... most
common are the leaded wrought brasses (C31400 to C 386 00),
leaded cast brasses (C83300 to C8 580 0), leaded phosphor
bronzes (C53200 to C5 480 0), and leaded tin bronzes (C92200 to
C92900).
LEADED ... lb/in
2
(87 MPa) with
elongation of 3%.
A hard lead with 10% antimony and 90 lead has a tensile strength
of 8, 800 lb/in
2
(61 MPa), elongation 17%, Brinell hardness 17, and
melting poin...
Materials Handbook 15th 2010 Part 1 pptx
... lb/in
2
(76 to 79 MPa) and 16,100 to
18, 100 lb/in
2
(111 to 125 MPa), respectively; ultimate elongation is 4.3
to 8. 8%; the flexural modulus is 470,000 to 480 ,000 lb/in
2
(3240 to
3310 MPa); and ... website.
Source: Materials Handbook
various particle sizes for use in glass and vitreous enamels to
increase the strength and luster. Hydrated alumina C-741 is this
material with particle...
Materials Handbook 15th 2010 Part 2 pps
... phosphorus.
BIOMATERIALS. Materials used to repair, restore, or replace dam-
aged or diseased tissue, or those that comprise parts of artificial
organs, artificial tissues, or prostheses. The use of biomaterials
dates ... glycerin. Cohune oil has a melting point
of 64 to 68 F ( 18 to 20°C), saponification value 252 to 256, iodine
value 10 to 14, and specific gravity 0 .86 8 to 0.971. The c...
Materials Handbook 15th 2010 Part 3 ppsx
... density of 0.317 lb/in
3
(8, 775 kg/m
3
); an 80 –20 bronze has a density of 0.315 lb/in
3
(8, 719
kg/m
3
). The 80 –20 bronze melts at 186 8°F (1020°C), and a 95–5
bronze melts at 2 480 °F (1360°C).
The family ... furnace black with particle sizes from 1,100
to 3,350 in ( 28 to 85 m) and a pH from 8 to 10, and the channel
blacks with particle size of about 1,140 in (29 m) and pH...
Materials Handbook 15th 2010 Part 4 pot
... about
40,000 lb/in
2
(276 MPa) to 70,000 lb/in
2
( 483 MPa) at 1200°F (649°C)
and from about 4,000 lb/in
2
( 28 MPa) to 15,000 lb/in
2
(103 MPa) at
180 0°F ( 982 °C). Cobalt is also an important alloying ... about 687 2°F ( 380 0°C). It is made by
sintering columbium powder and carbon in a hydrogen furnace.
COMPOSITES. In the broadest sense, materials comprising at least
two distinct inte...
Materials Handbook 15th 2010 Part 5 potx
... interparticle spacing, and the volume fraction of the
particle phase. In general, strength, especially at high temperatures,
improves as interparticle spacing decreases. Depending on the materials
involved, ... right-hand twill with a rayon warp and combed cotton fill-
ing. It is 8. 5 oz/yd
2
(0.29 kg/m
2
), 180 -lb (82 -kg) warp, and 80 -lb (36-
kg) filling. Cavalry twill is not a cotton...
Materials Handbook 15th 2010 Part 7 docx
... The specific gravity is 8. 7, density 0.314 lb/in
3
(8, 719
kg/m
3
), and Brinell hardness 65 to 74. This alloy is similar to G
bronze (C90300), which contains 88 % copper, 8 tin, and 4 zinc. In
England ... indium up to
a maximum of 18. Wood’s alloy, or Wood’s fusible metal, was
patented in 186 0 and was the first metal used for automatic sprinkler
plugs. It contains 7 to 8 parts bismu...
Materials Handbook 15th 2010 Part 10 doc
... soda-fountain parts, has 63% copper, 4 tin, 5
lead, 8 zinc, and 20 nickel. The higher-nickel alloys have a more per-
manent white finish for parts subject to corrosion. Ambrac 85 4 is a
wrought ... amorphous particles 12 to 1 38 in (0.3 to 3.5 m) in
diameter. Atomized powder has spherical particles of 50 to 200 mesh
and is free-flowing. The powders are used for coatings and parts for
se...
Materials Handbook 15th 2010 Part 12 doc
... 60 to 80 % alumina, withstands temperatures from 3290 to
3335°F ( 181 0 to 183 5°C). The melting point of a 99.5% pure alu-
mina is given as 3725°F (2052°C), and the decomposing point of a
98% pure ... gilding metal comes in three grades,
80 , 85 , and 90% copper, but the 80 –20 alloy has a definite golden-yellow
color and is not in the class of red brasses. The 80 –20 brass (C24000) is...
Materials Handbook 15th 2010 Part 15 doc
... website.
Materials, Their Properties and Uses
988 TUNGSTEN CARBIDE
and grinding quills and dies for die casting, extrusion, and hot upset-
ting. A CW tungsten-copper Series, with 68 to 80 % tungsten ... 0.0025 to 2 in (0.0064 to 5 cm) and approximately 48 by
80 in (122 by 203 cm) in size. Outside diameters of tubes range from
0. 187 5 to 4.375 in (0.4 78 to 11 cm). Rods are produced 0....