One-pot Synthesis of Soluble Nanoscale CIGS Photoactive
Functional Materials
Ying Lin Æ Yu Chen Æ Miao Feng Æ Aixia Yan Æ
Xiaodong ... used to prepare
soluble nanoscale triphenyl phosphine-coordinated CIGS
(TPP -CIGS) photoactive functional materials. This com-
plex is stable in the solid state under the irradiation of the
ambient ... Figure 1 compares...
Báo cáo hóa học: " One-pot Synthesis of Soluble Nanoscale CIGS Photoactive Functional Materials" pot
... Araki, O. Ito, Org. Lett.
7, 1613 (2005)
24 Nanoscale Res Lett (2008) 3:21–24
123
NANO EXPRESS
One-pot Synthesis of Soluble Nanoscale CIGS Photoactive
Functional Materials
Ying Lin Æ Yu Chen Æ ... used to prepare
soluble nanoscale triphenyl phosphine-coordinated CIGS
(TPP -CIGS) photoactive functional materials. This com-
plex is stable in the solid state under the...
Báo cáo hóa học: " Controllable synthesis of flake-like Al-doped ZnO nanostructures and its application in inverted organic solar cells" doc
... Correspondence: gjfang@whu.edu.cn
Key Laboratory of Artificial Micro- and Nano-structures of Ministry of
Education, Department of Electronic Science and Technology, School of
Physics and Technology, Wuhan University, ... The
active area of the IOSCs is 0.2 cm
2
. Figure 1c shows the
energy dispersive spectrum (EDS) of AZO
Figure 1 Schematic structure of the IOSCs, and FE-SEM i...
Báo cáo hóa học: " Hydrothermal synthesis of MnO2/CNT nanocomposite with a CNT core/porous MnO2 sheath hierarchy architecture for supercapacitors" potx
... nanostructure of the MnO
2
layer. A highly porous MnO
2
layer composed
of interconnected nanoflakes is introduced in the present study instead of a dense
MnO
2
layer composed of closely packed ... MnO
2
nanoflakes of pure MnO
2
microspheres, these MnO
2
nanoflakes grown on CNTs are
much smaller in dimension, typically with a thickness of less than 5 nm.
The formation mec...
Báo cáo hóa học: " Direct synthesis of ultrafine tetragonal BaTiO3 nanoparticles at room temperature" pptx
... optics [2,3].
For the existence of the size effect of ferroelectricity and
the potential application of bottom-up assembled novel
nanostructures, the synthesis of ultrafine BaTiO
3
nano-
particles ... generalized synthesis of oxide
nanoparticles. J Am Chem Soc 2001, 123:12085-12086.
8. Urban JJ, Yun WS, Gu Q, Park HK: Synthesis of single-crystalline perovskite
nanowires comp...
Báo cáo hóa học: " Solvothermal synthesis of uniform bismuth nanospheres using poly(N-vinyl-2-pyrrolidone) as a reducing agent" pptx
... Process of Ministry of Education and
School of Chemical Engineering & Pharmacy, Wuhan Institute of Technology,
Wuhan, 430073, P. R. China
2
Key Laboratory of Catalysis and Materials
Science of ... of Ministry of Education and
School of Chemical Engineering & Pharmacy, Wuhan Institute of Technology,
Wuhan, 430073, P. R. China
Full list of author information is ava...
Báo cáo hóa học: " Scalable synthesis of aligned carbon nanotubes bundles using green natural precursor: neem oil" doc
... setup for the synthesis of
aligned CNTs.
Figure 2 SEM micrographs of the as-grown ACNTs at 825°C.
(a, b) The Cross-sectional view of the dense block of the CNTs. The
complete block of ACNTs’ side-view ... arrangement
of the CNTs in the block.
Kumar et al. Nanoscale Research Letters 2011, 6:92
http://www.nanoscalereslett.com/content/6/1/92
Page 2 of 6
NANO EXPRESS Open Access...
báo cáo hóa học:" Facile synthesis of uniform large-sized InP nanocrystal quantum dots using tris(tert-butyldimethylsilyl)phosphine" pdf
... of various phosphorus precursors 1 to 3.
Figure 3. One-pot synthesis of core-shells and their optical properties. (a) One-pot
synthesis of InP with P(SiMe
2
-tert-Bu)
3
followed by ZnS shell ... experiments with a synthesis of the InP NQDs using compounds 2 (Figure 3a)
and 3. For a typical experiment, 0.04 mmol of In(OAc)
3
was added to a mixture of 0.12
mmol of...
báo cáo hóa học:" Controllable Synthesis of Single-Crystalline CdO and Cd(OH)2 Nanowires by a Simple Hydrothermal Approach" docx
... obtained
Fig. 4 Schematic of the
formation of nanowire bundles
Fig. 5 PL spectra of bundles of nanowires collected after a 10 h and
b 24 h of hydrothermal treatment
964 Nanoscale Res Lett (2010) ... images of the
as-fabricated CdO wires at
a low and b high
magnifications; c TEM image of
a bundle of CdO nanowires;
d HRTEM image of nanowires
that make up the bundle; and
e EDX...