 DIN 1018 — — — UNI 6630 67 DIN 1019 NF A 45 011 BS 4848 UNE 36-548 UNI-EU 67 91 DIN 59 200 NF A 46 012 BS 4360 — UNI-EU 91 103 DIN 50 601 NF A 04 102 BS 4490 UNE 7-280 UNI 3245 NF A 04 305 BS 5996 NF A 37 101 BS 2994 UNE 36-570 UNI 7344 NF A 03 116 BS 4360 UNE 36-800 UNI-EU 168 NF A 36 000 BS 5135 — — 160 162 DIN 17 118 006a a UNI-EU 160 DIN 59 413 168 186 ECCS IC a SEW 088 NF A 45 001 and NF A 45 101 shall be added for the tolerances 14 © BSI 12-1998 EN 10113-1:1993 Table B.1 — EURONORMS with corresponding national standards EURONORM Corresponding national standard in Belgium 18 NBN A 03-001 Portugal NP-2451 Sweden SS 11 01 20 Austria — SS 11 01 05 Norway NS 10 005 NS 10 006 19 NBN 533 NP-2116 SS 21 27 40 M 3262 — 24 NBN 632-01 — SS 21 27 25 M 3261 NS 911 Licensed Copy: Puan Ms Norhayati, Petroliam Nasional Berhad, 31 July 2002, Uncontrolled Copy, (c) BSI SS 21 27 35 48 — — — DIN 1016 — 53 NBN 633 NP-2117 SS 21 27 50 — NS 1907 SS 21 27 51 NS 1908 SS 21 27 52 54 NBN A 24-204 NP-338 — M 3260 — 55 NBN A 24-205 NP-337 SS 21 27 20 — NS 1905 56 NBN A 24-201 NP-335 SS 21 27 11 M 3246 NS 1903 57 NBN A 24-202 NP-336 SS 21 27 12 M 3247 NS 1904 58 NBN A 34-201 — SS 21 21 50 M 3230 NS 1902 59 NBN A 34-202 NP-333 SS 21 27 25 M 3226 NS 1901 NP-334 60 NBN A 34-203 NP-331 SS 21 25 02 M 3221 NS 1900 61 NBN A 34-204 — — M 3227 — M 3228 65 NBN A 24-206 — — M 3223 — 66 — — — — — 67 NBN A 24-203 — SS 21 11 70 — NS 6034 91 NBN A 43-301 — SS 21 21 50 M 3231 — 103 NBN A 14-101 NP–1787 — — — 160 SS 11 42 01 SS 21 91 14 162 NBN A 02-002 — — M 3316 — 168 — — SS 11 00 12 — — — — SS 06 40 25 — — 186 ECCS IC © BSI 12-1998 15